BASF Ultramid® 8233G HS BK-106 33% Glass Filled PA6 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® 8233G HS BK-106 33% Glass Filled PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid 8233G HS BK-106 is a heat stabilized, weather resistant, 33% glass fiber reinforced PA6 injection molding compound offering excellent strength, stiffness, high temperature performance and dimensional stability. This balance of engineering properties in combination with excellent processability make it ideal in applications replacing metal, resulting in an overall cost and weight savings.
Physical Properties Metric English Comments
Density 1.39 g/cc
0.0502 lb/in³
ISO 1183
Water Absorption 1.1 %
1.1 %
24 hour; ISO Test
6.4 %
6.4 %
ISO 62
Moisture Absorption at Equilibrium 1.8 %
1.8 %
23°C/50% R.H.; ISO 62
Relative Viscosity 2.6 cP
2.6 cP
ISO Test; 96 % SAV
Viscosity Measurement 50
50
Formic Acid
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Hardness, Rockwell R 121
121
ASTM Test
Tensile Strength at Break 160 MPa
23200 psi
0.2 in/min; ASTM Test
70.0 MPa

@Temperature 120 °C
10200 psi

@Temperature 248 °F
ISO Data
70.0 MPa

@Temperature 120 °C
10200 psi

@Temperature 248 °F
ASTM Test
85.0 MPa

@Temperature 80.0 °C
12300 psi

@Temperature 176 °F
ASTM Test
85.0 MPa

@Temperature 80.0 °C
12300 psi

@Temperature 176 °F
ISO Data
210 MPa

@Temperature -40.0 °C
30500 psi

@Temperature -40.0 °F
ISO Data
210 MPa

@Temperature -40.0 °C
30500 psi

@Temperature -40.0 °F
ASTM Test
Tensile Strength, Ultimate 155 MPa
22500 psi
5mm/min; ISO 527
Elongation at Break 2.0 %
2.0 %
5mm/min; ISO 527
2.0 %
2.0 %
0.2 in/min; ASTM Test
3.0 %

@Temperature -40.0 °C
3.0 %

@Temperature -40.0 °F
ASTM Test
3.0 %

@Temperature -40.0 °C
3.0 %

@Temperature -40.0 °F
ISO Data
7.0 %

@Temperature 120 °C
7.0 %

@Temperature 248 °F
ISO Data
7.0 %

@Temperature 80.0 °C
7.0 %

@Temperature 176 °F
ISO Data
7.0 %

@Temperature 120 °C
7.0 %

@Temperature 248 °F
ASTM Test
7.0 %

@Temperature 80.0 °C
7.0 %

@Temperature 176 °F
ASTM Test
Tensile Modulus 10.5 GPa
1520 ksi
1mm/min; ISO 527
4.015 GPa

@Temperature 120 °C
582.3 ksi

@Temperature 248 °F
ISO Data
4.66 GPa

@Temperature 80.0 °C
676 ksi

@Temperature 176 °F
ISO Data
10.4 GPa

@Temperature -40.0 °C
1510 ksi

@Temperature -40.0 °F
ISO Data
Flexural Strength 225 MPa
32600 psi
ISO Data
Flexural Modulus 8.70 GPa
1260 ksi
ISO Data
Izod Impact, Notched (ISO) 8.50 kJ/m²
4.04 ft-lb/in²
ISO Test
6.00 kJ/m²

@Temperature -40.0 °C
2.86 ft-lb/in²

@Temperature -40.0 °F
ISO Test
Charpy Impact Unnotched 5.50 J/cm²
26.2 ft-lb/in²
ISO 179
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
ISO 179
0.550 J/cm²

@Temperature -30.0 °C
2.62 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Thermal Properties Metric English Comments
CTE, linear 38.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
21.1 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM Test
Melting Point 220 °C
428 °F
10 K/min
220 °C
428 °F
ASTM Test
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
401 °F
ISO 75
208 °C
406 °F
ASTM Test
Flammability, UL94 HB

@Thickness 0.710 mm
HB

@Thickness 0.0280 in
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
IEC 60093
Processing Properties Metric English Comments
Melt Temperature 275 °C
527 °F
Injection molding
Mold Temperature 95.0 °C
203 °F
Injection molding
Descriptive Properties Value Comments
Color BK-106
Commercial Status Active America
Form Pellets
Impact Modified No
Primary Processing Technique Injection Molding
Processing Injection Molding
Special characteristic Heat stabilized or stable to heat
UL.UL-C Yes