Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Plating Grade

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Plating Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Plating Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), Plating Grade". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.03 - 2.50 g/cc
0.0372 - 0.0903 lb/in³
Average value: 1.11 g/cc Grade Count:25
Water Absorption 0.200 - 1.00 %
0.200 - 1.00 %
Average value: 0.400 % Grade Count:6
Linear Mold Shrinkage 0.00300 - 0.00800 cm/cm
0.00300 - 0.00800 in/in
Average value: 0.00537 cm/cm Grade Count:18
Linear Mold Shrinkage, Transverse 0.00400 - 0.00800 cm/cm
0.00400 - 0.00800 in/in
Average value: 0.00583 cm/cm Grade Count:3
Melt Flow 1.20 - 45.0 g/10 min
1.20 - 45.0 g/10 min
Average value: 13.5 g/10 min Grade Count:24
Mechanical Properties Metric English Comments
Hardness, Rockwell R 101 - 112
101 - 112
Average value: 107 Grade Count:17
Tensile Strength, Ultimate 20.0 - 46.0 MPa
2900 - 6670 psi
Average value: 37.5 MPa Grade Count:16
Tensile Strength, Yield 36.0 - 54.0 MPa
5220 - 7830 psi
Average value: 44.1 MPa Grade Count:19
Elongation at Break 3.00 - 40.0 %
3.00 - 40.0 %
Average value: 24.3 % Grade Count:18
Elongation at Yield 2.00 - 6.00 %
2.00 - 6.00 %
Average value: 3.30 % Grade Count:8
Modulus of Elasticity 1.70 - 2.62 GPa
247 - 380 ksi
Average value: 2.26 GPa Grade Count:10
Flexural Yield Strength 56.0 - 82.0 MPa
8120 - 11900 psi
Average value: 68.8 MPa Grade Count:19
Flexural Modulus 1.96 - 5.47 GPa
284 - 793 ksi
Average value: 2.44 GPa Grade Count:25
Izod Impact, Notched 0.230 - 5.82 J/cm
0.431 - 10.9 ft-lb/in
Average value: 2.65 J/cm Grade Count:20
0.5339 - 3.50 J/cm

@Temperature -40.0 - 0.000 °C
1.000 - 6.56 ft-lb/in

@Temperature -40.0 - 32.0 °F
Average value: 1.23 J/cm Grade Count:2
0.784532 - 0.882598 J/cm

@Temperature -30.0 - -30.0 °C
1.46975 - 1.65347 ft-lb/in

@Temperature -22.0 - -22.0 °F
Average value: 1.23 J/cm Grade Count:1
0.784532 - 0.882598 J/cm

@Thickness 3.17 - 6.35 mm
1.46975 - 1.65347 ft-lb/in

@Thickness 0.125 - 0.250 in
Average value: 1.23 J/cm Grade Count:1
Izod Impact, Unnotched 1.471 - 1.56906 J/cm

@Temperature -30.0 - -30.0 °C
2.756 - 2.93950 ft-lb/in

@Temperature -22.0 - -22.0 °F
Average value: 1.52 J/cm Grade Count:1
1.471 - 1.56906 J/cm

@Thickness 3.20 - 6.40 mm
2.756 - 2.93950 ft-lb/in

@Thickness 0.126 - 0.252 in
Average value: 1.52 J/cm Grade Count:1
Izod Impact, Notched (ISO) 16.0 - 28.0 kJ/m²
7.61 - 13.3 ft-lb/in²
Average value: 20.7 kJ/m² Grade Count:6
6.00 - 13.0 kJ/m²

@Temperature -30.0 - -20.0 °C
2.86 - 6.19 ft-lb/in²

@Temperature -22.0 - -4.00 °F
Average value: 8.67 kJ/m² Grade Count:4
Charpy Impact Unnotched 17.0 J/cm² - NB
80.9 ft-lb/in² - NB
Average value: 17.0 J/cm² Grade Count:3
1.00 - 11.0 J/cm²

@Temperature -30.0 - -30.0 °C
4.76 - 52.4 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 6.00 J/cm² Grade Count:2
Charpy Impact, Notched 1.60 - 2.60 J/cm²
7.61 - 12.4 ft-lb/in²
Average value: 2.00 J/cm² Grade Count:7
0.600 - 1.20 J/cm²

@Temperature -30.0 - -20.0 °C
2.86 - 5.71 ft-lb/in²

@Temperature -22.0 - -4.00 °F
Average value: 0.875 J/cm² Grade Count:4
Thermal Properties Metric English Comments
CTE, linear 80.0 - 100 µm/m-°C
44.4 - 55.6 µin/in-°F
Average value: 90.0 µm/m-°C Grade Count:4
Deflection Temperature at 0.46 MPa (66 psi) 87.8 - 106 °C
190 - 223 °F
Average value: 94.4 °C Grade Count:12
Deflection Temperature at 1.8 MPa (264 psi) 76.1 - 203 °C
169 - 397 °F
Average value: 94.0 °C Grade Count:25
Vicat Softening Point 94.0 - 115 °C
201 - 239 °F
Average value: 100 °C Grade Count:21
UL RTI, Electrical 60.0 - 80.0 °C
140 - 176 °F
Average value: 63.3 °C Grade Count:4
UL RTI, Mechanical with Impact 60.0 - 80.0 °C
140 - 176 °F
Average value: 63.3 °C Grade Count:4
UL RTI, Mechanical without Impact 60.0 - 80.0 °C
140 - 176 °F
Average value: 63.3 °C Grade Count:4
Flammability, UL94 HB
HB
Grade Count:22
Glow Wire Test 650 °C
1200 °F
Average value: 650 °C Grade Count:3
Optical Properties Metric English Comments
Gloss 90.0 - 98.0 %
90.0 - 98.0 %
Average value: 94.7 % Grade Count:3
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+14 - 1.00e+16 ohm-cm
1.00e+14 - 1.00e+16 ohm-cm
Average value: 4.73e+15 ohm-cm Grade Count:7
Surface Resistance 1.00e+14 - 1.00e+16 ohm
1.00e+14 - 1.00e+16 ohm
Average value: 3.02e+15 ohm Grade Count:4
Dielectric Constant 2.60 - 3.00
2.60 - 3.00
Average value: 2.81 Grade Count:4
Dielectric Strength 18.0 - 38.0 kV/mm
457 - 965 kV/in
Average value: 29.9 kV/mm Grade Count:5
Dissipation Factor 0.00400 - 0.0150
0.00400 - 0.0150
Average value: 0.00771 Grade Count:4
Comparative Tracking Index 600 V
600 V
Average value: 600 V Grade Count:4
Processing Properties Metric English Comments
Melt Temperature 188 - 265 °C
370 - 509 °F
Average value: 220 °C Grade Count:12
Mold Temperature 40.0 - 85.0 °C
104 - 185 °F
Average value: 63.0 °C Grade Count:12
Drying Temperature 70.0 - 93.3 °C
158 - 200 °F
Average value: 83.4 °C Grade Count:12
Injection Pressure 4.83 - 150 MPa
700 - 21800 psi
Average value: 61.7 MPa Grade Count:8