Lanxess Durethan® BKV 325 Z H2.0 901510 Nylon 6, 25% Glass Fibers
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® BKV 325 Z H2.0 901510 Nylon 6, 25% Glass Fibers.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, 25% glass fibers, blow molding, impact modified, heat-ageing stabilized
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.283 g/cc | 1.283 g/cc | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm @Thickness 2.00 mm |
0.0060 in/in @Thickness 0.0787 in |
Mold Temp 80°C; Melt Temp 280°C; 600 bar; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm @Thickness 2.00 mm |
0.0060 in/in @Thickness 0.0787 in |
Mold Temp 80°C; Melt Temp 280°C; 600 bar; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 70.0 MPa | 10200 psi | Conditioned; ISO 527-1,-2 |
| 130 MPa | 18900 psi | ISO 527-1,-2 | |
| Elongation at Break | 3.5 % | 3.5 % | ISO 527-1,-2 |
| 10 % | 10 % | Conditioned; ISO 527-1,-2 | |
| Tensile Modulus | 4.00 GPa | 580 ksi | Conditioned; ISO 527-1,-2 |
| 7.50 GPa | 1090 ksi | ISO 527-1,-2 | |
| Flexural Strength | 100 MPa @Strain 6.50 % |
14500 psi @Strain 6.50 % |
Conditioned; ISO 178 |
| 200 MPa @Strain 4.50 % |
29000 psi @Strain 4.50 % |
ISO 178 | |
| Flexural Yield Strength | 85.0 MPa @Strain 3.50 % |
12300 psi @Strain 3.50 % |
Conditioned; ISO 178 |
| 180 MPa @Strain 3.50 % |
26100 psi @Strain 3.50 % |
ISO 178 | |
| Flexural Modulus | 3.40 GPa | 493 ksi | Conditioned; ISO 178 |
| 6.50 GPa | 943 ksi | ISO 178 | |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1A |
| 25.0 kJ/m² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 180-1A | |
| Izod Impact, Unnotched (ISO) | 55.0 kJ/m² @Temperature 23.0 °C |
26.2 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1U |
| 60.0 kJ/m² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 180-1U | |
| 70.0 kJ/m² @Temperature -30.0 °C |
33.3 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1U | |
| 75.0 kJ/m² @Temperature 23.0 °C |
35.7 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 180-1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 218 °C | 424 °F | ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75-1,-2 |
| Deflection Temperature at 8.0 MPa | 80.0 °C | 176 °F | ISO 75-1,-2 |
| Shrinkage | 0.10 % @Temperature 120 °C, Time 14400 sec |
0.10 % @Temperature 248 °F, Time 4.00 hour |
Molding Post-shrinkage; ISO 294-4 |
| 0.10 % @Temperature 120 °C, Time 14400 sec |
0.10 % @Temperature 248 °F, Time 4.00 hour |
Molding Post-shrinkage; ISO 294-4 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 °C | 536 °F | Processing conditions for test specimens; ISO 294 |
| 270 - 290 °C | 518 - 554 °F | Recommended | |
| Mold Temperature | 80.0 °C | 176 °F | Processing conditions for test specimens; ISO 294 |
| 80.0 - 120 °C | 176 - 248 °F | Recommended | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2 - 6 hour | 2 - 6 hour | |
| Moisture Content | 0.030 - 1.12 % | 0.030 - 1.12 % | Residual; Acc. To Karl Fischer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shortname | ISO 1874-PA 6-HI,BHR,14-070,GF25 |
Users viewing this material also viewed the following:
- Premix Thermoplastics PRE-ELEC® PC 1431
- Industrial Laminates/Norplex NP344 Cotton Fabric
- Suzhou Hipro Polymers Hiprolon® 400 MC HLS G30 Nylon, 30% glass fiber filled
- Toyobo GLAMIDE® TY-145TZ Nylon-6
- DSM Akulon® K222-KGV4 Nylon 6-20% Glass Reinforced (European and Asian Grade) (Dry)
- Arlon R35928R025 0.025" (0.635 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- A. Schulman ComAlloy Hiloy® 513 Polycarbonate, Glass Reinforced, UL
- Carpenter Extendo-Die® Hot Work Die Steel, Tempered 621°C
- PolyOne Synprene® RT-3860E Thermoplastic Elastomer - SBC (discontinued **)
Copyright © lookpolymers.com All Rights Reserved