Ascend Performance Materials Vydyne® 909 BK Nylon 66/6, 25% Glass Reinforced, DAM

Category Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, 30% Glass Fiber Reinforced
Manufacturer Ascend Performance Materials (formerly Solutia)
Trade Name VYDYNE®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ascend Performance Materials Vydyne® 909 BK Nylon 66/6, 25% Glass Reinforced, DAM.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Vydyne® 909 BK is a halogenated, 25% glass-filled, flame-retardant PA66/6 copolymer with excellent strength and toughness. It is lubricated for machine feed and easy mold release and has Underwriters Laboratories UL 94 flammability classification of V-0 at 0.4 mm (0.016”) thick.Availability:Asia PacificEuropeNorth AmericaFiller/Reinforcement:Glass Fiber, 25% Filler by WeightAdditive:HalogenLubricant Features:Flame RetardantGood Crack ResistanceGood Mold ReleaseGood ToughnessHalogenatedHigh RigidityHigh Strength Ignition ResistantLubricatedUses:AppliancesAutomotive ElectronicsBobbinsConnectorsElectrical HousingElectrical PartsElectrical/Electronic ApplicationsFastenersIndustrial ApplicationsLighting ApplicationsLiving HingesPrinted Circuit BoardsSwitchesAppearance: BlackForms: PelletsProcessing Method: Injection MoldingInformation provided by Ascend Performance Materials.
Physical Properties Metric English Comments
Density 1.47 g/cc
0.0531 lb/in³
ISO 1183
Water Absorption 0.70 %

@Time 86400 sec
0.70 %

@Time 24.0 hour
ISO 62
Moisture Absorption at Equilibrium 1.3 %
1.3 %
50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0040 cm/cm

@Diameter 2.00 mm
0.0040 in/in

@Diameter 0.0787 in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.010 cm/cm

@Diameter 2.00 mm
0.010 in/in

@Diameter 0.0787 in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 2.20 MPa
319 psi
ISO 527-2
Tensile Strength, Yield 132 MPa
19100 psi
ISO 527-2
Tensile Modulus 9.10 GPa
1320 ksi
ISO 527-2
Flexural Strength 193 MPa
28000 psi
ISO 178
Flexural Modulus 8.30 GPa
1200 ksi
ISO 178
Poissons Ratio 0.40
0.40
ISO 527-2
Izod Impact, Notched (ISO) 9.00 kJ/m²
4.28 ft-lb/in²
ISO 180
Charpy Impact Unnotched 3.50 J/cm²

@Temperature -30.0 °C
16.7 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
4.00 J/cm²

@Temperature 23.0 °C
19.0 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.940 J/cm²

@Temperature 23.0 °C
4.47 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
0.950 J/cm²

@Temperature -30.0 °C
4.52 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 2.00 µm/m-°C

@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C
1.11 µin/in-°F

@Thickness 0.0787 in,
Temperature 73.4 - 131 °F
ISO 11359-2
CTE, linear, Transverse to Flow 10.0 µm/m-°C

@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C
5.56 µin/in-°F

@Thickness 0.0787 in,
Temperature 73.4 - 131 °F
ISO 11359-2
Melting Point 250 °C
482 °F
ISO 11357-3
Deflection Temperature at 0.46 MPa (66 psi) 250 °C
482 °F
Unannealed; ISO 75-2/B
Deflection Temperature at 1.8 MPa (264 psi) 230 °C
446 °F
Unannealed; ISO 75-2/A
UL RTI, Electrical 65.0 °C

@Thickness 0.400 mm
149 °F

@Thickness 0.0157 in
UL 746
130 °C

@Thickness 0.750 mm
266 °F

@Thickness 0.0295 in
UL 746
130 °C

@Thickness 1.50 mm
266 °F

@Thickness 0.0591 in
UL 746
130 °C

@Thickness 3.00 mm
266 °F

@Thickness 0.118 in
UL 746
UL RTI, Mechanical with Impact 65.0 °C

@Thickness 0.400 mm
149 °F

@Thickness 0.0157 in
UL 746
65.0 °C

@Thickness 0.750 mm
149 °F

@Thickness 0.0295 in
UL 746
95.0 °C

@Thickness 1.50 mm
203 °F

@Thickness 0.0591 in
UL 746
95.0 °C

@Thickness 3.00 mm
203 °F

@Thickness 0.118 in
UL 746
UL RTI, Mechanical without Impact 65.0 °C

@Thickness 0.400 mm
149 °F

@Thickness 0.0157 in
UL 746
110 °C

@Thickness 0.750 mm
230 °F

@Thickness 0.0295 in
UL 746
110 °C

@Thickness 1.50 mm
230 °F

@Thickness 0.0591 in
UL 746
110 °C

@Thickness 3.00 mm
230 °F

@Thickness 0.118 in
UL 746
Flammability, UL94 V-0

@Thickness 0.400 mm
V-0

@Thickness 0.0157 in
V-0

@Thickness 0.750 mm
V-0

@Thickness 0.0295 in
V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
V-0

@Thickness 3.00 mm
V-0

@Thickness 0.118 in
Oxygen Index 32 %
32 %
ISO 4589-2
Glow Wire Test 750 °C

@Thickness 0.750 mm
1380 °F

@Thickness 0.0295 in
Ignition Temperature; IEC 60695-2-13
750 °C

@Thickness 1.50 mm
1380 °F

@Thickness 0.0591 in
Ignition Temperature; IEC 60695-2-13
800 °C

@Thickness 3.00 mm
1470 °F

@Thickness 0.118 in
Ignition Temperature; IEC 60695-2-13
930 °C

@Thickness 0.400 mm
1710 °F

@Thickness 0.0157 in
Ignition Temperature; IEC 60695-2-13
960 °C

@Thickness 0.400 mm
1760 °F

@Thickness 0.0157 in
Flammability Index; IEC 60695-2-12
960 °C

@Thickness 0.750 mm
1760 °F

@Thickness 0.0295 in
Flammability Index; IEC 60695-2-12
960 °C

@Thickness 1.50 mm
1760 °F

@Thickness 0.0591 in
Flammability Index; IEC 60695-2-12
960 °C

@Thickness 3.00 mm
1760 °F

@Thickness 0.118 in
Flammability Index; IEC 60695-2-12
Electrical Properties Metric English Comments
Arc Resistance 60 - 119 sec

@Thickness 3.00 mm
60 - 119 sec

@Thickness 0.118 in
ASTM D495
Comparative Tracking Index 250 - 399 V

@Thickness 3.00 mm
250 - 399 V

@Thickness 0.118 in
IEC 60112
Hot Wire Ignition, HWI >= 120 sec

@Thickness 0.750 mm
>= 120 sec

@Thickness 0.0295 in
UL 746
>= 120 sec

@Thickness 1.50 mm
>= 120 sec

@Thickness 0.0591 in
UL 746
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 1.50 mm
>= 120 arcs

@Thickness 0.0591 in
UL 746
>= 120 arcs

@Thickness 3.00 mm
>= 120 arcs

@Thickness 0.118 in
UL 746
High Voltage Arc-Tracking Rate, HVTR 80.1 - 150 mm/min

@Thickness 3.00 mm
3.15 - 5.91 in/min

@Thickness 0.118 in
UL 746
Processing Properties Metric English Comments
Rear Barrel Temperature 240 - 270 °C
464 - 518 °F
Middle Barrel Temperature 240 - 270 °C
464 - 518 °F
Front Barrel Temperature 240 - 270 °C
464 - 518 °F
Nozzle Temperature 240 - 270 °C
464 - 518 °F
Melt Temperature 250 - 270 °C
482 - 518 °F
Mold Temperature 65.0 - 95.0 °C
149 - 203 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 4.00 hour
4.00 hour
Descriptive Properties Value Comments
Suggested Max Regrind 25 %