Lanxess Durethan® BKV 50 000000 Nylon 6, Glass Fiber Reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled
Manufacturer Lanxess
Trade Name Durethan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® BKV 50 000000 Nylon 6, Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
PA 6, 50% glass fibers, injection moldingInformation provided by LANXESS.
Physical Properties Metric English Comments
Specific Gravity 1.57 g/cc
1.57 g/cc
ISO 1183
Moisture Absorption at Equilibrium 1.5 %
1.5 %
50% RH; ISO 62
Water Absorption at Saturation 5.0 %
5.0 %
ISO 62
Linear Mold Shrinkage, Flow 0.00020 cm/cm
0.00020 in/in
Post-shrinkage, 150x105x3; 120°C; 4 hour; ISO 2577
0.0016 cm/cm
0.0016 in/in
150x105x3; 280°C / MT 80°C; 400 bar; ISO 2577
Linear Mold Shrinkage, Transverse 0.00050 cm/cm
0.00050 in/in
Post-shrinkage, 150x105x3; 120°C; 4 hour; ISO 2577
0.0085 cm/cm
0.0085 in/in
150x105x3; 280°C / MT 80°C; 400 bar; ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 145 MPa
21000 psi
cond.; ISO 527-1, -2; 5 mm/min
220 MPa
31900 psi
d.a.m.; ISO 527-1, -2; 5 mm/min
Elongation at Break 3.0 %
3.0 %
d.a.m.; ISO 527-1, -2; 5 mm/min
5.0 %
5.0 %
cond.; ISO 527-1, -2; 5 mm/min
Tensile Modulus 9.80 GPa
1420 ksi
cond.; ISO 527-1, -2; 1 mm/min
16.3 GPa
2360 ksi
d.a.m.; ISO 527-1, -2; 1 mm/min
Flexural Strength 235 MPa

@Strain 5.00 %
 34100 psi

@Strain 5.00 %
 cond., 2 mm/min; ISO 178-A
365 MPa

@Strain 3.00 %
 52900 psi

@Strain 3.00 %
 d.a.m., 2 mm/min; ISO 178-A
Flexural Yield Strength 210 MPa

@Strain 3.50 %
 30500 psi

@Strain 3.50 %
 cond., 2 mm/min; ISO 178-A
Flexural Modulus 9.70 GPa
1410 ksi
cond., 2 mm/min; ISO 178-A
15.1 GPa
2190 ksi
d.a.m., 2 mm/min; ISO 178-A
Izod Impact, Notched (ISO) 13.0 kJ/m²

@Temperature -30.0 °C
 6.19 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 180-1A
14.0 kJ/m²

@Temperature -30.0 °C
 6.66 ft-lb/in²

@Temperature -22.0 °F
 cond.; ISO 180-1A
20.0 kJ/m²

@Temperature 23.0 °C
 9.52 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 180-1A
25.0 kJ/m²

@Temperature 23.0 °C
 11.9 ft-lb/in²

@Temperature 73.4 °F
 cond.; ISO 180-1A
Charpy Impact Unnotched 8.50 J/cm²

@Temperature -30.0 °C
 40.4 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 179-1eU
8.50 J/cm²

@Temperature -30.0 °C
 40.4 ft-lb/in²

@Temperature -22.0 °F
 cond.; ISO 179-1eU
10.0 J/cm²

@Temperature 23.0 °C
 47.6 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 179-1eU
11.0 J/cm²

@Temperature 23.0 °C
 52.3 ft-lb/in²

@Temperature 73.4 °F
 cond.; ISO 179-1eU
Charpy Impact, Notched 1.50 J/cm²

@Temperature -30.0 °C
 7.14 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 179-1eA
1.50 J/cm²

@Temperature -30.0 °C
 7.14 ft-lb/in²

@Temperature -22.0 °F
 cond.; ISO 179-1eA
2.00 J/cm²

@Temperature 23.0 °C
 9.52 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 179-1eA
2.50 J/cm²

@Temperature 23.0 °C
 11.9 ft-lb/in²

@Temperature 73.4 °F
 cond.; ISO 179-1eA
Puncture Energy 6.00 J

@Temperature -30.0 °C
 4.43 ft-lb

@Temperature -22.0 °F
 d.a.m.; ISO 6603-2
9.00 J

@Temperature 23.0 °C
 6.64 ft-lb

@Temperature 73.4 °F
 d.a.m.; ISO 6603-2
14.0 J

@Temperature 23.0 °C
 10.3 ft-lb

@Temperature 73.4 °F
 cond.; ISO 6603-2
Tensile Creep Modulus, 1 hour 8100 MPa
1.17e+6 psi
cond.; ISO 899-1
Tensile Creep Modulus, 1000 hours 6600 MPa
957000 psi
cond.; ISO 899-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 20.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 11.1 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1, -2
CTE, linear, Transverse to Flow 70.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 38.9 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1, -2
Melting Point 222 °C
432 °F
10°C/min; ISO 11357-1, -3
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
ISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
401 °F
ISO 75-1, -2
Vicat Softening Point >= 200 °C

@Load 5.10 kg
 >= 392 °F

@Load 11.2 lb
 120°C/hour; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
HB

@Thickness 3.20 mm
 HB

@Thickness 0.126 in
Oxygen Index 24 %
24 %
Method A; ISO 4589-2
Glow Wire Test 650 °C

@Diameter 2.00 mm
 1200 °F

@Diameter 0.0787 in
 GWFI; IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+12 ohm-cm
1.00e+12 ohm-cm
cond.; IEC 60093
1.00e+15 ohm-cm
1.00e+15 ohm-cm
d.a.m.; IEC 60093
Surface Resistance 1.00e+12 ohm
1.00e+12 ohm
cond.; IEC 60093
1.00e+14 ohm
1.00e+14 ohm
d.a.m.; IEC 60093
Dielectric Constant 4.0

@Frequency 100 Hz
 4.0

@Frequency 100 Hz
 d.a.m.; IEC 60250
4.0

@Frequency 1.00e+6 Hz
 4.0

@Frequency 1.00e+6 Hz
 d.a.m.; IEC 60250
5.0

@Frequency 1.00e+6 Hz
 5.0

@Frequency 1.00e+6 Hz
 cond.; IEC 60250
Dielectric Strength 35.0 kV/mm

@Thickness 1.00 mm
 889 kV/in

@Thickness 0.0394 in
 cond.; IEC 60243-1
40.0 kV/mm

@Thickness 1.00 mm
 1020 kV/in

@Thickness 0.0394 in
 d.a.m.; IEC 60243-1
Dissipation Factor 0.010

@Frequency 100 Hz
 0.010

@Frequency 100 Hz
 d.a.m.; IEC 60250
0.015

@Frequency 1.00e+6 Hz
 0.015

@Frequency 1.00e+6 Hz
 d.a.m.; IEC 60250
0.14

@Frequency 1.00e+6 Hz
 0.14

@Frequency 1.00e+6 Hz
 cond.; IEC 60250
Comparative Tracking Index 525 V
525 V
d.a.m.; Solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 270 - 290 °C
518 - 554 °F
280 °C
536 °F
for test specimens; ISO 294
Mold Temperature 80.0 °C
176 °F
for test specimens; ISO 294
80.0 - 120 °C
176 - 248 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 2 - 6 hour
2 - 6 hour
Moisture Content 0.030 - 0.12 %
0.030 - 0.12 %
residual; Karl Fischer Test
Descriptive Properties Value Comments
ISO Shortname ISO 1874-PA 6, GR, 14-160, GF50