Lehmann & Voss LUVOCOM® 1/CF/10/GK/20/TF/5/BK Polyamide 66, with carbon fiber, glass spheres and PTFE, heat stabilized
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass/Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1/CF/10/GK/20/TF/5/BK Polyamide 66, with carbon fiber, glass spheres and PTFE, heat stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Improved friction and wear behaviour. Emergency running property.Electrically conductive, suitable for continuous discharging of statically generated electricity.High dimensionally stable precision parts, even at elevated temperatures and narrow tolerance range.Gear parts for automotive appliances, control disks, cams, sliding elements.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.36 g/cc | 1.36 g/cc | ISO 1183 |
| Water Absorption | <= 1.0 % | <= 1.0 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 170 MPa | 24700 psi | |
| Elongation at Yield | 2.5 % | 2.5 % | |
| 3.4 % | 3.4 % | flexural | |
| Modulus of Elasticity | 11.0 GPa | 1600 ksi | |
| Flexural Strength | 255 MPa | 37000 psi | |
| Flexural Modulus | 9.00 GPa | 1310 ksi | |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | flatwise; ISO 179 1fU |
| Coefficient of Friction, Dynamic | 0.20 | 0.20 | |
| Coefficient of Friction, Static | 0.17 | 0.17 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 µm/m-°C | 16.7 µin/in-°F | DIN 53752 |
| Thermal Conductivity | 0.400 W/m-K | 2.78 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 120 °C | 248 °F | |
| 160 °C | 320 °F | short term | |
| Vicat Softening Point | 253 °C | 487 °F | DIN ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 10000 ohm | 10000 ohm | |
| Insulation Resistance | 1000 ohm | 1000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 290 °C | 554 °F | mass temp |
| Nozzle Temperature | 280 - 300 °C | 536 - 572 °F | |
| Zone 1 | 290 - 310 °C | 554 - 590 °F | |
| Zone 2 | 290 - 310 °C | 554 - 590 °F | |
| Zone 3 | 290 - 310 °C | 554 - 590 °F | |
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F | |
| Drying Temperature | 75.0 °C @Time 21600 - 57600 sec |
167 °F @Time 6.00 - 16.0 hour |
Dehumidifying dryer |
| 105 °C @Time 14400 - 21600 sec |
221 °F @Time 4.00 - 6.00 hour |
Vacuum Dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black |
Users viewing this material also viewed the following:
- Network Polymers PC-1011 L
- Solvay Engineered Polymers DEXFLEX® 810HSF TPO (discontinued **)
- Eastman 1810E Polyethylene (discontinued **)
- A. Schulman SCHULAMID® 66 GF50 50% Glass Fiber Reinforced 66
- Westlake Elevate™ EF545 4% Ethylene Vinyl Acetate Copolymer
- DuPont™ Kapton® 300KN Polyimide Film, 75 Micron Thickness
- Dow TUFLIN™ HS-7046 NT 7 Linear Low Density Polyethylene Resin
- Solvay RHODAPON® LS-92/RN Surfactant
- Plastcom SLOVALEN PH 51 T 10 Polypropylene Homopolymer, 10% Mineral Filled
Copyright © lookpolymers.com All Rights Reserved