Styrolution Styrolux 3G33 SBC
| Category | Polymer , Thermoplastic , Styrene-Butadiene , Styrene-Butadiene Copolymer, SBC |
| Manufacturer | Styrolution |
| Trade Name | Styrolux |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution Styrolux 3G33 SBC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Styrolux 3G33 is a thermoplastic styrene-butadiene block copolymer which is suitable for injection molding, extrusion and thermoforming. It offers an outstanding combination of crystal clarity and good toughness.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in³ | ISO 1183 |
| Water Absorption | 0.070 % | 0.070 % | ISO 62 |
| Moisture Absorption at Equilibrium | 0.070 % | 0.070 % | 23°C/50% R.H.; ISO 62 |
| Linear Mold Shrinkage | 0.0065 cm/cm | 0.0065 in/in | ASTM Data; MD |
| Melt Flow | 11 g/10 min @Load 5.00 kg, Temperature 200 °C |
11 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM Test |
| 12 g/10 min @Load 5.00 kg, Temperature 200 °C |
12 g/10 min @Load 11.0 lb, Temperature 392 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 68 | 68 | ASTM Test |
| Tensile Strength, Yield | 28.3 MPa | 4100 psi | 2 in/min; ASTM Test |
| 32.0 MPa | 4640 psi | 50mm/min; ISO 527 | |
| Elongation at Break | 40 % | 40 % | 50mm/min, Nominal strain; ISO 527 |
| 100 % | 100 % | 2 in/min; ASTM Test | |
| 100 % | 100 % | 0.2 in/min; ASTM Test | |
| Elongation at Yield | 2.0 % | 2.0 % | 50mm/min; ISO 527 |
| Tensile Modulus | 1.60 GPa | 232 ksi | 1mm/min; ISO 527 |
| 1.72 GPa | 249 ksi | 2 in/min; ASTM Test | |
| Flexural Strength | 31.0 MPa | 4500 psi | ASTM Test |
| 45.0 MPa | 6530 psi | ISO Data | |
| Flexural Modulus | 1.48 GPa | 215 ksi | ASTM Test |
| 1.75 GPa | 254 ksi | ISO Data | |
| Izod Impact, Notched | 0.270 J/cm @Thickness 3.17 mm |
0.506 ft-lb/in @Thickness 0.125 in |
ASTM Test |
| Izod Impact, Notched (ISO) | 3.50 kJ/m² | 1.67 ft-lb/in² | ISO Test |
| Charpy Impact Unnotched | 10.0 J/cm² | 47.6 ft-lb/in² | ISO 179 |
| 3.00 J/cm² @Temperature -30.0 °C |
14.3 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179 |
| Dart Drop, Total Energy | 5.00 J | 3.69 ft-lb | ASTM Test |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 75.0 µm/m-°C | 41.7 µin/in-°F | ISO 11359 |
| CTE, linear, Transverse to Flow | 72.0 µm/m-°C | 40.0 µin/in-°F | ASTM Test |
| Deflection Temperature at 0.46 MPa (66 psi) | 77.0 °C | 171 °F | ISO 75 |
| 82.0 °C | 180 °F | ASTM Test | |
| Deflection Temperature at 1.8 MPa (264 psi) | 63.0 °C | 145 °F | ISO 75 |
| 66.0 °C | 151 °F | ASTM Test | |
| Vicat Softening Point | 56.0 °C | 133 °F | (50 °C/h / 50N) - B/50; ISO 306 |
| 91.0 °C | 196 °F | Rate "B" Loading 1 (120 degC/h 10N); ASTM Test | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.573 | 1.573 | ASTM Test |
| Haze | 0.21 % @Thickness 3.20 mm |
0.21 % @Thickness 0.126 in |
ASTM Test |
| Transmission, Visible | 92 % | 92 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | IEC 60093 |
| Dielectric Constant | 2.5 @Frequency 1e+9 Hz |
2.5 @Frequency 1e+9 Hz |
ASTM Data |
| 2.5 @Frequency 1.00e+6 Hz |
2.5 @Frequency 1.00e+6 Hz |
ASTM Data | |
| 2.5 @Frequency 100 Hz |
2.5 @Frequency 100 Hz |
IEC 60250 | |
| 2.5 @Frequency 1.00e+6 Hz |
2.5 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Dielectric Strength | 140 kV/mm | 3560 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.00030 @Frequency 1e+9 Hz |
0.00030 @Frequency 1e+9 Hz |
ASTM Data |
| 0.00080 @Frequency 1.00e+6 Hz |
0.00080 @Frequency 1.00e+6 Hz |
ASTM Data | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 190 - 230 °C | 374 - 446 °F | Extrusion |
| 180 - 250 °C | 356 - 482 °F | Injection Molding | |
| 230 °C | 446 °F | Injection molding | |
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | Injection Molding |
| Injection Velocity | 50.0 mm/sec | 1.97 in/sec | Injection molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Clear | |
| Commercial Status | Active America | |
| FDA | Yes | |
| Form | Yes | |
| Impact Modified | Yes | |
| NSF Std. 51 | No | |
| NSF Std. 61 | No | |
| Primary Processing Technique | Injection Molding | |
| Processing | Film Extrusion | |
| Injection Molding | ||
| UL.UL-C | No |
Users viewing this material also viewed the following:
- PolyOne Stat-Tech™ AS-10SS/000 ABS - 10% Stainless Steel Fiber (discontinued **)
- SABIC Innovative Plastics XYLEX EXXX0292 PC+POLYESTER (Europe-Africa-Middle East)
- Zeon Chemicals Zetpol® 1000L Hydrogenated Nitrile Elastomomer
- Tra-Con Tra-Bond 2116 Low Vapor Pressure Epoxy Staking Compound
- Chevron Phillips K-Resin® XK40 Styrene-Butadiene Copolymer, Sheet Grade
- Ashley Polymers Ashlene® P260WO PPO
- Teknor Apex Sarlink® 3490 Thermoplastic Elastomer
- Addiplast Addilene H 210 Polypropylene Homopolymer
- Pyrotek Wollite 45 Insulating Castable
Copyright © lookpolymers.com All Rights Reserved