Overview of materials for PVC, Extruded

Category Polymer , Thermoplastic , Vinyl (PVC) , PVC, Extruded
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for PVC, Extruded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "PVC, Extruded". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 0.549 - 1.85 g/cc
0.0198 - 0.0668 lb/in³
Average value: 1.37 g/cc Grade Count:538
Moisture Absorption at Equilibrium 0.100 - 0.200 %
0.100 - 0.200 %
Average value: 0.167 % Grade Count:3
Water Absorption at Saturation 0.100 - 0.200 %
0.100 - 0.200 %
Average value: 0.167 % Grade Count:3
Viscosity 1.02 - 2.51 cP
1.02 - 2.51 cP
Average value: 1.73 cP Grade Count:6
Linear Mold Shrinkage 0.0150 - 0.0310 cm/cm
0.0150 - 0.0310 in/in
Average value: 0.0193 cm/cm Grade Count:6
ASTM Color -59.0 - 97.5
-59.0 - 97.5
Average value: 24.5 Grade Count:81
Mechanical Properties Metric English Comments
Hardness, Shore A 40.0 - 110
40.0 - 110
Average value: 74.2 Grade Count:289
Hardness, Shore D 37.0 - 88.0
37.0 - 88.0
Average value: 77.4 Grade Count:160
Tensile Strength, Ultimate 3.74 - 55.9 MPa
542 - 8110 psi
Average value: 23.2 MPa Grade Count:482
Tensile Strength, Yield 1.79 - 57.4 MPa
260 - 8330 psi
Average value: 33.9 MPa Grade Count:181
Elongation at Break 3.50 - 720 %
3.50 - 720 %
Average value: 274 % Grade Count:389
Modulus of Elasticity 1.06 - 4.83 GPa
154 - 700 ksi
Average value: 2.84 GPa Grade Count:77
Flexural Yield Strength 28.0 - 99.9 MPa
4060 - 14500 psi
Average value: 81.0 MPa Grade Count:70
Flexural Modulus 1.30 - 4.69 GPa
188 - 680 ksi
Average value: 2.84 GPa Grade Count:66
Izod Impact, Notched 0.179 - 12.9 J/cm
0.335 - 24.2 ft-lb/in
Average value: 3.51 J/cm Grade Count:95
11.7 - 11.7 J/cm

@Temperature -40.0 - -40.0 °C
21.9 - 21.9 ft-lb/in

@Temperature -40.0 - -40.0 °F
Average value: 11.7 J/cm Grade Count:1
11.7 - 11.7 J/cm

@Thickness 3.18 - 3.18 mm
21.9 - 21.9 ft-lb/in

@Thickness 0.125 - 0.125 in
Average value: 11.7 J/cm Grade Count:1
Izod Impact, Unnotched 0.300 - 34.2 J/cm
0.562 - 64.1 ft-lb/in
Average value: 2.28 J/cm Grade Count:88
Charpy Impact Unnotched 1.50 - 1000 J/cm²
7.14 - 4760 ft-lb/in²
Average value: 1.50 J/cm² Grade Count:3
Charpy Impact, Notched 0.300 - 1.00 J/cm²
1.43 - 4.76 ft-lb/in²
Average value: 0.567 J/cm² Grade Count:3
Tear Strength Test 145 - 550
145 - 550
Average value: 322 Grade Count:64
Tear Strength 17.5 - 105 kN/m
99.9 - 599 pli
Average value: 53.8 kN/m Grade Count:29
Dart Drop Total Energy 5.34 - 178 J/cm
0.0100 - 0.333 ft-lb/mil
Average value: 70.9 J/cm Grade Count:38
Compression Set 18.0 - 50.0 %
18.0 - 50.0 %
Average value: 31.3 % Grade Count:16
Clash Berg Modulus 0.0331 - 0.689 GPa
4.80 - 99.9 ksi
Average value: 0.205 GPa Grade Count:10
0.00745 - 0.558 GPa

@Temperature -50.0 - -26.0 °C
1.08 - 80.9 ksi

@Temperature -58.0 - -14.8 °F
Average value: 0.306 GPa Grade Count:13
Thermal Properties Metric English Comments
CTE, linear 45.0 - 90.0 µm/m-°C
25.0 - 50.0 µin/in-°F
Average value: 63.7 µm/m-°C Grade Count:46
Thermal Conductivity 0.140 - 0.190 W/m-K
0.972 - 1.32 BTU-in/hr-ft²-°F
Average value: 0.162 W/m-K Grade Count:4
Maximum Service Temperature, Air 60.0 - 80.0 °C
140 - 176 °F
Average value: 65.0 °C Grade Count:4
Deflection Temperature at 0.46 MPa (66 psi) 69.0 - 85.0 °C
156 - 185 °F
Average value: 76.0 °C Grade Count:8
Deflection Temperature at 1.8 MPa (264 psi) 51.0 - 79.0 °C
124 - 174 °F
Average value: 70.0 °C Grade Count:65
Vicat Softening Point 52.0 - 87.0 °C
126 - 189 °F
Average value: 80.0 °C Grade Count:123
Heat Distortion Temperature 65.0 - 76.0 °C
149 - 169 °F
Average value: 73.5 °C Grade Count:24
Minimum Service Temperature, Air -40.0 - -5.00 °C
-40.0 - 23.0 °F
Average value: -25.0 °C Grade Count:4
Brittleness Temperature -60.0 - 35.0 °C
-76.0 - 95.0 °F
Average value: -30.4 °C Grade Count:146
Flammability, UL94 HB - 5VB
HB - 5VB
Grade Count:40
Flame Spread 0.0100 - 24.0 mm/min
0.000394 - 0.945 in/min
Average value: 6.26 mm/min Grade Count:4
Oxygen Index 22.0 - 30.0 %
22.0 - 30.0 %
Average value: 26.7 % Grade Count:13
Optical Properties Metric English Comments
Transmission, Visible 74.0 - 90.0 %
74.0 - 90.0 %
Average value: 88.3 % Grade Count:51
Component Elements Properties Metric English Comments
Cadmium, Cd 0.00500 %
0.00500 %
Average value: 0.00500 % Grade Count:5
Chromium, Cr 0.0100 %
0.0100 %
Average value: 0.0100 % Grade Count:5
Lead, Pb 0.0100 %
0.0100 %
Average value: 0.0100 % Grade Count:5
Mercury, Hg 0.0100 %
0.0100 %
Average value: 0.0100 % Grade Count:5
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+13 - 1.00e+17 ohm-cm
1.00e+13 - 1.00e+17 ohm-cm
Average value: 3.36e+16 ohm-cm Grade Count:6
Dielectric Constant 3.00 - 3.30
3.00 - 3.30
Average value: 3.12 Grade Count:4
Dielectric Strength 18.0 - 50.0 kV/mm
457 - 1270 kV/in
Average value: 32.0 kV/mm Grade Count:4
Processing Properties Metric English Comments
Melt Temperature 154 - 210 °C
310 - 410 °F
Average value: 181 °C Grade Count:157