DuPont Performance Polymers Hytrel® G4074 Polyester Elastomer TPC-ET  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polyester Thermoplastic Elastomer
Manufacturer DuPont Performance Polymers
Trade Name Hytrel®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Hytrel® G4074 Polyester Elastomer TPC-ET  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
40 Shore D Standard Performance Polyester Elastomer with Heat Ageing ProtectionHytrel G4074 is a low modulus grade with nominal hardness of 40D. It contains discoloring stabilizer. It can be processed by many conventional thermoplastic processing technInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.03 g/cc
0.0372 lb/in³
1.18 g/cc
0.0426 lb/in³
ISO 1183
Water Absorption 3.7 %

@Thickness 2.00 mm
 3.7 %

@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.400 %

@Thickness 2.00 mm
 0.400 %

@Thickness 0.0787 in
 Sim. to ISO 62
Water Absorption at Saturation 2.1 %
2.1 %
Immersion 24h; ASTM D570
Viscosity 67967 cP

@Shear Rate 5000 1/s,
Temperature 200 °C
 67967 cP

@Shear Rate 5000 1/s,
Temperature 392 °F
 ISO 11403-1 -2
81258 cP

@Shear Rate 5000 1/s,
Temperature 185 °C
 81258 cP

@Shear Rate 5000 1/s,
Temperature 365 °F
 ISO 11403-1 -2
281800 cP

@Shear Rate 500 1/s,
Temperature 200 °C
 281800 cP

@Shear Rate 500 1/s,
Temperature 392 °F
 ISO 11403-1 -2
346800 cP

@Shear Rate 500 1/s,
Temperature 185 °C
 346800 cP

@Shear Rate 500 1/s,
Temperature 365 °F
 ISO 11403-1 -2
Linear Mold Shrinkage, Flow 0.0080 cm/cm
0.0080 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
0.0080 in/in
ISO 294-4 2577
Melt Flow 5.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 5.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 cm³/10min; ISO 1133
5.3 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 5.3 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 35
35
15s; ISO 868
<= 40
<= 40
ISO 868
Tensile Strength at Break 20.0 MPa
2900 psi
ISO 527-1/-2
Tensile Stress 2.50 MPa

@Strain 5.00 %
 363 psi

@Strain 5.00 %
 ISO 527-1/-2
4.40 MPa

@Strain 10.0 %
 638 psi

@Strain 10.0 %
 ISO 527-1/-2
8.00 MPa

@Strain 50.0 %
 1160 psi

@Strain 50.0 %
 ISO 527-1/-2
1.34 MPa

@Strain 6.82 %,
Temperature 120 °C
 194 psi

@Strain 6.82 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
1.52 MPa

@Strain 5.88 %,
Temperature 100 °C
 220 psi

@Strain 5.88 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
1.53 MPa

@Strain 6.00 %,
Temperature 90.0 °C
 222 psi

@Strain 6.00 %,
Temperature 194 °F
 ISO 11403-1 -2
1.78 MPa

@Strain 6.36 %,
Temperature 90.0 °C
 258 psi

@Strain 6.36 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
2.16 MPa

@Strain 16.56 %,
Temperature 120 °C
 313 psi

@Strain 16.56 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
2.20 MPa

@Strain 6.30 %,
Temperature 60.0 °C
 319 psi

@Strain 6.30 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
2.57 MPa

@Strain 14.17 %,
Temperature 100 °C
 373 psi

@Strain 14.17 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
2.57 MPa

@Strain 26.3 %,
Temperature 120 °C
 373 psi

@Strain 26.3 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
2.60 MPa

@Strain 6.00 %,
Temperature 40.0 °C
 377 psi

@Strain 6.00 %,
Temperature 104 °F
 ISO 11403-1 -2
2.79 MPa

@Strain 6.00 %,
Temperature 23.0 °C
 405 psi

@Strain 6.00 %,
Temperature 73.4 °F
 ISO 11403-1 -2
2.84 MPa

@Strain 36.05 %,
Temperature 120 °C
 412 psi

@Strain 36.05 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
2.95 MPa

@Strain 6.60 %,
Temperature 40.0 °C
 428 psi

@Strain 6.60 %,
Temperature 104 °F
 TPE; ISO 11403-1 -2
2.99 MPa

@Strain 15.33 %,
Temperature 90.0 °C
 434 psi

@Strain 15.33 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
3.03 MPa

@Strain 45.79 %,
Temperature 120 °C
 439 psi

@Strain 45.79 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
3.16 MPa

@Strain 22.47 %,
Temperature 100 °C
 458 psi

@Strain 22.47 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
3.18 MPa

@Strain 24.0 %,
Temperature 90.0 °C
 461 psi

@Strain 24.0 %,
Temperature 194 °F
 ISO 11403-1 -2
3.23 MPa

@Strain 59.43 %,
Temperature 120 °C
 468 psi

@Strain 59.43 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
3.35 MPa

@Strain 5.86 %,
Temperature 23.0 °C
 486 psi

@Strain 5.86 %,
Temperature 73.4 °F
 TPE; ISO 11403-1 -2
3.38 MPa

@Strain 72.42 %,
Temperature 120 °C
 490 psi

@Strain 72.42 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
3.50 MPa

@Strain 85.41 %,
Temperature 120 °C
 508 psi

@Strain 85.41 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
3.57 MPa

@Strain 31.45 %,
Temperature 100 °C
 518 psi

@Strain 31.45 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
3.60 MPa

@Strain 23.55 %,
Temperature 90.0 °C
 522 psi

@Strain 23.55 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
3.60 MPa

@Strain 98.4 %,
Temperature 120 °C
 522 psi

@Strain 98.4 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
3.65 MPa

@Strain 6.00 %,
Temperature 0.000 °C
 529 psi

@Strain 6.00 %,
Temperature 32.0 °F
 ISO 11403-1 -2
3.66 MPa

@Strain 14.45 %,
Temperature 60.0 °C
 531 psi

@Strain 14.45 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
3.69 MPa

@Strain 42.0 %,
Temperature 90.0 °C
 535 psi

@Strain 42.0 %,
Temperature 194 °F
 ISO 11403-1 -2
3.71 MPa

@Strain 117.88 %,
Temperature 120 °C
 538 psi

@Strain 117.88 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
3.78 MPa

@Strain 130.87 %,
Temperature 120 °C
 548 psi

@Strain 130.87 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
3.80 MPa

@Strain 5.85 %,
Temperature 0.000 °C
 551 psi

@Strain 5.85 %,
Temperature 32.0 °F
 TPE; ISO 11403-1 -2
3.84 MPa

@Strain 147.11 %,
Temperature 120 °C
 557 psi

@Strain 147.11 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
3.84 MPa

@Strain 39.75 %,
Temperature 100 °C
 557 psi

@Strain 39.75 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
3.93 MPa

@Strain 170.49 %,
Temperature 120 °C
 570 psi

@Strain 170.49 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
4.03 MPa

@Strain 196.47 %,
Temperature 120 °C
 585 psi

@Strain 196.47 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
4.03 MPa

@Strain 32.53 %,
Temperature 90.0 °C
 585 psi

@Strain 32.53 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
4.14 MPa

@Strain 50.81 %,
Temperature 100 °C
 600 psi

@Strain 50.81 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
4.35 MPa

@Strain 41.5 %,
Temperature 90.0 °C
 631 psi

@Strain 41.5 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
4.38 MPa

@Strain 61.87 %,
Temperature 100 °C
 635 psi

@Strain 61.87 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
4.53 MPa

@Strain 22.6 %,
Temperature 60.0 °C
 657 psi

@Strain 22.6 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
4.58 MPa

@Strain 72.93 %,
Temperature 100 °C
 664 psi

@Strain 72.93 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
4.68 MPa

@Strain 53.46 %,
Temperature 90.0 °C
 679 psi

@Strain 53.46 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
4.76 MPa

@Strain 84.68 %,
Temperature 100 °C
 690 psi

@Strain 84.68 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
4.94 MPa

@Strain 64.68 %,
Temperature 90.0 °C
 716 psi

@Strain 64.68 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
4.95 MPa

@Strain 15.62 %,
Temperature 40.0 °C
 718 psi

@Strain 15.62 %,
Temperature 104 °F
 TPE; ISO 11403-1 -2
4.95 MPa

@Strain 6.00 %,
Temperature -20.0 °C
 718 psi

@Strain 6.00 %,
Temperature -4.00 °F
 ISO 11403-1 -2
5.01 MPa

@Strain 101.27 %,
Temperature 100 °C
 727 psi

@Strain 101.27 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
5.15 MPa

@Strain 112.33 %,
Temperature 100 °C
 747 psi

@Strain 112.33 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
5.15 MPa

@Strain 31.49 %,
Temperature 60.0 °C
 747 psi

@Strain 31.49 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
Users viewing this material also viewed the following: