Overview of materials for Polycarbonate, PTFE Filled

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, PTFE Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polycarbonate, PTFE Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, PTFE Filled". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.08 - 1.55 g/cc
0.0390 - 0.0560 lb/in³
Average value: 1.28 g/cc Grade Count:77
Water Absorption 0.0200 - 0.200 %
0.0200 - 0.200 %
Average value: 0.137 % Grade Count:34
Additive Loading 5.00 - 15.0 %
5.00 - 15.0 %
Average value: 8.33 % Grade Count:3
Linear Mold Shrinkage 0.00100 - 0.0160 cm/cm
0.00100 - 0.0160 in/in
Average value: 0.00673 cm/cm Grade Count:70
Linear Mold Shrinkage, Transverse 0.00400 - 0.0150 cm/cm
0.00400 - 0.0150 in/in
Average value: 0.00756 cm/cm Grade Count:16
Melt Flow 4.50 - 55.0 g/10 min
4.50 - 55.0 g/10 min
Average value: 17.8 g/10 min Grade Count:22
Mechanical Properties Metric English Comments
Hardness, Rockwell R 75.0 - 118
75.0 - 118
Average value: 109 Grade Count:13
Tensile Strength, Ultimate 20.0 - 136 MPa
2900 - 19700 psi
Average value: 54.5 MPa Grade Count:71
Tensile Strength, Yield 40.7 - 121 MPa
5900 - 17500 psi
Average value: 62.8 MPa Grade Count:27
Elongation at Break 1.50 - 100 %
1.50 - 100 %
Average value: 21.4 % Grade Count:52
Elongation at Yield 1.00 - 91.0 %
1.00 - 91.0 %
Average value: 7.45 % Grade Count:28
Modulus of Elasticity 1.93 - 9.31 GPa
280 - 1350 ksi
Average value: 2.54 GPa Grade Count:42
Flexural Yield Strength 68.6 - 214 MPa
9960 - 31000 psi
Average value: 87.7 MPa Grade Count:72
Flexural Modulus 1.60 - 13.7 GPa
232 - 1990 ksi
Average value: 2.68 GPa Grade Count:72
Compressive Yield Strength 62.1 - 68.9 MPa
9000 - 10000 psi
Average value: 62.9 MPa Grade Count:8
Izod Impact, Notched 0.427 - 8.01 J/cm
0.800 - 15.0 ft-lb/in
Average value: 1.98 J/cm Grade Count:61
Izod Impact, Unnotched 3.90 J/cm - NB
7.31 ft-lb/in - NB
Average value: 14.7 J/cm Grade Count:35
Izod Impact, Notched (ISO) 5.70 - 28.5 kJ/m²
2.71 - 13.6 ft-lb/in²
Average value: 15.5 kJ/m² Grade Count:5
Izod Impact, Unnotched (ISO) 26.7 - 137 kJ/m²
12.7 - 65.2 ft-lb/in²
Average value: 87.1 kJ/m² Grade Count:5
Charpy Impact Unnotched 5.00 - 12.0 J/cm²
23.8 - 57.1 ft-lb/in²
Average value: 8.23 J/cm² Grade Count:15
5.20 - 8.00 J/cm²

@Temperature -40.0 - -20.0 °C
24.7 - 38.1 ft-lb/in²

@Temperature -40.0 - -4.00 °F
Average value: 6.57 J/cm² Grade Count:5
Charpy Impact, Notched 0.700 - 2.50 J/cm²
3.33 - 11.9 ft-lb/in²
Average value: 1.62 J/cm² Grade Count:5
0.500 - 1.50 J/cm²

@Temperature -30.0 - -30.0 °C
2.38 - 7.14 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 1.00 J/cm² Grade Count:2
Gardner Impact 36.2 J
26.7 ft-lb
Average value: 36.2 J Grade Count:7
Falling Dart Impact 7.36 - 47.5 J
5.43 - 35.0 ft-lb
Average value: 30.3 J Grade Count:8
Coefficient of Friction 0.0800 - 0.250
0.0800 - 0.250
Average value: 0.151 Grade Count:15
Coefficient of Friction, Static 0.0600 - 0.260
0.0600 - 0.260
Average value: 0.133 Grade Count:15
K (wear) Factor 3.50 - 100 x 10-8 mm³/N-M
1.74 - 49.6 x 10-10 in³-min/ft-lb-hr
Average value: 53.8 x 10<sup>-8</sup> mm³/N-M Grade Count:6
Thermal Properties Metric English Comments
CTE, linear 23.0 - 74.0 µm/m-°C
12.8 - 41.1 µin/in-°F
Average value: 59.6 µm/m-°C Grade Count:24
CTE, linear, Transverse to Flow 34.0 - 76.0 µm/m-°C
18.9 - 42.2 µin/in-°F
Average value: 51.7 µm/m-°C Grade Count:3
Thermal Conductivity 0.187 - 0.200 W/m-K
1.30 - 1.39 BTU-in/hr-ft²-°F
Average value: 0.199 W/m-K Grade Count:9
Maximum Service Temperature, Air 130 - 150 °C
266 - 302 °F
Average value: 140 °C Grade Count:12
Deflection Temperature at 0.46 MPa (66 psi) 85.0 - 182 °C
185 - 360 °F
Average value: 138 °C Grade Count:24
Deflection Temperature at 1.8 MPa (264 psi) 75.0 - 143 °C
167 - 290 °F
Average value: 130 °C Grade Count:59
Vicat Softening Point 90.0 - 160 °C
194 - 320 °F
Average value: 151 °C Grade Count:19
Flammability, UL94 HB - V-0
HB - V-0
Grade Count:45
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+14 - 1.00e+16 ohm-cm
1.00e+14 - 1.00e+16 ohm-cm
Average value: 5.88e+15 ohm-cm Grade Count:19
Surface Resistance 100 - 1.00e+16 ohm
100 - 1.00e+16 ohm
Average value: 2.52e+15 ohm Grade Count:4
Insulation Resistance 1.00e+12 ohm
1.00e+12 ohm
Average value: 1.00e+12 ohm Grade Count:12
Processing Properties Metric English Comments
Processing Temperature 249 - 295 °C
480 - 563 °F
Average value: 289 °C Grade Count:16
Nozzle Temperature 271 - 310 °C
520 - 590 °F
Average value: 298 °C Grade Count:16
Melt Temperature 220 - 343 °C
428 - 650 °F
Average value: 301 °C Grade Count:60
Mold Temperature 40.0 - 121 °C
104 - 250 °F
Average value: 95.3 °C Grade Count:64
Drying Temperature 70.0 - 130 °C
158 - 266 °F
Average value: 120 °C Grade Count:60
Moisture Content 0.0200 %
0.0200 %
Average value: 0.0200 % Grade Count:35
Dew Point -28.9 °C
-20.0 °F
Average value: -28.9 °C Grade Count:15
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi
Average value: 86.2 MPa Grade Count:19
Vent Depth 0.00250 - 0.00760 cm
0.000984 - 0.00299 in
Average value: 0.00505 cm Grade Count:4