Overview of materials for Acrylic/Polycarbonate Alloy

Category Polymer , Thermoplastic , Acrylic (PMMA) , Acrylic/Polycarbonate Alloy , Polycarbonate (PC)
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Acrylic/Polycarbonate Alloy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Acrylic/Polycarbonate Alloy". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.12 - 1.29 g/cc
0.0405 - 0.0466 lb/in³
Average value: 1.19 g/cc Grade Count:26
Water Absorption 0.220 - 0.260 %
0.220 - 0.260 %
Average value: 0.251 % Grade Count:12
Linear Mold Shrinkage 0.00300 - 0.00900 cm/cm
0.00300 - 0.00900 in/in
Average value: 0.00639 cm/cm Grade Count:25
Melt Flow 1.90 - 7.90 g/10 min
1.90 - 7.90 g/10 min
Average value: 3.85 g/10 min Grade Count:6
Mechanical Properties Metric English Comments
Hardness, Rockwell M 44.0 - 55.0
44.0 - 55.0
Average value: 48.5 Grade Count:6
Hardness, Rockwell R 46.0
46.0
Average value: 46.0 Grade Count:3
Tensile Strength, Ultimate 41.4 - 61.0 MPa
6000 - 8850 psi
Average value: 49.7 MPa Grade Count:22
Tensile Strength, Yield 48.3 - 62.7 MPa
7010 - 9090 psi
Average value: 55.7 MPa Grade Count:4
Elongation at Break 10.0 - 88.0 %
10.0 - 88.0 %
Average value: 26.7 % Grade Count:25
Elongation at Yield 3.70 - 4.70 %
3.70 - 4.70 %
Average value: 4.23 % Grade Count:6
Modulus of Elasticity 1.72 - 2.60 GPa
250 - 377 ksi
Average value: 2.18 GPa Grade Count:25
Flexural Yield Strength 62.1 - 91.7 MPa
9000 - 13300 psi
Average value: 78.0 MPa Grade Count:26
Flexural Modulus 1.93 - 2.41 GPa
280 - 350 ksi
Average value: 2.18 GPa Grade Count:25
Izod Impact, Notched 2.24 - 16.0 J/cm
4.20 - 30.0 ft-lb/in
Average value: 9.69 J/cm Grade Count:26
2.1356 - 9.12969 J/cm

@Temperature 0.000 - 0.000 °C
4.0009 - 17.1037 ft-lb/in

@Temperature 32.0 - 32.0 °F
Average value: 5.63 J/cm Grade Count:2
2.1356 - 9.12969 J/cm

@Diameter 6.35 - 6.35 mm
4.0009 - 17.1037 ft-lb/in

@Diameter 0.250 - 0.250 in
Average value: 5.63 J/cm Grade Count:2
Izod Impact, Unnotched 20.3 - 5340 J/cm
38.0 - 10000 ft-lb/in
Average value: 21.0 J/cm Grade Count:16
Thermal Properties Metric English Comments
CTE, linear 93.6 µm/m-°C
52.0 µin/in-°F
Average value: 93.6 µm/m-°C Grade Count:6
93.6 - 93.6 µm/m-°C

@Temperature 0.000 - 100 °C
52.0 - 52.0 µin/in-°F

@Temperature 32.0 - 212 °F
Average value: 93.6 µm/m-°C Grade Count:3
Deflection Temperature at 0.46 MPa (66 psi) 102 - 123 °C
215 - 253 °F
Average value: 114 °C Grade Count:10
Deflection Temperature at 1.8 MPa (264 psi) 82.2 - 123 °C
180 - 253 °F
Average value: 99.7 °C Grade Count:19
Vicat Softening Point 119 - 152 °C
246 - 306 °F
Average value: 136 °C Grade Count:6
Flammability, UL94 HB - 5VA
HB - 5VA
Grade Count:20
Optical Properties Metric English Comments
Transmission, Visible 0.000 %
0.000 %
Average value: 0.000 % Grade Count:3
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+8 - 9.90e+10 ohm-cm
1.00e+8 - 9.90e+10 ohm-cm
Average value: 2.02e+10 ohm-cm Grade Count:6
Surface Resistance 1.00e+9 - 9.90e+11 ohm
1.00e+9 - 9.90e+11 ohm
Average value: 1.64e+11 ohm Grade Count:6
Static Decay 2.00 sec
2.00 sec
Average value: 2.00 sec Grade Count:6
Dielectric Constant 2.72
2.72
Average value: 2.72 Grade Count:3
Dissipation Factor 0.00900
0.00900
Average value: 0.00900 Grade Count:3
Processing Properties Metric English Comments
Processing Temperature 193 - 249 °C
380 - 480 °F
Average value: 222 °C Grade Count:9
Melt Temperature 199 - 266 °C
390 - 510 °F
Average value: 244 °C Grade Count:14
Mold Temperature 32.2 - 98.9 °C
90.0 - 210 °F
Average value: 55.4 °C Grade Count:23
Drying Temperature 82.2 °C
180 °F
Average value: 82.2 °C Grade Count:13
Moisture Content 0.0200 %
0.0200 %
Average value: 0.0200 % Grade Count:10
Dew Point -17.8 °C
0.000 °F
Average value: -17.8 °C Grade Count:10
Injection Pressure 33.1 - 103 MPa
4800 - 15000 psi
Average value: 71.2 MPa Grade Count:20