Solvay Specialty Polymers Ixef® 1032 Polyarylamide (PARA)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyarylamide (PAA) , Polyarylamide, Glass Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Ixef® 1032 Polyarylamide (PARA)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ixef 1032 is a 60% glass-fiber reinforced, general purpose polyarylamide compound which exhibits very high strength and rigidity, outstanding surface gloss, and excellent creep resistance. - Natural: Ixef 1032/0008 - Black: Ixef 1032/9008 - Custom ColorableInjection Notes: Injection time: 0.5 to 2.5 sec Holding time: 3e sec Cooling time: 2.5e² sec (e= wall thickness in mm) Drying The material as supplied is ready for molding without drying. However, If the bags have been open for longer than 24 hours, the material needs to be dried. When using a desiccant air dryer with dew point of -28°C (-18°F) or lower, these guidelines can be followed: 0.5-1.5 hour at 120°C (248°F), 1-3 hours at 100°C (212°F), or 1-7 hours at 80°C (176°F). Injection Molding IXEF 1032 compound can be readily injection molded in most screw injection molding machines. A general purpose screw is recommended, with minimum back pressure. The measured melt temperature should be about 280°C (536°F), and the barrel temperatures should be around 250 to 260°C (482°F to 500°F) in the rear zone, gradually increasing to 260°C to 290°C (500°F to 554°F) in the front zone. If hot runners are used, they should be set to 250°C to 260°C (482°F to 500°F). To maximize crystallinity, the temperature of the mold cavity surface must be held between 120°C and 140°C (248°F and 284°F). Molding at lower temperatures will produce articles that may warp, have poor surface appearance, and have a greater tendency to creep. Set injection pressure to give rapid injection. Adjust holding pressure and hold time to maximize part weight. Transfer from injection to hold pressure at the screw position just before the part is completely filled (95%-99%).Data is presented for dry polymer unless noted as 'conditioned'.Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.77 g/cc
0.0639 lb/in³
ISO 1183
Filler Content 60 %
60 %
Glass Fiber Reinforcement
Water Absorption 0.13 %

@Temperature 23.0 °C,
Time 86400 sec
0.13 %

@Temperature 73.4 °F,
Time 24.0 hour
ISO 62
Moisture Absorption at Equilibrium 1.3 %
1.3 %
65% RH; Internal Method
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
Internal Method
Mechanical Properties Metric English Comments
Tensile Strength at Break 250 MPa
36300 psi
Conditioned; ISO 527-2
280 MPa
40600 psi
ISO 527-2
Elongation at Break 1.8 %
1.8 %
ISO 527-2
2.0 %
2.0 %
Conditioned; ISO 527-2
Tensile Modulus 23.0 GPa
3340 ksi
Conditioned; ISO 527-2
24.0 GPa
3480 ksi
ISO 527-2
Flexural Strength 400 MPa
58000 psi
ISO 178
Flexural Modulus 23.5 GPa
3410 ksi
ISO 178
Izod Impact, Notched 1.20 J/cm
2.25 ft-lb/in
ASTM D256
9.00 J/cm
16.9 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
CTE, linear 14.0 µm/m-°C
7.78 µin/in-°F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 230 °C
446 °F
Unannealed; ISO 75-2/A
Flammability, UL94 HB
HB
UL 94
Oxygen Index 25 %
25 %
ISO 4589-2
Glow Wire Test 775 °C

@Thickness 1.50 mm
1430 °F

@Thickness 0.0591 in
Glow Wire Flammability Index; IEC 60695-2-12
775 °C

@Thickness 0.800 mm
1430 °F

@Thickness 0.0315 in
Glow Wire Flammability Index; IEC 60695-2-12
800 °C

@Thickness 0.800 mm
1470 °F

@Thickness 0.0315 in
Glow Wire Ignition Temperature; IEC 60695-2-13
800 °C

@Thickness 1.50 mm
1470 °F

@Thickness 0.0591 in
Glow Wire Ignition Temperature; IEC 60695-2-13
825 °C

@Thickness 3.00 mm
1520 °F

@Thickness 0.118 in
Glow Wire Ignition Temperature; IEC 60695-2-13
960 °C

@Thickness 3.00 mm
1760 °F

@Thickness 0.118 in
Glow Wire Flammability Index; IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
IEC 60093
Dielectric Constant 4.5

@Frequency 110 Hz
4.5

@Frequency 110 Hz
IEC 60250
Dielectric Strength 24.0 kV/mm
610 kV/in
IEC 60243-1
Dissipation Factor 0.0090

@Frequency 110 Hz
0.0090

@Frequency 110 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 60112
Processing Properties Metric English Comments
Rear Barrel Temperature 250 - 260 °C
482 - 500 °F
Middle Barrel Temperature 260 - 270 °C
500 - 518 °F
Front Barrel Temperature 270 - 280 °C
518 - 536 °F
Nozzle Temperature 260 - 290 °C
500 - 554 °F
Melt Temperature 280 °C
536 °F
Mold Temperature 120 - 140 °C
248 - 284 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 12.0 hour
12.0 hour
Moisture Content 0.30 %
0.30 %
Injection Pressure 50.0 - 150 MPa
7250 - 21800 psi
Hold Pressure 75.0 MPa
10900 psi
Back Pressure 0.000 - 1.00 MPa
0.000 - 145 psi
Descriptive Properties Value Comments
Appearance Black
Colors Available
Natural Color
Automotive Specifications ASTM D6779 PA111G60
GM GM7001M
GM GM7001M PAMXD6 A4 A22 A64 BA661 DC1770 G30 KS2400 MS1800 NS340 RT7 SS225 Color: 0008 Natural
GM GM7001M PAMXD6 A4 A22 A64 BA661 DC1770 G30 KS2400 MS1800 NS340 RT7 SS225 Color: 9008 Black
Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Features Good Chemical Resistance
Good Creep Resistance
Good Dimensional Stability
High Flow
High Strength
Low Moisture Absorption
Outstanding Surface Finish
Ultra High Stiffness
Forms Pellets
Generic PARA
Injection Rate Fast
Processing Method Injection Molding
RoHS Compliance RoHS Compliant
Screw L/D Ratio 15.0:1.0 to 20.0:1.0
Uses Automotive Applications
Automotive Electronics
Automotive Interior Parts
Furniture
High Gloss Applications
Metal Replacement
Sporting Goods