DuPont Performance Polymers Crastin® S600F40 NC010 Polybutylene Terephthalate (PBT)  (Unverified Data**)&l

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer DuPont Performance Polymers
Trade Name Crastin®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Crastin® S600F40 NC010 Polybutylene Terephthalate (PBT)  (Unverified Data**)&l.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Unreinforced Low Viscosity Polybutylene Terephthalate Crastin S600F40 NC010 is an unreinforced lubricated low viscosity polybutylene terephthalate resin for injection molding.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.11 g/cc
0.0401 lb/in³
1.31 g/cc
0.0473 lb/in³
ISO 1183
Water Absorption 0.40 %

@Thickness 2.00 mm
 0.40 %

@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.200 %

@Thickness 2.00 mm
 0.200 %

@Thickness 0.0787 in
 Sim. to ISO 62
Viscosity 75900 cP

@Shear Rate 5000 1/s,
Temperature 260 °C
 75900 cP

@Shear Rate 5000 1/s,
Temperature 500 °F
 ISO 11403-1 -2
86676 cP

@Shear Rate 5000 1/s,
Temperature 250 °C
 86676 cP

@Shear Rate 5000 1/s,
Temperature 482 °F
 ISO 11403-1 -2
99080 cP

@Shear Rate 5000 1/s,
Temperature 240 °C
 99080 cP

@Shear Rate 5000 1/s,
Temperature 464 °F
 ISO 11403-1 -2
184900 cP

@Shear Rate 500 1/s,
Temperature 260 °C
 184900 cP

@Shear Rate 500 1/s,
Temperature 500 °F
 ISO 11403-1 -2
235700 cP

@Shear Rate 500 1/s,
Temperature 250 °C
 235700 cP

@Shear Rate 500 1/s,
Temperature 482 °F
 ISO 11403-1 -2
301100 cP

@Shear Rate 500 1/s,
Temperature 240 °C
 301100 cP

@Shear Rate 500 1/s,
Temperature 464 °F
 ISO 11403-1 -2
Viscosity Test 120 cm³/g
120 cm³/g
ISO 307 1157 1628
Linear Mold Shrinkage, Flow 0.019 cm/cm
0.019 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.018 cm/cm
0.018 in/in
ISO 294-4 2577
Melt Flow 32.9 g/10 min

@Load 2.16 kg,
Temperature 250 °C
 32.9 g/10 min

@Load 4.76 lb,
Temperature 482 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Stress 29.24 MPa

@Strain 1.10 %,
Temperature 23.0 °C
 4241 psi

@Strain 1.10 %,
Temperature 73.4 °F
 ISO 11403-1 -2
36.41 MPa

@Strain 1.40 %,
Temperature 23.0 °C
 5281 psi

@Strain 1.40 %,
Temperature 73.4 °F
 ISO 11403-1 -2
41.88 MPa

@Strain 1.40 %,
Temperature -40.0 °C
 6074 psi

@Strain 1.40 %,
Temperature -40.0 °F
 ISO 11403-1 -2
46.12 MPa

@Strain 1.90 %,
Temperature 23.0 °C
 6689 psi

@Strain 1.90 %,
Temperature 73.4 °F
 ISO 11403-1 -2
49.47 MPa

@Strain 1.70 %,
Temperature -40.0 °C
 7175 psi

@Strain 1.70 %,
Temperature -40.0 °F
 ISO 11403-1 -2
50.61 MPa

@Strain 2.20 %,
Temperature 23.0 °C
 7341 psi

@Strain 2.20 %,
Temperature 73.4 °F
 ISO 11403-1 -2
64.81 MPa

@Strain 2.40 %,
Temperature -40.0 °C
 9400 psi

@Strain 2.40 %,
Temperature -40.0 °F
 ISO 11403-1 -2
79.66 MPa

@Strain 3.30 %,
Temperature -40.0 °C
 11550 psi

@Strain 3.30 %,
Temperature -40.0 °F
 ISO 11403-1 -2
Tensile Strength, Yield 58.0 MPa
8410 psi
ISO 527-1/-2
Elongation at Break 30 %
30 %
Nominal; ISO 527-1/-2
Elongation at Yield 6.0 %
6.0 %
ISO 527-1/-2
Tensile Modulus 2.60 GPa
377 ksi
ISO 527-1/-2
Flexural Strength 85.0 MPa
12300 psi
ISO 178
Flexural Modulus 2.40 GPa
348 ksi
ISO 178
Secant Modulus 0.371 GPa

@Strain 2.70 %,
Temperature 100 °C
 53.9 ksi

@Strain 2.70 %,
Temperature 212 °F
 ISO 11403-1 -2
0.426 GPa

@Strain 2.70 %,
Temperature 80.0 °C
 61.8 ksi

@Strain 2.70 %,
Temperature 176 °F
 ISO 11403-1 -2
0.43735 GPa

@Strain 1.00 %,
Temperature 100 °C
 63.433 ksi

@Strain 1.00 %,
Temperature 212 °F
 ISO 11403-1 -2
0.4985 GPa

@Strain 1.00 %,
Temperature 80.0 °C
 72.30 ksi

@Strain 1.00 %,
Temperature 176 °F
 ISO 11403-1 -2
2.05 GPa

@Strain 4.40 %,
Temperature -40.0 °C
 297 ksi

@Strain 4.40 %,
Temperature -40.0 °F
 ISO 11403-1 -2
2.18 GPa

@Strain 2.40 %,
Temperature 23.0 °C
 317 ksi

@Strain 2.40 %,
Temperature 73.4 °F
 ISO 11403-1 -2
2.39 GPa

@Strain 2.00 %,
Temperature 23.0 °C
 346 ksi

@Strain 2.00 %,
Temperature 73.4 °F
 ISO 11403-1 -2
2.60 GPa

@Strain 1.40 %,
Temperature 23.0 °C
 377 ksi

@Strain 1.40 %,
Temperature 73.4 °F
 ISO 11403-1 -2
2.61 GPa

@Strain 2.70 %,
Temperature -40.0 °C
 378 ksi

@Strain 2.70 %,
Temperature -40.0 °F
 ISO 11403-1 -2
2.66 GPa

@Strain 1.10 %,
Temperature 23.0 °C
 386 ksi

@Strain 1.10 %,
Temperature 73.4 °F
 ISO 11403-1 -2
2.91 GPa

@Strain 1.70 %,
Temperature -40.0 °C
 422 ksi

@Strain 1.70 %,
Temperature -40.0 °F
 ISO 11403-1 -2
2.99 GPa

@Strain 1.40 %,
Temperature -40.0 °C
 434 ksi

@Strain 1.40 %,
Temperature -40.0 °F
 ISO 11403-1 -2
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
ISO 180/1A
Charpy Impact Unnotched NB
NB
ISO 179/1eU
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 ISO 179/1eU
Charpy Impact, Notched 0.400 J/cm²
1.90 ft-lb/in²
ISO 179/1eA
0.400 J/cm²

@Temperature -30.0 °C
 1.90 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
Tensile Creep Modulus, 1 hour 2600 MPa

@Time 3600 sec
 377000 psi

@Time 1.00 hour
 ISO 899-1
Tensile Creep Modulus, 1000 hours 1800 MPa

@Time 3.60e+6 sec
 261000 psi

@Time 1000 hour
 ISO 899-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 110 µm/m-°C
61.1 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 120 µm/m-°C
66.7 µin/in-°F
ISO 11359-1/-2
Specific Heat Capacity 2.11 J/g-°C
0.504 BTU/lb-°F
Thermal Conductivity 0.210 W/m-K
1.46 BTU-in/hr-ft²-°F
of melt
Melting Point 225 °C
437 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 115 °C
239 °F
ISO 75-1/-2
180 °C
356 °F
annealed; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 50.0 °C
122 °F
ISO 75-1/-2
60.0 °C
140 °F
annealed; ISO 75-1/-2
Vicat Softening Point 175 °C
347 °F
50°C/h 50N; ISO 306
Glass Transition Temp, Tg 55.0 °C
131 °F
10°C/min; ISO 11357-1/-2
Flammability, UL94 HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
 IEC 60695-11-10
HB

@Thickness 0.800 mm
 HB

@Thickness 0.0315 in
 IEC 60695-11-10
Oxygen Index 22 %
22 %
ISO 4589-1/-2
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Dielectric Constant 3.2

@Frequency 1.00e+6 Hz
 3.2

@Frequency 1.00e+6 Hz
 IEC 60250
3.8

@Frequency 100 Hz
 3.8

@Frequency 100 Hz
 IEC 60250
Dielectric Strength 26.0 kV/mm
660 kV/in
IEC 60243-1
Dissipation Factor 0.0020

@Frequency 100 Hz
 0.0020

@Frequency 100 Hz
 IEC 60250
0.020

@Frequency 1.00e+6 Hz
 0.020

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 60112
Descriptive Properties Value Comments
Additives Release agent
Delivery Form Pellets
Part Marking Code >PBT<
ISO 11469
Processing Injection Moulding
Regional Availability Asia Pacific
Europe
Global