LG Chemical LUMID HI5006A(W) PA6/ABS, High Impact, Good Dimensional Stability
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade |
| Manufacturer | LG Chemical |
| Trade Name | LUMID |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUMID HI5006A(W) PA6/ABS, High Impact, Good Dimensional Stability.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Injection Molding, PA6/ABS, High Impact, Good Dimensional StabilityApplication: Pipe Fitting, Electrical and Electronic partsCAS No. 25038-54-4, 9003-56-9 and 9003-54-7Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM D792 |
| Water Absorption | 0.70 % | 0.70 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.012 cm/cm @Thickness 3.20 mm |
0.0080 - 0.012 in/in @Thickness 0.126 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 44.1 MPa @Thickness 3.20 mm |
6400 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 100 % @Thickness 3.20 mm |
100 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 58.8 MPa @Thickness 3.20 mm |
8530 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Flexural Modulus | 1.57 GPa @Thickness 3.20 mm |
228 ksi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Izod Impact, Notched | 6.86 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
12.9 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C | 44.4 µin/in-°F | ASTM D696 |
| Melting Point | 220 °C | 428 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C @Thickness 6.40 mm |
230 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C @Thickness 6.40 mm |
176 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 2.9 @Frequency 1.00e+6 Hz |
2.9 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 26.0 kV/mm @Thickness 1.00 mm |
660 kV/in @Thickness 0.0394 in |
ASTM D419 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 235 - 250 °C | 455 - 482 °F | Injection Molding |
| Middle Barrel Temperature | 240 - 260 °C | 464 - 500 °F | Injection Molding |
| Front Barrel Temperature | 240 - 260 °C | 464 - 500 °F | Injection Molding |
| Nozzle Temperature | 250 - 265 °C | 482 - 509 °F | Injection Molding |
| Melt Temperature | 250 - 265 °C | 482 - 509 °F | Injection Molding |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Drying Temperature | 70.0 - 90.0 °C | 158 - 194 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |
Users viewing this material also viewed the following:
- MV Labs GD1000 Gd2(SO4)3·xH2O Gadolinium sulfate octahydrate
- MV Labs TA560 K2TaF7 Potassium heptafluorotantalate(V)
- NOVA Chemicals Sclair® FG220-A Octene LLDPE Film Resin
- SABIC Innovative Plastics LNP LUBRICOMP DL003 PC
- LATI LATAMID 12 H FE90 Nylon 12 Base Magnetizable Compound (Unverified Data**)
- Karina E 36/209-GIN Reddy Brown MB (SP31455) for PVC
- Breplast Bretene PP Polypropylene Composite
- Addiplast Addinyl A2 X Nylon 66
- Polykemi AB POLYfill PPH TS4020 Polypropylene Homopolymer, Mineral Reinforced
Copyright © lookpolymers.com All Rights Reserved