Covestro Makrolon® 6487 Polycarbonate, Flame Retardant Grade

Category	Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Extruded
Manufacturer	Covestro
Trade Name	Makrolon®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Covestro Makrolon® 6487 Polycarbonate, Flame Retardant Grade.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

ISO 7391-PC,MFLR,(,,)-18-9Global gradeMVR (300 °C/1.2 kg) 12.5 cm3/10 minFlame retardantUL 94V-0/1.5 mm and 5VA/3.0 mmMedium viscosityUV stabilizedEasy releaseInjection molding - Melt temperature 280 - 320 °CAvailable in opaque colors onlyPreprocessingMax. Water content

Physical Properties	Metric	English	Comments
Density	1.20 g/cc	0.0434 lb/in³	ISO 1183
	1.02 g/cc @Temperature 290 °C	0.0368 lb/in³ @Temperature 554 °F	Melt
Water Absorption	0.30 %	0.30 %	Similar to ISO 62
Moisture Absorption at Equilibrium	0.12 %	0.12 %	Similar to ISO 62
Linear Mold Shrinkage, Flow	0.0070 cm/cm	0.0070 in/in	ISO 294-4,2577
Linear Mold Shrinkage, Transverse	0.0070 cm/cm	0.0070 in/in	ISO 294-4,2577
Melt Flow	13 g/10 min @Load 1.20 kg, Temperature 300 °C	13 g/10 min @Load 2.65 lb, Temperature 572 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	67.0 MPa	9720 psi	ISO 527-1/-2
Elongation at Break	>= 50 %	>= 50 %	Nominal; ISO 527-1/-2
Elongation at Yield	6.0 %	6.0 %	ISO 527-1/-2
Tensile Modulus	2.45 GPa	355 ksi	ISO 527-1/-2
Charpy Impact Unnotched	NB	NB	ISO 179/1eU
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	ISO 179/1eU
Impact	5200	5200	Puncture - maximum force (N); ISO 6603-2
	6000 @Temperature -30.0 °C	6000 @Temperature -22.0 °F	Puncture - maximum force (N); ISO 6603-2
Puncture Energy	50.0 J	36.9 ft-lb	ISO 6603-2
	55.0 J @Temperature -30.0 °C	40.6 ft-lb @Temperature -22.0 °F	ISO 6603-2

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	65.0 µm/m-°C	36.1 µin/in-°F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	65.0 µm/m-°C	36.1 µin/in-°F	ISO 11359-1/-2
Specific Heat Capacity	1.70 J/g-°C	0.406 BTU/lb-°F	Melt
Thermal Conductivity	0.173 W/m-K	1.20 BTU-in/hr-ft²-°F	Melt
Deflection Temperature at 0.46 MPa (66 psi)	134 °C	273 °F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	122 °C	252 °F	ISO 75-1/-2
Vicat Softening Point	143 °C	289 °F	50°C/h 50N; ISO 306
Flammability, UL94	V-0 @Thickness 1.50 mm	V-0 @Thickness 0.0591 in	IEC 60695-11-10
	V-0 @Thickness 3.00 mm	V-0 @Thickness 0.118 in	IEC 60695-11-10
	5VA @Thickness 3.00 mm	5VA @Thickness 0.118 in	IEC 60695-11-20
Oxygen Index	35 %	35 %	ISO 4589-1/-2

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+13 ohm-cm	>= 1.00e+13 ohm-cm	IEC 60093
Surface Resistance	>= 1.00e+15 ohm	>= 1.00e+15 ohm	IEC 60093
Dielectric Constant	3.0 @Frequency 1.00e+6 Hz	3.0 @Frequency 1.00e+6 Hz	IEC 60250
	3.1 @Frequency 100 Hz	3.1 @Frequency 100 Hz	IEC 60250
Dielectric Strength	34.0 kV/mm	864 kV/in	IEC 60243-1
Dissipation Factor	0.00080 @Frequency 100 Hz	0.00080 @Frequency 100 Hz	IEC 60250
	0.0090 @Frequency 1.00e+6 Hz	0.0090 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	225 V	225 V	IEC 60112

Processing Properties	Metric	English	Comments
Melt Temperature	290 °C	554 °F	Injection Molding; ISO 294
	280 - 320 °C	536 - 608 °F
Mold Temperature	80.0 °C	176 °F	Injection Molding; ISO 10724
	80.0 - 120 °C	176 - 248 °F
Ejection Temperature	130 °C	266 °F
Injection Velocity	200 mm/sec	7.87 in/sec	ISO 294

Descriptive Properties	Value	Comments
Availability	Asia Pacific
	Europe
	India
	Near East/Africa
	North America
	South and Central America
Eff. thermal diffusivity (m²/s)	1E-07
Feature	Light stabilised or stable to light
	Release agent
	U.V. stabilised or stable to weather
Form	Pellets
Process	Injection Molding
	Other Extrusion