Solvay Specialty Polymers Ixef® 1002 Polyarylamide (PARA), 30% Glass Fiber

Category Polymer , Thermoplastic , PVDC , Polyvinyl Dichloride (PVDC)
Manufacturer Solvay Specialty Polymers
Trade Name Ixef®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Ixef® 1002 Polyarylamide (PARA), 30% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ixef® 1002 is a 30% glass-fiber reinforced, general purpose polyarylamide compound which exhibits high strength and rigidity, outstanding surface finish, and excellent creep resistance.Features: Good Chemical Resistance; Good Creep Resistance; Good Dimensional Stability; High Flow; High Stiffness; High Strength; Low Moisture Absorption; Outstanding Surface FinishUses: Appliance Components; Appliances; Automotive Applications; Automotive Electronics; Automotive Exterior Parts; Automotive Interior Parts; Automotive Under the Hood; Bushings; Camera Applications; Cell Phones; Electrical Housing; Electrical/Electronic Applications; Furniture; Gears; Industrial Applications; Machine/Mechanical Parts; Metal Replacement; Power/Other ToolsInjection Molding Notes: Ixef® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Ixef® resins be dried prior to molding.Additional Properties: Moisture Absorption - Internal Method 1.9 %Automotive Specifications ASTM D6779 PA111G30; BMW GS 93016Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.43 g/cc
0.0517 lb/in³
ISO 1183
Filler Content 30 %
30 %
Glass Fiber
Water Absorption 0.20 %

@Time 86400 sec
0.20 %

@Time 24.0 hour
ISO 62
Linear Mold Shrinkage 0.0010 - 0.0040 cm/cm
0.0010 - 0.0040 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 190 MPa
27600 psi
ISO 527-2
Elongation at Break 2.0 %
2.0 %
ISO 527-2
Tensile Modulus 11.5 GPa
1670 ksi
ISO 527-2
Flexural Strength 285 MPa
41300 psi
ISO 178
Flexural Modulus 11.5 GPa
1670 ksi
ISO 178
Izod Impact, Notched 0.700 J/cm
1.31 ft-lb/in
ASTM D256
Izod Impact, Unnotched 4.60 J/cm
8.62 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 18.0 µm/m-°C
10.0 µin/in-°F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 230 °C
446 °F
Unannealed; ISO 75-2/A
Flammability, UL94 HB
HB
Oxygen Index 25 %
25 %
ISO 4589-2
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
IIEC 60093
Dielectric Constant 3.9

@Frequency 110 Hz
3.9

@Frequency 110 Hz
IEC 60250
Dielectric Strength 30.0 kV/mm
762 kV/in
IEC 60243-1
Dissipation Factor 0.010

@Frequency 110 Hz
0.010

@Frequency 110 Hz
IEC 60250
Comparative Tracking Index 400 V
400 V
IEC 60112
Processing Properties Metric English Comments
Rear Barrel Temperature 250 - 260 °C
482 - 500 °F
Front Barrel Temperature 260 - 290 °C
500 - 554 °F
Melt Temperature 280 °C
536 °F
Mold Temperature 120 - 140 °C
248 - 284 °F
Drying Temperature 120 °C

@Time 1800 - 5400 sec
248 °F

@Time 0.500 - 1.50 hour
Descriptive Properties Value Comments
Availability Africa & Middle East
Asia Pacific
Europe
Latin America
North America
Color Black; Colors; Natural
Form Pellets
Injection Rate Fast
Processing Technique Injection Molding
RoHS Compliance RoHS Compliant