Lanxess Durethan® A 30 S 000000 Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® A 30 S 000000 Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 66 standard injection molding-grade, non-reinforced, good demolding, very rapid solidificationApplication Examples: plug connectors, terminal blocks, cable clips, bobbins
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.136 g/cc | 0.04104 lb/in³ | ISO 1183 |
| Water Absorption | 8.5 % | 8.5 % | Test Sim. to ISO 62 |
| Moisture Absorption at Equilibrium | 2.8 % | 2.8 % | 23°C/50% R.H.; Test Sim. to ISO 62 |
| Viscosity Test | 144 cm³/g | 144 cm³/g | Viscosity number; ISO 307, 1157, 1628 |
| Melt Flow | 75 g/10 min @Load 5.00 kg, Temperature 270 °C |
75 g/10 min @Load 11.0 lb, Temperature 518 °F |
Calculated from MVR using melt density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | Conditioned; ISO 527-1/-2 |
| 95.0 MPa | 13800 psi | ISO 527-1/-2 | |
| Elongation at Yield | 4.5 % | 4.5 % | ISO 527-1/-2 |
| 18 % | 18 % | Conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 1.60 GPa | 232 ksi | Conditioned; ISO 527-1/-2 |
| 3.60 GPa | 522 ksi | ISO 527-1/-2 | |
| Charpy Impact Unnotched | 10.0 J/cm² @Temperature -30.0 °C |
47.6 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 15.0 J/cm² @Temperature -30.0 °C |
71.4 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eU | |
| 15.0 J/cm² @Temperature 23.0 °C |
71.4 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eA | |
| <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |
| 1.20 J/cm² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eA | |
| Impact | 4620 | 4620 | Puncture maximum force, Conditioned (N); ISO 6603-2 |
| 5505 | 5505 | Puncture maximum force (N); ISO 6603-2 | |
| 6143 @Temperature -30.0 °C |
6143 @Temperature -22.0 °F |
Puncture maximum force (N); ISO 6603-2 | |
| Puncture Energy | 27.0 J | 19.9 ft-lb | Conditioned; ISO 6603-2 |
| 30.0 J | 22.1 ft-lb | ISO 6603-2 | |
| 26.0 J @Temperature -30.0 °C |
19.2 ft-lb @Temperature -22.0 °F |
ISO 6603-2 | |
| 26.0 J @Temperature -30.0 °C |
19.2 ft-lb @Temperature -22.0 °F |
Conditioned; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 263 °C | 505 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 55.0 °C | 131 °F | ISO 75-1/-2 |
| Vicat Softening Point | 230 °C | 446 °F | 50°C/h 50N; ISO 306 |
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
IEC 60695-11-10 |
| V-2 @Thickness 3.20 mm |
V-2 @Thickness 0.126 in |
IEC 60695-11-10 | |
| Oxygen Index | 26 % | 26 % | ISO 4589-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | Conditioned; IEC 60093 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 |
| Dielectric Constant | 3.4 @Frequency 1.00e+6 Hz |
3.4 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.8 @Frequency 100 Hz |
3.8 @Frequency 100 Hz |
IEC 60250 | |
| 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 | |
| 10 @Frequency 100 Hz |
10 @Frequency 100 Hz |
Conditioned; IEC 60250 | |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 60243-1 |
| 30.0 kV/mm | 762 kV/in | Conditioned; IEC 60243-1 | |
| Dissipation Factor | 0.0060 @Frequency 100 Hz |
0.0060 @Frequency 100 Hz |
IEC 60250 |
| 0.018 @Frequency 1.00e+6 Hz |
0.018 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| 0.070 @Frequency 1.00e+6 Hz |
0.070 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 | |
| 0.14 @Frequency 100 Hz |
0.14 @Frequency 100 Hz |
Conditioned; IEC 60250 | |
| Comparative Tracking Index | 575 V | 575 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Release agent | |
| Form | Pellets | |
| ISO Shortname | ISO 1874-PA 66,MR,14-040 | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Hogen HM1150 Tungsten-Based Metal
- ICO Polymers ICORENEâ„¢ 190-1329 LMDPE Rotational Molding Resin
- IDI Composites M-106 Thermoset Polyester, Molding
- SABIC Innovative Plastics Noryl GTX GTX8430W PPE+PA
- Saint-Gobain Normount® V1300 White Polyurethane Foam Bonding Tape for Interior Use
- ExxonMobil SpectraSyn Elite™ 150 Metallocene Polyalphaolefin (mPAO) Fluid
- Eurotec® Tecopet® PT70 KK45 PET, 45% glass fiber/mineral reinforced, flame retardant - halogen (RoHS compliant), heat stabilized, natural
- 3M FM012 Indoor UL Recognized Clear Polyester Overlaminate Label Product
- Polimeri Europa Extir® LN 2000 Expandable Polystyrene
Copyright © lookpolymers.com All Rights Reserved