Overview of materials for Nylon 610

Category Polymer , Thermoplastic , Nylon , Nylon 610
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Nylon 610.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 610". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.03 - 3.80 g/cc
0.0372 - 0.137 lb/in³
Average value: 1.30 g/cc Grade Count:215
Filler Content 10.0 - 50.0 %
10.0 - 50.0 %
Average value: 28.6 % Grade Count:52
Water Absorption 0.0900 - 4.00 %
0.0900 - 4.00 %
Average value: 1.21 % Grade Count:92
0.900 - 1.50 %

@Temperature 70.0 - 70.0 °C
0.900 - 1.50 %

@Temperature 158 - 158 °F
Average value: 1.23 % Grade Count:8
Moisture Absorption at Equilibrium 0.0900 - 4.80 %
0.0900 - 4.80 %
Average value: 0.630 % Grade Count:71
Water Absorption at Saturation 0.400 - 1.20 %

@Temperature 45.0 - 400 °C
0.400 - 1.20 %

@Temperature 113 - 752 °F
Average value: 0.814 % Grade Count:2
0.400 - 1.20 %

@Treatment Temp. 70.0 - 70.0 °C
0.400 - 1.20 %

@Treatment Temp. 158 - 158 °F
Average value: 0.814 % Grade Count:2
Viscosity 360000 - 360000 cP

@Temperature 250 - 250 °C
360000 - 360000 cP

@Temperature 482 - 482 °F
Average value: 221000 cP Grade Count:1
700 - 527068 cP

@Temperature 230 - 280 °C
700 - 527068 cP

@Temperature 446 - 536 °F
Average value: 221000 cP Grade Count:3
700 - 527068 cP

@Shear Rate 10.0 - 5000 1/s
700 - 527068 cP

@Shear Rate 10.0 - 5000 1/s
Average value: 221000 cP Grade Count:3
Viscosity Test 150 - 170 cm³/g
150 - 170 cm³/g
Average value: 157 cm³/g Grade Count:3
Linear Mold Shrinkage 0.000600 - 0.0300 cm/cm
0.000600 - 0.0300 in/in
Average value: 0.00621 cm/cm Grade Count:175
Linear Mold Shrinkage, Transverse 0.00200 - 0.0400 cm/cm
0.00200 - 0.0400 in/in
Average value: 0.0111 cm/cm Grade Count:94
Melt Flow 4.00 - 130 g/10 min
4.00 - 130 g/10 min
Average value: 42.8 g/10 min Grade Count:13
Spiral Flow 35.0 - 700 cm
13.8 - 276 in
Average value: 110 cm Grade Count:10
Mechanical Properties Metric English Comments
Hardness, Rockwell R 111 - 122
111 - 122
Average value: 118 Grade Count:20
Ball Indentation Hardness 35.0 - 245 MPa
5080 - 35500 psi
Average value: 125 MPa Grade Count:24
Tensile Strength, Ultimate 16.5 - 524 MPa
2390 - 76000 psi
Average value: 126 MPa Grade Count:190
70.0 - 155 MPa

@Temperature 60.0 - 150 °C
10200 - 22500 psi

@Temperature 140 - 302 °F
Average value: 61.4 MPa Grade Count:2
7.36 - 191.87 MPa

@Temperature -40.0 - 150 °C
1070 - 27828 psi

@Temperature -40.0 - 302 °F
Average value: 61.4 MPa Grade Count:2
7.36 - 191.87 MPa

@Strain 0.180 - 160 %
1070 - 27828 psi

@Strain 0.180 - 160 %
Average value: 61.4 MPa Grade Count:2
Tensile Strength, Yield 32.0 - 237 MPa
4640 - 34400 psi
Average value: 101 MPa Grade Count:51
Elongation at Break 0.500 - 240 %
0.500 - 240 %
Average value: 19.0 % Grade Count:193
3.30 - 6.10 %

@Temperature 60.0 - 150 °C
3.30 - 6.10 %

@Temperature 140 - 302 °F
Average value: 36.4 % Grade Count:3
Elongation at Yield 1.50 - 100 %
1.50 - 100 %
Average value: 7.91 % Grade Count:58
Modulus of Elasticity 0.450 - 44.2 GPa
65.3 - 6410 ksi
Average value: 8.04 GPa Grade Count:181
0.109 - 12.1 GPa

@Temperature -40.0 - 150 °C
15.8 - 1750 ksi

@Temperature -40.0 - 302 °F
Average value: 2.88 GPa Grade Count:7
Tenacity 0.370 - 0.509 N/tex
4.19 - 5.77 g/denier
Average value: 0.447 N/tex Grade Count:3
Flexural Yield Strength 22.0 - 393 MPa
3190 - 57000 psi
Average value: 206 MPa Grade Count:148
Flexural Modulus 0.530 - 22.4 GPa
76.9 - 3250 ksi
Average value: 7.86 GPa Grade Count:164
Compressive Yield Strength 68.9 - 179 MPa
10000 - 26000 psi
Average value: 140 MPa Grade Count:12
Shear Modulus 0.477 - 3.05 GPa
69.2 - 443 ksi
Average value: 1.44 GPa Grade Count:3
>= 0.0417 GPa

@Temperature -50.0 - 150 °C
>= 6.05 ksi

@Temperature -58.0 - 302 °F
Average value: 0.756 GPa Grade Count:3
Shear Strength 65.5 - 79.0 MPa
9500 - 11500 psi
Average value: 72.2 MPa Grade Count:3
0.03597 - 0.677 MPa

@Temperature 250 - 280 °C
5.217 - 98.2 psi

@Temperature 482 - 536 °F
Average value: 0.280 MPa Grade Count:1
0.03597 - 0.677 MPa

@Shear Rate 50.0 - 5000 1/s
5.217 - 98.2 psi

@Shear Rate 50.0 - 5000 1/s
Average value: 0.280 MPa Grade Count:1
Secant Modulus 0.901953 - 10.9027 GPa

@Temperature -40.0 - 100 °C
130.819 - 1581.33 ksi

@Temperature -40.0 - 212 °F
Average value: 5.67 GPa Grade Count:1
0.901953 - 10.9027 GPa

@Strain 0.190 - 10.2 %
130.819 - 1581.33 ksi

@Strain 0.190 - 10.2 %
Average value: 5.67 GPa Grade Count:1
Izod Impact, Notched 0.290 - 6.03 J/cm
0.543 - 11.3 ft-lb/in
Average value: 1.10 J/cm Grade Count:126
Izod Impact, Unnotched 3.25 - 5340 J/cm
6.09 - 10000 ft-lb/in
Average value: 8.41 J/cm Grade Count:87
Izod Impact, Notched (ISO) 1.00 - 88.2 kJ/m²
0.476 - 42.0 ft-lb/in²
Average value: 15.8 kJ/m² Grade Count:56
Izod Impact, Unnotched (ISO) 20.0 - 21000 kJ/m²
9.52 - 9990 ft-lb/in²
Average value: 54.3 kJ/m² Grade Count:46
Charpy Impact Unnotched 3.00 - 1000 J/cm²
14.3 - 4760 ft-lb/in²
Average value: 8.87 J/cm² Grade Count:69
4.50 - 999.9 J/cm²

@Temperature -30.0 - 30.0 °C
21.4 - 4759 ft-lb/in²

@Temperature -22.0 - 86.0 °F
Average value: 9.28 J/cm² Grade Count:42
Charpy Impact, Notched 0.370 - 1000 J/cm²
1.76 - 4760 ft-lb/in²
Average value: 2.01 J/cm² Grade Count:64
0.300 - 2.10 J/cm²

@Temperature -40.0 - 30.0 °C
1.43 - 9.99 ft-lb/in²

@Temperature -40.0 - 86.0 °F
Average value: 1.09 J/cm² Grade Count:46
Gardner Impact 4.63 - 36.2 J
3.42 - 26.7 ft-lb
Average value: 28.3 J Grade Count:4
Dart Drop, Total Energy 1.00 - 22.0 J
0.738 - 16.2 ft-lb
Average value: 7.13 J Grade Count:23
Falling Dart Impact 8.50 - 11.8 J
6.27 - 8.70 ft-lb
Average value: 9.88 J Grade Count:4
Coefficient of Friction 0.190 - 0.710
0.190 - 0.710
Average value: 0.421 Grade Count:21
Coefficient of Friction, Static 0.100 - 0.520
0.100 - 0.520
Average value: 0.326 Grade Count:21
K (wear) Factor 6.04 - 894 x 10-8 mm³/N-M
3.00 - 444 x 10-10 in³-min/ft-lb-hr
Average value: 137 x 10<sup>-8</sup> mm³/N-M Grade Count:19
Taber Abrasion, mg/1000 Cycles 6.00
6.00
Average value: 6.00 Grade Count:5