Solvay TECHNYL® A 205F PA66, Conditioned

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer Solvay
Trade Name Technyl®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay TECHNYL® A 205F PA66, Conditioned.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: TECHNYL ® A 205F is an unreinforced polyamide 66 for injection molding. It is available in natural color.Benefits: The product offers two main advantages: excellent filling qualities and UL 94 V2 under 0.4 mm. It is particularly suitable for the molding of long parts with thin wall sections. Available in: Asia Pacific, Europe, Latin America and North AmericaRegulations compliance: Grades produced or imported in Europe comply with directive 453/2010/EC, which amends REACH directive 1907/2006/EC. This grade complies with RoHS directive 2002/95/EC. Unless specified, this grade is not suitable for food contact, medical devices or toy applications.Applications: Cable ties, fasteners or connectorsInformation provided by Rhodia, Rhodia has been acquired by Solvay.
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
ISO 1183/A
Mechanical Properties Metric English Comments
Tensile Strength at Break 40.0 MPa
5800 psi
ISO 527 Type 1A
Tensile Stress 5.00 MPa

@Strain 2.50 %,
Temperature 150 °C
725 psi

@Strain 2.50 %,
Temperature 302 °F
8.00 MPa

@Strain 2.50 %,
Temperature 120 °C
1160 psi

@Strain 2.50 %,
Temperature 248 °F
8.00 MPa

@Strain 5.00 %,
Temperature 150 °C
1160 psi

@Strain 5.00 %,
Temperature 302 °F
10.0 MPa

@Strain 2.50 %,
Temperature 80.0 °C
1450 psi

@Strain 2.50 %,
Temperature 176 °F
10.0 MPa

@Strain 5.00 %,
Temperature 120 °C
1450 psi

@Strain 5.00 %,
Temperature 248 °F
13.0 MPa

@Strain 10.0 %,
Temperature 150 °C
1890 psi

@Strain 10.0 %,
Temperature 302 °F
15.0 MPa

@Strain 2.50 %,
Temperature 23.0 °C
2180 psi

@Strain 2.50 %,
Temperature 73.4 °F
15.0 MPa

@Strain 5.00 %,
Temperature 80.0 °C
2180 psi

@Strain 5.00 %,
Temperature 176 °F
19.0 MPa

@Strain 20.0 %,
Temperature 150 °C
2760 psi

@Strain 20.0 %,
Temperature 302 °F
22.0 MPa

@Strain 10.0 %,
Temperature 80.0 °C
3190 psi

@Strain 10.0 %,
Temperature 176 °F
22.0 MPa

@Strain 20.0 %,
Temperature 120 °C
3190 psi

@Strain 20.0 %,
Temperature 248 °F
25.0 MPa

@Strain 2.50 %,
Temperature 0.000 °C
3630 psi

@Strain 2.50 %,
Temperature 32.0 °F
26.0 MPa

@Strain 5.00 %,
Temperature 23.0 °C
3770 psi

@Strain 5.00 %,
Temperature 73.4 °F
28.0 MPa

@Strain 10.0 %,
Temperature 120 °C
4060 psi

@Strain 10.0 %,
Temperature 248 °F
30.0 MPa

@Strain 20.0 %,
Temperature 80.0 °C
4350 psi

@Strain 20.0 %,
Temperature 176 °F
34.0 MPa

@Strain 20.0 %,
Temperature 23.0 °C
4930 psi

@Strain 20.0 %,
Temperature 73.4 °F
39.0 MPa

@Strain 10.0 %,
Temperature 23.0 °C
5660 psi

@Strain 10.0 %,
Temperature 73.4 °F
58.0 MPa

@Strain 5.00 %,
Temperature 0.000 °C
8410 psi

@Strain 5.00 %,
Temperature 32.0 °F
68.0 MPa

@Strain 10.0 %,
Temperature 0.000 °C
9860 psi

@Strain 10.0 %,
Temperature 32.0 °F
71.0 MPa

@Strain 20.0 %,
Temperature 0.000 °C
10300 psi

@Strain 20.0 %,
Temperature 32.0 °F
Tensile Strength, Yield 50.0 MPa
7250 psi
ISO 527 type 1 A
Elongation at Break 250 %
250 %
ISO 527 Type 1A
Elongation at Yield 10 %
10 %
ISO 527 type 1 A
Tensile Modulus 1.40 GPa
203 ksi
ISO 527 Type 1A
Flexural Strength 50.0 MPa
7250 psi
ISO 178
Flexural Modulus 1.30 GPa
189 ksi
ISO 178
Izod Impact, Notched (ISO) 8.00 kJ/m²
3.81 ft-lb/in²
ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
ISO 180/1U
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
ISO 179/1eA
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
IEC 60093
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
IEC 60093
Dielectric Constant 3.2
3.2
IEC 60250
Dielectric Strength 26.0 kV/mm
660 kV/in
IEC 60243
Dissipation Factor 0.050
0.050
IEC 60250
Comparative Tracking Index 600 V
600 V
Solution A; IEC 60112
Processing Properties Metric English Comments
Moisture Content <= 0.20 %
<= 0.20 %