BASF Ultramid® A3XZG5 BK 23187 25% Glass Filled PA66 FR (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® A3XZG5 BK 23187 25% Glass Filled PA66 FR (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Impact-modified, 25% glass-fiber reinforced injection-molding grade with improved flame retardance and enhanced long-term stability. Flame retardant based on red phosphorus; for components requiring high stiffness and enhanced toughness like photovoltaic connectors and junction boxes.Information provided by BASF
Physical Properties Metric English Comments
Bulk Density 0.500 - 0.800 g/cc
0.0181 - 0.0289 lb/in³
Density 1.32 g/cc
0.0477 lb/in³
ISO 1183
Water Absorption 4.7 - 5.3 %
4.7 - 5.3 %
Saturation; ISO 62
Moisture Absorption at Equilibrium 1.0 - 1.4 %
1.0 - 1.4 %
23°C; 50% RH; ISO 62
Viscosity Measurement 140
140
ISO 307
Linear Mold Shrinkage 0.0055 cm/cm
0.0055 in/in
restricted
Mechanical Properties Metric English Comments
Tensile Strength, Yield 70.0 MPa
10200 psi
50 mm/min; ISO 527-1/-2
Elongation at Yield 11 %
11 %
50 mm/min; ISO 527-1/-2
Modulus of Elasticity 4.50 GPa
653 ksi
ISO 527-1/-2
Charpy Impact Unnotched 10.0 J/cm²

@Temperature 23.0 °C
47.6 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 3.00 J/cm²

@Temperature 23.0 °C
14.3 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Tensile Creep Modulus, 1000 hours 2000 MPa

@Strain <=0.500 %
290000 psi

@Strain <=0.500 %
ISO 899-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow >= 36.0 µm/m-°C
>= 20.0 µin/in-°F
Thermal Conductivity 0.330 W/m-K
2.29 BTU-in/hr-ft²-°F
DIN 52612
Melting Point 260 °C
500 °F
DIN 53765
Maximum Service Temperature, Air 180 °C
356 °F
Decomposition Temperature >= 310 °C
>= 590 °F
UL RTI, Electrical 120 °C

@Thickness 1.50 mm
248 °F

@Thickness 0.0591 in
UL 746B
Oxygen Index 28 %
28 %
ISO 4589-2
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+10 ohm-cm
1.00e+10 ohm-cm
IEC 60093
Surface Resistance 1.00e+10 ohm
1.00e+10 ohm
IEC 60093
Dielectric Constant 4.0

@Frequency 1.00 Hz
4.0

@Frequency 1.00 Hz
IEC 60250
Dissipation Factor 0.030

@Frequency 1.00e+6 Hz
0.030

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 575 V
575 V
Test solution A; IEC 60112
Hot Wire Ignition, HWI 0.00 sec

@Thickness >=0.750 mm
0.00 sec

@Thickness >=0.0295 in
ASTM D3874-88
High Amp Arc Ignition, HAI 0.00 arcs

@Thickness >=0.750 mm
0.00 arcs

@Thickness >=0.0295 in
UL 746C
Processing Properties Metric English Comments
Processing Temperature 80.0 °C
176 °F
Hopper Throat
Zone 1 290 °C
554 °F
Feed Zone
Zone 2 290 °C
554 °F
Compression
Zone 3 290 °C
554 °F
Metering-zone
Zone 4 290 °C
554 °F
Nozzle
Melt Temperature 280 - 300 °C
536 - 572 °F
Injection-molding/Extrusion
290 °C
554 °F
Optimal
Mold Temperature 60.0 - 90.0 °C
140 - 194 °F
Injection-molding
80.0 °C
176 °F
Optimal
Drying Temperature 80.0 °C
176 °F
Dry Time 4 hour
4 hour
Moisture Content 0.030 - 0.060 %
0.030 - 0.060 %
Optimal
<= 0.15 %
<= 0.15 %
Descriptive Properties Value Comments
Color BK 23187
Commercial Status Europe
Ignition Temperature >350°C
ASTM D1929
Peripheral screw speed < 0.3 m/s