Raschig Group MELOPAS® 2010 MF Melamine

Category Polymer , Thermoset , Melamine
Manufacturer Raschig Group
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Raschig Group MELOPAS® 2010 MF Melamine.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Organically and inorganically filled Melamine molding compound. Excellent surface hardness, good mechanical strength, good electrical properties. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS).Processing: Injection and compression molding Primary application: Mountings for household appliances, car ash-traysInformation provided by Raschig Group
Physical Properties Metric English Comments
Specific Gravity 1.50 - 1.70 g/cc
1.50 - 1.70 g/cc
ISO 1183
Apparent Bulk Density 0.550 - 0.750 g/cc
0.0199 - 0.0271 lb/in³
ISO 60
Water Absorption <= 2.00 %

@Temperature 23.0 °C,
Time 86400 sec
<= 2.00 %

@Temperature 73.4 °F,
Time 24.0 hour
ISO 62
Linear Mold Shrinkage, Flow 0.00500 - 0.0100 cm/cm
0.00500 - 0.0100 in/in
Compression; ISO 2577
0.00800 - 0.0130 cm/cm
0.00800 - 0.0130 in/in
Injection; ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength 40.0 - 65.0 MPa
5800 - 9430 psi
Compression; ISO 527
50.0 - 90.0 MPa
7250 - 13100 psi
Injection; ISO 527
Modulus of Elasticity 5.00 - 8.00 GPa
725 - 1160 ksi
Injection and Compression; ISO 527
Flexural Strength 90.0 - 120 MPa
13100 - 17400 psi
Compression; ISO 178
100 - 130 MPa
14500 - 18900 psi
Injection; ISO 178
Flexural Modulus 8.00 - 9.00 GPa
1160 - 1310 ksi
Injection and Compression; ISO 178
Compressive Strength 200 - 250 MPa
29000 - 36300 psi
ISO 604
Charpy Impact Unnotched 0.600 - 0.900 J/cm²
2.86 - 4.28 ft-lb/in²
Compression; ISO 179/1eU
0.800 - 1.40 J/cm²
3.81 - 6.66 ft-lb/in²
Injection; ISO 179/1eU
Charpy Impact, Notched 0.140 - 0.200 J/cm²
0.666 - 0.952 ft-lb/in²
Compression; ISO 179/1eA
0.150 - 0.200 J/cm²
0.714 - 0.952 ft-lb/in²
Injection; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 15.0 - 35.0 µm/m-°C

@Temperature 50.0 - 100 °C
8.33 - 19.4 µin/in-°F

@Temperature 122 - 212 °F
ISO 11359-2
Thermal Conductivity 0.400 - 0.500 W/m-K
2.78 - 3.47 BTU-in/hr-ft²-°F
ASTM E1461
Maximum Service Temperature, Air 135 °C

@Time 7.20e+7 sec
275 °F

@Time 20000 hour
IEC 60216/T1
160 °C

@Time <=180000 sec
320 °F

@Time <=50.0 hour
IEC 60216/T1
Deflection Temperature at 1.8 MPa (264 psi) 155 - 180 °C
311 - 356 °F
ISO 75-A
Deflection Temperature at 8.0 MPa 110 - 130 °C
230 - 266 °F
ISO 75-C
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
Shrinkage 1.00 - 1.50 %

@Temperature 110 °C,
Time 605000 sec
1.00 - 1.50 %

@Temperature 230 °F,
Time 168 hour
Post shrinkage; ISO 2577
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+11 - 1.00e+12 ohm-cm
1.00e+11 - 1.00e+12 ohm-cm
IEC 60093
Surface Resistance 1.00e+10 - 1.00e+11 ohm
1.00e+10 - 1.00e+11 ohm
IEC 60093
Dielectric Constant 7.00 - 9.00

@Frequency 1.00e+6 Hz
7.00 - 9.00

@Frequency 1.00e+6 Hz
IEC 60250
11.0 - 16.0

@Frequency 100 Hz
11.0 - 16.0

@Frequency 100 Hz
IEC 60250
Dielectric Strength 15.0 - 20.0 kV/mm
381 - 508 kV/in
IEC 60243-1
Dissipation Factor 0.0300 - 0.0500

@Frequency 1.00e+6 Hz
0.0300 - 0.0500

@Frequency 1.00e+6 Hz
IEC 60250
0.300 - 0.500

@Frequency 100 Hz
0.300 - 0.500

@Frequency 100 Hz
IEC 60250
Arc Resistance 120 - 180 sec
120 - 180 sec
ASTM D495
Comparative Tracking Index 600 V
600 V
IEC 60112
Processing Properties Metric English Comments
Shelf Life 6.00 Month

@Temperature 15.0 - 25.0 °C
6.00 Month

@Temperature 59.0 - 77.0 °F
Descriptive Properties Value Comments
Glow wire flammability test 960/1
IEC 60695 2-12
Glow wire ignitability test 900/1
IEC 60695 2-13
Water Absorption <115 mg
24 hr, 23°C; ISO 62