Overview of materials for Nylon 66, 10% Mineral Filled

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Mineral Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Nylon 66, 10% Mineral Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 10% Mineral Filled". Specific grades with primary filler content between 5% and 14% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.10 - 1.60 g/cc
0.0397 - 0.0578 lb/in³
Average value: 1.33 g/cc Grade Count:12
Water Absorption 0.600 - 2.30 %
0.600 - 2.30 %
Average value: 1.34 % Grade Count:6
Moisture Absorption at Equilibrium 0.600 - 0.700 %
0.600 - 0.700 %
Average value: 0.633 % Grade Count:3
Water Absorption at Saturation 0.500 - 8.00 %
0.500 - 8.00 %
Average value: 5.00 % Grade Count:6
Linear Mold Shrinkage 0.00200 - 0.0250 cm/cm
0.00200 - 0.0250 in/in
Average value: 0.0122 cm/cm Grade Count:10
Mechanical Properties Metric English Comments
Hardness, Rockwell R 118 - 120
118 - 120
Average value: 119 Grade Count:4
Tensile Strength, Ultimate 48.0 - 90.0 MPa
6960 - 13100 psi
Average value: 72.6 MPa Grade Count:7
Tensile Strength, Yield 70.0 - 93.1 MPa
10200 - 13500 psi
Average value: 81.2 MPa Grade Count:4
Elongation at Break 1.00 - 14.0 %
1.00 - 14.0 %
Average value: 5.36 % Grade Count:9
Modulus of Elasticity 3.10 - 8.00 GPa
450 - 1160 ksi
Average value: 5.19 GPa Grade Count:8
Flexural Yield Strength 90.0 - 138 MPa
13100 - 20000 psi
Average value: 110 MPa Grade Count:8
Flexural Modulus 2.30 - 7.50 GPa
334 - 1090 ksi
Average value: 5.04 GPa Grade Count:7
Izod Impact, Notched 0.210 - 0.490 J/cm
0.393 - 0.919 ft-lb/in
Average value: 0.399 J/cm Grade Count:4
Izod Impact, Notched (ISO) 3.00 - 12.0 kJ/m²
1.43 - 5.71 ft-lb/in²
Average value: 6.00 kJ/m² Grade Count:4
3.00 - 4.00 kJ/m²

@Temperature -40.0 - -20.0 °C
1.43 - 1.90 ft-lb/in²

@Temperature -40.0 - -4.00 °F
Average value: 3.56 kJ/m² Grade Count:3
Izod Impact, Unnotched (ISO) 22.0 - 27.0 kJ/m²
10.5 - 12.8 ft-lb/in²
Average value: 24.3 kJ/m² Grade Count:3
22.0 - 27.0 kJ/m²

@Temperature -30.0 - -30.0 °C
10.5 - 12.8 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 24.3 kJ/m² Grade Count:3
Charpy Impact Unnotched 2.00 J/cm² - NB
9.52 ft-lb/in² - NB
Average value: 2.63 J/cm² Grade Count:6
2.50 J/cm² - NB

@Temperature -40.0 - -30.0 °C
11.9 ft-lb/in² - NB

@Temperature -40.0 - -22.0 °F
Average value: 2.83 J/cm² Grade Count:4
Charpy Impact, Notched 0.130 - 0.530 J/cm²
0.619 - 2.52 ft-lb/in²
Average value: 0.363 J/cm² Grade Count:6
0.300 - 0.460 J/cm²

@Temperature -40.0 - -30.0 °C
1.43 - 2.19 ft-lb/in²

@Temperature -40.0 - -22.0 °F
Average value: 0.388 J/cm² Grade Count:5
Taber Abrasion, mg/1000 Cycles 20.0 - 49.0
20.0 - 49.0
Average value: 34.3 Grade Count:3
Thermal Properties Metric English Comments
CTE, linear 30.6 - 60.0 µm/m-°C
17.0 - 33.3 µin/in-°F
Average value: 44.1 µm/m-°C Grade Count:5
CTE, linear, Transverse to Flow 45.0 - 68.0 µm/m-°C
25.0 - 37.8 µin/in-°F
Average value: 54.5 µm/m-°C Grade Count:4
Thermal Conductivity 0.350 W/m-K
2.43 BTU-in/hr-ft²-°F
Average value: 0.350 W/m-K Grade Count:3
Hot Ball Pressure Test 123 - 127 °C
253 - 261 °F
Average value: 125 °C Grade Count:3
Deflection Temperature at 0.46 MPa (66 psi) 200 - 252 °C
392 - 485 °F
Average value: 235 °C Grade Count:10
Deflection Temperature at 1.8 MPa (264 psi) 115 - 250 °C
239 - 482 °F
Average value: 181 °C Grade Count:9
Vicat Softening Point 234 - 323 °C
453 - 613 °F
Average value: 249 °C Grade Count:5
Flammability, UL94 HB - V-0
HB - V-0
Average value: 2.00 Grade Count:6
Oxygen Index 32.0 %
32.0 %
Average value: 32.0 % Grade Count:3
Glow Wire Test 960 °C
1760 °F
Average value: 960 °C Grade Count:3
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+8 - 1.00e+15 ohm-cm
1.00e+8 - 1.00e+15 ohm-cm
Average value: 8.57e+14 ohm-cm Grade Count:7
Surface Resistance 1.00e+8 - 1.00e+16 ohm
1.00e+8 - 1.00e+16 ohm
Average value: 7.50e+15 ohm Grade Count:4
Dielectric Constant 3.20 - 3.40
3.20 - 3.40
Average value: 3.30 Grade Count:3
Dielectric Strength 16.9 - 24.0 kV/mm
430 - 610 kV/in
Average value: 21.2 kV/mm Grade Count:4
Dissipation Factor 0.0104 - 0.0200
0.0104 - 0.0200
Average value: 0.0135 Grade Count:5
Comparative Tracking Index 425 - 600 V
425 - 600 V
Average value: 568 V Grade Count:6
Processing Properties Metric English Comments
Melt Temperature 260 - 300 °C
500 - 572 °F
Average value: 275 °C Grade Count:6
Mold Temperature 60.0 - 107 °C
140 - 225 °F
Average value: 80.0 °C Grade Count:6
Drying Temperature 75.0 - 107 °C
167 - 225 °F
Average value: 85.8 °C Grade Count:6
Moisture Content 0.200 %
0.200 %
Average value: 0.200 % Grade Count:4