Eurostar Starflam PZ0042E PA6, 20% Glass Filled, Injection Molded

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled
Manufacturer Eurostar Engineering Plastics
Trade Name Starflam
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eurostar Starflam PZ0042E PA6, 20% Glass Filled, Injection Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PZ0042E is a Halogen Free and Red Phosphorous Free, Flame Retardant, Glass Reinforced, Polyamide 6 Injection Molding (also known as PF1004Z222 or PA620GFU9Z22)Information provided by Polymer Technology & Services, the North American exclusive supplier.
Physical Properties Metric English Comments
Density 1.33 g/cc
0.0480 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0070 - 0.0090 cm/cm
0.0070 - 0.0090 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 95.0 MPa
13800 psi
5 mm/min; ISO 527
Elongation at Break 3.2 %
3.2 %
5 mm/min; ISO 527
Tensile Modulus 6.20 GPa
899 ksi
1 mm/min; ISO 527
Flexural Strength 160 MPa
23200 psi
2 mm/min; ISO 178
Flexural Modulus 6.15 GPa
892 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80x10x4; ISO 180/1A
Izod Impact, Unnotched (ISO) 45.0 kJ/m²
21.4 ft-lb/in²
80x10x4; ISO 180/1U
Charpy Impact Unnotched 5.00 J/cm²
23.8 ft-lb/in²
Edgew 80x10x4; ISO 179/1eU
Charpy Impact, Notched 0.700 J/cm²
3.33 ft-lb/in²
Edgew 80x10x4; ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 185 °C
365 °F
Edgew 80x10x4, sp=64 mm; ISO 75/Af
Vicat Softening Point 209 °C
408 °F
B/50; ISO 306
UL RTI, Electrical 125 °C

@Thickness 0.750 mm
 257 °F

@Thickness 0.0295 in
125 °C

@Thickness 0.800 mm
 257 °F

@Thickness 0.0315 in
125 °C

@Thickness 1.00 mm
 257 °F

@Thickness 0.0394 in
125 °C

@Thickness 1.50 mm
 257 °F

@Thickness 0.0591 in
125 °C

@Thickness 3.00 mm
 257 °F

@Thickness 0.118 in
UL RTI, Mechanical with Impact 125 °C

@Thickness 0.750 mm
 257 °F

@Thickness 0.0295 in
125 °C

@Thickness 0.800 mm
 257 °F

@Thickness 0.0315 in
125 °C

@Thickness 1.00 mm
 257 °F

@Thickness 0.0394 in
125 °C

@Thickness 1.50 mm
 257 °F

@Thickness 0.0591 in
125 °C

@Thickness 3.00 mm
 257 °F

@Thickness 0.118 in
UL RTI, Mechanical without Impact 130 °C

@Thickness 0.750 mm
 266 °F

@Thickness 0.0295 in
130 °C

@Thickness 0.800 mm
 266 °F

@Thickness 0.0315 in
130 °C

@Thickness 1.00 mm
 266 °F

@Thickness 0.0394 in
130 °C

@Thickness 1.50 mm
 266 °F

@Thickness 0.0591 in
140 °C

@Thickness 3.00 mm
 284 °F

@Thickness 0.118 in
Flammability, UL94 V-2

@Thickness 0.750 mm
 V-2

@Thickness 0.0295 in
 IEC 60695-11-10
V-2

@Thickness 0.800 mm
 V-2

@Thickness 0.0315 in
 IEC 60695-11-10
V-2

@Thickness 1.00 mm
 V-2

@Thickness 0.0394 in
 IEC 60695-11-10
V-2

@Thickness 1.50 mm
 V-2

@Thickness 0.0591 in
 IEC 60695-11-10
V-2

@Thickness 3.00 mm
 V-2

@Thickness 0.118 in
 IEC 60695-11-10
Glow Wire Test 725 °C

@Thickness 1.00 mm
 1340 °F

@Thickness 0.0394 in
 Glow-Wire Ignition; IEC 60695-2-13
960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 Glow-Wire Flammability; IEC 60695-2-12
Electrical Properties Metric English Comments
Comparative Tracking Index 500 V
500 V
IEC 60112
Hot Wire Ignition, HWI 15 - 30 sec

@Thickness 0.750 mm
 15 - 30 sec

@Thickness 0.0295 in
 PLC 3
>= 120 sec

@Thickness 0.800 mm
 >= 120 sec

@Thickness 0.0315 in
 PLC 0
>= 120 sec

@Thickness 1.00 mm
 >= 120 sec

@Thickness 0.0394 in
 PLC 0
>= 120 sec

@Thickness 1.50 mm
 >= 120 sec

@Thickness 0.0591 in
 PLC 0
>= 120 sec

@Thickness 3.00 mm
 >= 120 sec

@Thickness 0.118 in
 PLC 0
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 0.750 mm
 >= 120 arcs

@Thickness 0.0295 in
 PLC 0
>= 120 arcs

@Thickness 0.800 mm
 >= 120 arcs

@Thickness 0.0315 in
 PLC 0
>= 120 arcs

@Thickness 1.00 mm
 >= 120 arcs

@Thickness 0.0394 in
 PLC 0
>= 120 arcs

@Thickness 1.50 mm
 >= 120 arcs

@Thickness 0.0591 in
 PLC 0
>= 120 arcs

@Thickness 3.00 mm
 >= 120 arcs

@Thickness 0.118 in
 PLC 0
Processing Properties Metric English Comments
Rear Barrel Temperature 240 - 250 °C
464 - 482 °F
Zone 1
Middle Barrel Temperature 250 - 260 °C
482 - 500 °F
Zone 2
Front Barrel Temperature 250 - 270 °C
482 - 518 °F
Zone 3
Melt Temperature 250 - 270 °C
482 - 518 °F
Mold Temperature 50.0 - 90.0 °C
122 - 194 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 4.00 hour
4.00 hour
Moisture Content 0.20 %
0.20 %