Overview of materials for Modified ETFE, Unreinforced

Category Polymer , Thermoplastic , Fluoropolymer , ETFE/ECTFE , Modified ETFE, Unreinforced
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Modified ETFE, Unreinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Modified ETFE, Unreinforced". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.59 - 1.86 g/cc
0.0574 - 0.0672 lb/in³
Average value: 1.75 g/cc Grade Count:15
Water Absorption 0.00500 - 0.100 %
0.00500 - 0.100 %
Average value: 0.0914 % Grade Count:11
Oxygen Transmission 70.0 cc-mm/m²-24hr-atm
178 cc-mil/100 in²-24hr-atm
Average value: 70.0 cc-mm/m²-24hr-atm Grade Count:14
Nitrogen Transmission 20.0 - 104 cc-mm/m²-24hr-atm
50.8 - 263 cc-mil/100 in²-24hr-atm
Average value: 32.0 cc-mm/m²-24hr-atm Grade Count:14
Viscosity 1.00e+6 - 1.00e+7 cP

@Temperature 300 - 330 °C
1.00e+6 - 1.00e+7 cP

@Temperature 572 - 626 °F
Average value: 5.50e+6 cP Grade Count:10
Linear Mold Shrinkage 0.0300 - 0.0400 cm/cm
0.0300 - 0.0400 in/in
Average value: 0.0350 cm/cm Grade Count:10
Melt Flow 2.00 - 50.0 g/10 min
2.00 - 50.0 g/10 min
Average value: 17.8 g/10 min Grade Count:16
Mechanical Properties Metric English Comments
Hardness, Shore D 75.0
75.0
Average value: 75.0 Grade Count:10
Tensile Strength, Ultimate 35.0 - 50.0 MPa
5080 - 7250 psi
Average value: 43.8 MPa Grade Count:16
Elongation at Break 300 - 460 %
300 - 460 %
Average value: 418 % Grade Count:17
Modulus of Elasticity 0.490 - 0.827 GPa
71.1 - 120 ksi
Average value: 0.654 GPa Grade Count:11
Flexural Modulus 0.647 - 1.37 GPa
93.8 - 199 ksi
Average value: 1.06 GPa Grade Count:15
Compressive Yield Strength 11.0 MPa
1600 psi
Average value: 11.0 MPa Grade Count:10
Izod Impact, Notched 100 - 5340 J/cm
187 - 10000 ft-lb/in
Grade Count:4
Izod Impact, Unnotched NB
NB
Grade Count:10
Coefficient of Friction 0.0550 - 0.0780
0.0550 - 0.0780
Average value: 0.0665 Grade Count:10
Coefficient of Friction, Static 0.0600
0.0600
Average value: 0.0600 Grade Count:10
Taber Abrasion, mg/1000 Cycles 127 - 149
127 - 149
Average value: 141 Grade Count:10
Thermal Properties Metric English Comments
CTE, linear 50.0 - 131 µm/m-°C
27.8 - 73.0 µin/in-°F
Average value: 75.6 µm/m-°C Grade Count:11
Thermal Conductivity 0.240 W/m-K
1.67 BTU-in/hr-ft²-°F
Average value: 0.240 W/m-K Grade Count:10
Melting Point 160 - 266 °C
320 - 510 °F
Average value: 233 °C Grade Count:15
Maximum Service Temperature, Air 150 - 154 °C
302 - 310 °F
Average value: 150 °C Grade Count:11
Flammability, UL94 V-0
V-0
Grade Count:17
Oxygen Index 31.0 - 40.0 %
31.0 - 40.0 %
Average value: 31.5 % Grade Count:17
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
Average value: 1.00e+16 ohm-cm Grade Count:10
Dielectric Constant 2.40 - 2.75
2.40 - 2.75
Average value: 2.58 Grade Count:17
Dielectric Strength 7.87 - 16.0 kV/mm
200 - 406 kV/in
Average value: 15.3 kV/mm Grade Count:11
Dissipation Factor 0.000400 - 0.00820
0.000400 - 0.00820
Average value: 0.00281 Grade Count:16