BASF Ultrason S 2010 PSU

Category	Polymer , Thermoplastic , Polysulfone (PSU)
Manufacturer	BASF
Trade Name	Ultrason S
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultrason S 2010 PSU.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Ultrason S 2010 is an unreinforced, medium viscosity standard injection molding PSU grade. It flows readily and offers outstanding heat resistance and dimensional stability. It conforms to FDA requirements of 21 CFR 177.1655.

Physical Properties	Metric	English	Comments
Density	1.24 g/cc	0.0448 lb/in³	ISO 1183
Water Absorption	0.80 %	0.80 %	ISO 62
Moisture Absorption at Equilibrium	0.30 %	0.30 %	23°C/50% R.H.; ISO 62
Viscosity Test	63 cm³/g	63 cm³/g	Viscosity number
Linear Mold Shrinkage, Flow	0.0068 cm/cm	0.0068 in/in	ISO 294
Linear Mold Shrinkage, Transverse	0.0072 cm/cm	0.0072 in/in	ISO 294
Melt Flow	90 g/10 min @Load 10.0 kg, Temperature 360 °C	90 g/10 min @Load 22.0 lb, Temperature 680 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	135 MPa	19600 psi	ISO 11359-1/-2
Tensile Strength at Break	75.0 MPa	10900 psi	5mm/min; ISO 527-2
Tensile Strength, Yield	75.0 MPa	10900 psi	50mm/min; ISO 527-2
Elongation at Break	5.7 %	5.7 %	5mm/min; ISO 527-2
Elongation at Yield	5.7 %	5.7 %	50mm/min; ISO 527-2
Tensile Modulus	2.60 GPa	377 ksi	ISO 527-2
Shear Modulus	0.0250 GPa @Temperature 200 °C	3.63 ksi @Temperature 392 °F	ISO 6721
	0.800 GPa @Temperature 175 °C	116 ksi @Temperature 347 °F	ISO 6721
	0.900 GPa @Temperature 100 °C	131 ksi @Temperature 212 °F	ISO 6721
	0.950 GPa @Temperature 50.0 °C	138 ksi @Temperature 122 °F	ISO 6721
Izod Impact, Notched (ISO)	5.00 kJ/m²	2.38 ft-lb/in²	ISO 180/A
	6.00 kJ/m² @Temperature -30.0 °C	2.86 ft-lb/in² @Temperature -22.0 °F	ISO 180/A
Charpy Impact Unnotched	NB	NB	ISO 179/1eU
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	ISO 179/1eU
Charpy Impact, Notched	0.550 J/cm²	2.62 ft-lb/in²	ISO 179/1eA
	0.0600 J/cm² @Temperature -30.0 °C	0.286 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eA
Tensile Creep Modulus, 1000 hours	2500 MPa	363000 psi	elongation <0.5%, 23°C; ISO 899

Thermal Properties	Metric	English	Comments
CTE, linear	53.0 µm/m-°C @Temperature 26.0 °C	29.4 µin/in-°F @Temperature 78.8 °F	DIN 53752
	60.0 µm/m-°C @Temperature 125 °C	33.3 µin/in-°F @Temperature 257 °F	DIN 53752
	65.0 µm/m-°C @Temperature 175 °C	36.1 µin/in-°F @Temperature 347 °F	DIN 53752
CTE, linear, Parallel to Flow	53.0 µm/m-°C @Temperature 23.0 - 80.0 °C	29.4 µin/in-°F @Temperature 73.4 - 176 °F	ISO 11359-1/-2
	60.0 µm/m-°C @Temperature 140 - 180 °C	33.3 µin/in-°F @Temperature 284 - 356 °F	ISO 11359-1/-2
Maximum Service Temperature, Air	180 °C	356 °F	short cycle operations
Deflection Temperature at 1.8 MPa (264 psi)	167 °C	333 °F	ISO 75
Glass Transition Temp, Tg	187 °C	369 °F	ISO 11357-1/-3
UL RTI, Electrical	155 °C	311 °F	50% decrease of tensile strength after 20000h; 746B
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in
	V-2 @Thickness 3.20 mm	V-2 @Thickness 0.126 in

Optical Properties	Metric	English	Comments
Refractive Index	1.63	1.63
	1.63 @Wavelength 700 nm	1.63 @Wavelength 700 nm
	1.63 @Wavelength 550 nm	1.63 @Wavelength 550 nm
	1.64 @Wavelength 590 nm	1.64 @Wavelength 590 nm
	1.65 @Wavelength 540 nm	1.65 @Wavelength 540 nm
	1.66 @Wavelength 450 nm	1.66 @Wavelength 450 nm
Transmission, Visible	89 % @Thickness 2.00 mm	89 % @Thickness 0.0787 in	ASTM D 1003
	75 % @Wavelength 400 nm	75 % @Wavelength 400 nm
	85 % @Wavelength 500 nm	85 % @Wavelength 500 nm
	85 % @Wavelength 600 nm	85 % @Wavelength 600 nm
UV Transmittance	3.0 % @Wavelength 300 nm	3.0 % @Wavelength 300 nm
	15 % @Wavelength 200 nm	15 % @Wavelength 200 nm
	40 % @Wavelength 350 nm	40 % @Wavelength 350 nm

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+13 ohm-cm	>= 1.00e+13 ohm-cm	IEC 60093
Surface Resistance	>= 1.00e+14 ohm	>= 1.00e+14 ohm	IEC 60093
Dielectric Constant	3.1 @Frequency 100 Hz	3.1 @Frequency 100 Hz	IEC 60250
	3.1 @Frequency 1.00e+6 Hz	3.1 @Frequency 1.00e+6 Hz	IEC 60250
Dielectric Strength	40.0 kV/mm	1020 kV/in	IEC 60243-1 3
Dissipation Factor	0.00080 @Frequency 100 Hz	0.00080 @Frequency 100 Hz	IEC 60250
	0.0064 @Frequency 1.00e+6 Hz	0.0064 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	125 V	125 V	Test Liquid A & B; IEC 60112

Processing Properties	Metric	English	Comments
Adapter Temperature	300 °C	572 °F
Die Temperature	310 °C	590 °F
Melt Temperature	330 - 390 °C	626 - 734 °F	Injection molding
Mold Temperature	120 - 160 °C	248 - 320 °F	Injection molding
Die Opening	110 cm	43.3 in

Descriptive Properties	Value	Comments
Color	Natural
Commercial Status	North America and Europe
FDA	21 CFR 177.1655
Impact Modified	No
NSF Std. 61	Yes
Primary Processing Technique	Injection Molding, Extrusion and Blow Molding