Lehmann & Voss LUVOCOM® 1301-7661/RD PPS, linear, with glass fiber and PTFE
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 10% Glass Fiber Filler |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1301-7661/RD PPS, linear, with glass fiber and PTFE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile-and office machinery, medical- and precision engineering.High continuous use and heat distortion temperature. Non flammable.Strong, stiff parts.Improved friction and wear behaviour. Emergency running property.High chemical resistance parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | ISO 1183 |
| Water Absorption | <= 0.050 % | <= 0.050 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 80.0 MPa | 11600 psi | |
| Elongation at Yield | 2.2 % | 2.2 % | |
| 3.0 % | 3.0 % | flexural | |
| Modulus of Elasticity | 5.00 GPa | 725 ksi | |
| Flexural Strength | 115 MPa | 16700 psi | |
| Flexural Modulus | 4.00 GPa | 580 ksi | |
| Charpy Impact Unnotched | 2.50 J/cm² | 11.9 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 220 °C | 428 °F | |
| 240 °C | 464 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 330 °C | 626 °F | mass temp |
| Nozzle Temperature | 320 - 340 °C | 608 - 644 °F | |
| Zone 1 | 300 - 320 °C | 572 - 608 °F | |
| Zone 2 | 310 - 330 °C | 590 - 626 °F | |
| Zone 3 | 320 - 340 °C | 608 - 644 °F | |
| Mold Temperature | 150 - 180 °C | 302 - 356 °F | |
| Drying Temperature | 50.0 - 90.0 °C @Time >=14400 sec |
122 - 194 °F @Time >=4.00 hour |
|
| 100 - 140 °C @Time 7200 - 14400 sec |
212 - 284 °F @Time 2.00 - 4.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | red |
Users viewing this material also viewed the following:
- Rogers Corporation Bisco™ HT-800 Cellular Silicone Foam
- ExxonMobil Vyram™ 9271-85 Thermoplastic Rubber (discontinued **)
- SABIC BC 110 Crystalline Polyethylene Terephthalate
- Sylvin Technologies 9604-90 LMW Clear PVC for Injection Molding
- Eagle Brass 510 Phosphor Bronzes 5% A, Spring
- CPC - Vycom CELTEC® Expanded Rigid foam PVC board
- Americas Styrenics STYRON® 666D High Heat Crystal Polystyrene
- A. Schulman ComAlloy Aqualoy® 135 Polypropylene, Glass Reinforced, Chemically Coupled NSF, UL
Copyright © lookpolymers.com All Rights Reserved