Overview of materials for Nylon 66, 10% Carbon Fiber Filled

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Carbon Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Nylon 66, 10% Carbon Fiber Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 10% Carbon Fiber Filled". Specific grades with carbon fiber content between 5% and 14% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.10 - 1.45 g/cc
0.0397 - 0.0524 lb/in³
Average value: 1.24 g/cc Grade Count:53
Filler Content 5.00 - 10.0 %
5.00 - 10.0 %
Average value: 8.75 % Grade Count:4
Water Absorption 0.450 - 2.50 %
0.450 - 2.50 %
Average value: 1.01 % Grade Count:41
Moisture Absorption at Equilibrium 2.20 - 2.70 %
2.20 - 2.70 %
Average value: 2.47 % Grade Count:3
Linear Mold Shrinkage 0.00100 - 0.0180 cm/cm
0.00100 - 0.0180 in/in
Average value: 0.00481 cm/cm Grade Count:51
Linear Mold Shrinkage, Transverse 0.00900 - 0.0110 cm/cm
0.00900 - 0.0110 in/in
Average value: 0.00967 cm/cm Grade Count:3
Mechanical Properties Metric English Comments
Hardness, Rockwell R 110 - 125
110 - 125
Average value: 114 Grade Count:8
Tensile Strength, Ultimate 75.0 - 320 MPa
10900 - 46400 psi
Average value: 179 MPa Grade Count:43
Tensile Strength, Yield 105 - 208 MPa
15200 - 30200 psi
Average value: 157 MPa Grade Count:11
Elongation at Break 1.00 - 6.00 %
1.00 - 6.00 %
Average value: 3.08 % Grade Count:25
Elongation at Yield 1.30 - 11.0 %
1.30 - 11.0 %
Average value: 3.21 % Grade Count:28
Modulus of Elasticity 4.69 - 34.0 GPa
680 - 4930 ksi
Average value: 13.9 GPa Grade Count:43
Flexural Yield Strength 110 - 440 MPa
16000 - 63800 psi
Average value: 252 MPa Grade Count:49
Flexural Modulus 3.59 - 29.0 GPa
520 - 4210 ksi
Average value: 11.7 GPa Grade Count:50
Izod Impact, Notched 0.370 - 2.03 J/cm
0.693 - 3.80 ft-lb/in
Average value: 0.913 J/cm Grade Count:16
0.5339 - 0.5339 J/cm

@Temperature -40.0 - -40.0 °C
1.000 - 1.000 ft-lb/in

@Temperature -40.0 - -40.0 °F
Average value: 0.534 J/cm Grade Count:1
0.5339 - 0.5339 J/cm

@Thickness 3.17 - 3.17 mm
1.000 - 1.000 ft-lb/in

@Thickness 0.125 - 0.125 in
Average value: 0.534 J/cm Grade Count:1
Izod Impact, Unnotched 4.27 - 10.1 J/cm
8.00 - 19.0 ft-lb/in
Average value: 6.89 J/cm Grade Count:10
Izod Impact, Notched (ISO) 5.00 - 8.10 kJ/m²
2.38 - 3.85 ft-lb/in²
Average value: 6.58 kJ/m² Grade Count:6
Izod Impact, Unnotched (ISO) 41.0 - 52.0 kJ/m²
19.5 - 24.7 ft-lb/in²
Average value: 46.3 kJ/m² Grade Count:4
Charpy Impact Unnotched 2.20 - 9.50 J/cm²
10.5 - 45.2 ft-lb/in²
Average value: 5.15 J/cm² Grade Count:32
2.20 - 9.00 J/cm²

@Temperature -40.0 - -30.0 °C
10.5 - 42.8 ft-lb/in²

@Temperature -40.0 - -22.0 °F
Average value: 4.59 J/cm² Grade Count:16
Charpy Impact, Notched 0.400 - 1.50 J/cm²
1.90 - 7.14 ft-lb/in²
Average value: 0.981 J/cm² Grade Count:24
0.700 - 1.10 J/cm²

@Temperature -30.0 - -30.0 °C
3.33 - 5.24 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 0.960 J/cm² Grade Count:5
Coefficient of Friction 0.180 - 0.250
0.180 - 0.250
Average value: 0.213 Grade Count:10
Coefficient of Friction, Static 0.130 - 0.180
0.130 - 0.180
Average value: 0.165 Grade Count:10
Thermal Properties Metric English Comments
CTE, linear 12.0 - 79.2 µm/m-°C
6.67 - 44.0 µin/in-°F
Average value: 28.1 µm/m-°C Grade Count:23
Thermal Conductivity 0.380 - 3.50 W/m-K
2.64 - 24.3 BTU-in/hr-ft²-°F
Average value: 0.886 W/m-K Grade Count:15
Melting Point 221 - 265 °C
430 - 509 °F
Average value: 256 °C Grade Count:11
Maximum Service Temperature, Air 90.0 - 160 °C
194 - 320 °F
Average value: 135 °C Grade Count:30
Deflection Temperature at 0.46 MPa (66 psi) 210 - 260 °C
410 - 500 °F
Average value: 247 °C Grade Count:13
Deflection Temperature at 1.8 MPa (264 psi) 177 - 259 °C
350 - 498 °F
Average value: 239 °C Grade Count:33
Vicat Softening Point 200 - 260 °C
392 - 500 °F
Average value: 248 °C Grade Count:15
Flammability, UL94 HB - V-0
HB - V-0
Grade Count:19
Electrical Properties Metric English Comments
Electrical Resistivity 1.00 - 1.00e+13 ohm-cm
1.00 - 1.00e+13 ohm-cm
Average value: 4.17e+11 ohm-cm Grade Count:16
Surface Resistance 1.00 - 1.00e+13 ohm
1.00 - 1.00e+13 ohm
Average value: 2.00e+11 ohm Grade Count:40
Insulation Resistance 100 - 1.00e+12 ohm
100 - 1.00e+12 ohm
Average value: 7.14e+10 ohm Grade Count:28
Processing Properties Metric English Comments
Processing Temperature 270 - 300 °C
518 - 572 °F
Average value: 289 °C Grade Count:31
Nozzle Temperature 280 - 300 °C
536 - 572 °F
Average value: 290 °C Grade Count:28
Melt Temperature 260 - 310 °C
500 - 590 °F
Average value: 294 °C Grade Count:41
Mold Temperature 60.0 - 121 °C
140 - 250 °F
Average value: 98.2 °C Grade Count:44
Drying Temperature 75.0 - 107 °C
167 - 225 °F
Average value: 88.7 °C Grade Count:39
Moisture Content 0.150 - 0.250 %
0.150 - 0.250 %
Average value: 0.200 % Grade Count:9
Dew Point -17.8 °C
0.000 °F
Average value: -17.8 °C Grade Count:3
Injection Pressure 68.9 - 124 MPa
10000 - 18000 psi
Average value: 103 MPa Grade Count:5