Raschig Group 6502 DAIP Diallyl Phthalate (DAP), Cast, Mineral Filler

Category Polymer , Thermoset , Diallyl Phthalate (DAP) , Diallyl Phthalate (DAP) Molding Compound, Short Glass Fiber Filled
Manufacturer Raschig Group
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Raschig Group 6502 DAIP Diallyl Phthalate (DAP), Cast, Mineral Filler.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Glass-fiber reinforced diallyl isophthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensional stability even under severe environmental conditions. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS)Processing: Injection and transfer moldingApplications: Connectors, bobbins, potentiometers, switchesInformation provided by Raschig Group
Physical Properties Metric English Comments
Specific Gravity 1.80 - 2.00 g/cc
1.80 - 2.00 g/cc
ISO 1183
Apparent Bulk Density 0.700 - 0.850 g/cc
0.0253 - 0.0307 lb/in³
ISO 60
Water Absorption <= 0.200 %

@Temperature 23.0 °C,
Time 86400 sec
<= 0.200 %

@Temperature 73.4 °F,
Time 24.0 hour
ISO 62
Linear Mold Shrinkage, Flow 0.00200 - 0.00450 cm/cm
0.00200 - 0.00450 in/in
Injection; ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength 50.0 - 70.0 MPa
7250 - 10200 psi
Injection; ISO 527
Modulus of Elasticity 14.0 - 17.0 GPa
2030 - 2470 ksi
Injection; ISO 527
Flexural Strength 100 - 140 MPa
14500 - 20300 psi
Injection; ISO 178
Flexural Modulus 12.0 - 15.0 GPa
1740 - 2180 ksi
Injection; ISO 178
Compressive Strength 150 - 200 MPa
21800 - 29000 psi
ISO 604
Charpy Impact Unnotched 0.500 - 0.600 J/cm²
2.38 - 2.86 ft-lb/in²
Injection; ISO 179/1eU
Charpy Impact, Notched 0.300 - 0.400 J/cm²
1.43 - 1.90 ft-lb/in²
Injection; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 50.0 - 60.0 µm/m-°C

@Temperature 50.0 - 100 °C
27.8 - 33.3 µin/in-°F

@Temperature 122 - 212 °F
ISO 11359-2
Thermal Conductivity 0.400 - 0.600 W/m-K
2.78 - 4.16 BTU-in/hr-ft²-°F
ASTM E1461
Deflection Temperature at 1.8 MPa (264 psi) >= 200 °C
>= 392 °F
ISO 75-A
Deflection Temperature at 8.0 MPa >= 180 °C
>= 356 °F
ISO 75-C
Shrinkage <= 0.0500 %

@Temperature 110 °C,
Time 605000 sec
<= 0.0500 %

@Temperature 230 °F,
Time 168 hour
Post shrinkage; ISO 2577
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+14 - 1.00e+15 ohm-cm
1.00e+14 - 1.00e+15 ohm-cm
IEC 60093
Surface Resistance 1.00e+14 - 1.00e+15 ohm
1.00e+14 - 1.00e+15 ohm
IEC 60093
Dielectric Constant 4.00 - 5.00

@Frequency 100 Hz
4.00 - 5.00

@Frequency 100 Hz
IEC 60250
4.00 - 5.00

@Frequency 1.00e+6 Hz
4.00 - 5.00

@Frequency 1.00e+6 Hz
IEC 60250
Dielectric Strength 15.0 - 20.0 kV/mm
381 - 508 kV/in
IEC 60243-1
Dissipation Factor 0.0100 - 0.0300

@Frequency 100 Hz
0.0100 - 0.0300

@Frequency 100 Hz
IEC 60250
0.0100 - 0.0300

@Frequency 1.00e+6 Hz
0.0100 - 0.0300

@Frequency 1.00e+6 Hz
IEC 60250
Arc Resistance 180 - 240 sec
180 - 240 sec
ASTM D495
Comparative Tracking Index >= 550 V
>= 550 V
IEC 60112
Processing Properties Metric English Comments
Shelf Life 6.00 Month

@Temperature 15.0 - 25.0 °C
6.00 Month

@Temperature 59.0 - 77.0 °F
Descriptive Properties Value Comments
Glow wire flammability test 850/1
IEC 60695 2-12
Glow wire ignitability test 875/1
IEC 60695 2-13
Water Absorption <15 mg
24 hr, 23°C; ISO 62