Overview of materials for Polypropylene, Impact Modified; Molded/Extruded

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Impact Modified; Molded/Extruded
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polypropylene, Impact Modified; Molded/Extruded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Impact Modified; Molded/Extruded". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 0.780 - 2.80 g/cc
0.0282 - 0.101 lb/in³
Average value: 0.928 g/cc Grade Count:188
Water Absorption 0.0100 - 0.0500 %
0.0100 - 0.0500 %
Average value: 0.0131 % Grade Count:13
Thickness 50.0 - 840 microns
1.97 - 33.1 mil
Average value: 230 microns Grade Count:8
Linear Mold Shrinkage 0.00400 - 0.0252 cm/cm
0.00400 - 0.0252 in/in
Average value: 0.0158 cm/cm Grade Count:51
Linear Mold Shrinkage, Transverse 0.00110 - 0.0263 cm/cm
0.00110 - 0.0263 in/in
Average value: 0.0164 cm/cm Grade Count:15
Melt Flow 0.300 - 100 g/10 min
0.300 - 100 g/10 min
Average value: 18.2 g/10 min Grade Count:222
Mechanical Properties Metric English Comments
Hardness, Rockwell R 49.0 - 111
49.0 - 111
Average value: 86.3 Grade Count:103
Hardness, Shore D 52.0 - 70.0
52.0 - 70.0
Average value: 62.2 Grade Count:21
Tensile Strength, Ultimate 5.00 - 34.5 MPa
725 - 5000 psi
Average value: 20.3 MPa Grade Count:29
Tensile Strength, Yield 8.96 - 35.2 MPa
1300 - 5110 psi
Average value: 25.1 MPa Grade Count:200
Film Elongation at Break, MD 600 - 700 %
600 - 700 %
Average value: 652 % Grade Count:5
Film Elongation at Break, TD 570 - 900 %
570 - 900 %
Average value: 804 % Grade Count:5
Elongation at Break 1.80 - 500 %
1.80 - 500 %
Average value: 189 % Grade Count:87
>= 100 %

@Temperature 60.0 - 90.0 °C
>= 100 %

@Temperature 140 - 194 °F
Average value: 100 % Grade Count:1
Elongation at Yield 0.900 - 350 %
0.900 - 350 %
Average value: 12.0 % Grade Count:115
8.50 - 9.00 %

@Temperature 60.0 - 90.0 °C
8.50 - 9.00 %

@Temperature 140 - 194 °F
Average value: 8.75 % Grade Count:1
Modulus of Elasticity 0.750 - 3.50 GPa
109 - 508 ksi
Average value: 1.35 GPa Grade Count:43
0.650 - 1.10 GPa

@Temperature 60.0 - 90.0 °C
94.3 - 160 ksi

@Temperature 140 - 194 °F
Average value: 0.875 GPa Grade Count:1
Flexural Yield Strength 17.0 - 51.7 MPa
2470 - 7500 psi
Average value: 29.7 MPa Grade Count:27
Flexural Modulus 0.134 - 2.89 GPa
19.4 - 419 ksi
Average value: 1.20 GPa Grade Count:215
Secant Modulus, MD 0.150 - 0.896 GPa
21.8 - 130 ksi
Average value: 0.425 GPa Grade Count:5
Secant Modulus, TD 0.250 - 0.772 GPa
36.3 - 112 ksi
Average value: 0.447 GPa Grade Count:5
Izod Impact, Notched 0.267 J/cm - NB
0.500 ft-lb/in - NB
Average value: 2.14 J/cm Grade Count:169
0.176 - 7.26104 J/cm

@Temperature -30.0 - 4.00 °C
0.330 - 13.6029 ft-lb/in

@Temperature -22.0 - 39.2 °F
Average value: 0.794 J/cm Grade Count:56
0.850 - 0.850 J/cm

@Temperature -10.0 - 0.000 °C
1.59 - 1.59 ft-lb/in

@Temperature 14.0 - 32.0 °F
Average value: 0.794 J/cm Grade Count:2
0.850 - 0.850 J/cm

@Thickness 3.17 - 6.40 mm
1.59 - 1.59 ft-lb/in

@Thickness 0.125 - 0.252 in
Average value: 0.794 J/cm Grade Count:2
0.250 - 1.35 J/cm

@Diameter 0.125 - 3.17 mm
0.468 - 2.53 ft-lb/in

@Diameter 0.00492 - 0.125 in
Average value: 0.794 J/cm Grade Count:11
0.250 - 1.35 J/cm

@Temperature -20.0 - -20.0 °C
0.468 - 2.53 ft-lb/in

@Temperature -4.00 - -4.00 °F
Average value: 0.794 J/cm Grade Count:11
Izod Impact, Unnotched 0.539 J/cm - NB
1.01 ft-lb/in - NB
Average value: 3.18 J/cm Grade Count:37
0.294199 - 0.686465 J/cm

@Temperature -10.0 - -10.0 °C
0.551156 - 1.28603 ft-lb/in

@Temperature 14.0 - 14.0 °F
Average value: 0.498 J/cm Grade Count:22
Izod Impact, Notched (ISO) 4.00 - 60.9 kJ/m²
1.90 - 29.0 ft-lb/in²
Average value: 22.4 kJ/m² Grade Count:24
2.94 - 13.0 kJ/m²

@Temperature -40.0 - -10.0 °C
1.40 - 6.19 ft-lb/in²

@Temperature -40.0 - 14.0 °F
Average value: 5.20 kJ/m² Grade Count:10
Izod Impact, Unnotched (ISO) 14.0 kJ/m² - NB
6.66 ft-lb/in² - NB
Average value: 19.0 kJ/m² Grade Count:4
Charpy Impact Unnotched 0.600 - 1000 J/cm²
2.86 - 4760 ft-lb/in²
Average value: 3.37 J/cm² Grade Count:13
1.50 - 999.9 J/cm²

@Temperature -20.0 - -20.0 °C
7.14 - 4759 ft-lb/in²

@Temperature -4.00 - -4.00 °F
Average value: 5.63 J/cm² Grade Count:9
Charpy Impact, Notched 0.130 - 1000 J/cm²
0.619 - 4760 ft-lb/in²
Average value: 4.67 J/cm² Grade Count:31
0.100 - 12.0 J/cm²

@Temperature -30.0 - 0.000 °C
0.476 - 57.1 ft-lb/in²

@Temperature -22.0 - 32.0 °F
Average value: 1.91 J/cm² Grade Count:27
Gardner Impact 16.3 - 40.7 J
12.0 - 30.0 ft-lb
Average value: 32.4 J Grade Count:8
2.26422 - 40.6746 J

@Temperature -30.0 - -20.0 °C
1.67000 - 30.0000 ft-lb

@Temperature -22.0 - -4.00 °F
Average value: 23.4 J Grade Count:21
16.6088 - 31.8618 J

@Temperature -30.0 - -28.9 °C
12.2500 - 23.5000 ft-lb

@Temperature -22.0 - -20.0 °F
Average value: 23.4 J Grade Count:12
16.6088 - 31.8618 J

@Thickness 3.17 - 3.17 mm
12.2500 - 23.5000 ft-lb

@Thickness 0.125 - 0.125 in
Average value: 23.4 J Grade Count:12
Falling Dart Impact 5.09788 - 5.09788 J

@Temperature -30.0 - -30.0 °C
3.76000 - 3.76000 ft-lb

@Temperature -22.0 - -22.0 °F
Average value: 5.10 J Grade Count:1
5.09788 - 5.09788 J

@Thickness 1.78 - 1.78 mm
3.76000 - 3.76000 ft-lb

@Thickness 0.0701 - 0.0701 in
Average value: 5.10 J Grade Count:1
Dart Drop Test 23.2 - 120 g
0.0512 - 0.265 lb
Average value: 56.8 g Grade Count:3
Film Tensile Strength at Break, MD 30.0 - 65.0 MPa
4350 - 9430 psi
Average value: 44.4 MPa Grade Count:5
Film Tensile Strength at Break, TD 25.0 - 60.0 MPa
3630 - 8700 psi
Average value: 36.8 MPa Grade Count:5
Tangent Modulus 740 - 1590 MPa
107000 - 230000 psi
Average value: 1250 MPa Grade Count:10
Thermal Properties Metric English Comments
Melting Point 120 - 327 °C
248 - 621 °F
Average value: 190 °C Grade Count:40
Electrical Properties Metric English Comments
Electrical Resistivity 100 - 1.00e+16 ohm-cm
100 - 1.00e+16 ohm-cm
Average value: 5.17e+15 ohm-cm Grade Count:6
Surface Resistance 10000 - 1.00e+15 ohm
10000 - 1.00e+15 ohm
Average value: 1.67e+14 ohm Grade Count:6
Static Decay 1.00 sec
1.00 sec
Average value: 1.00 sec Grade Count:3