Lanxess Durethan® BKV 115 000000 Copolyamide, 15% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® BKV 115 000000 Copolyamide, 15% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
CoPA, injection molding grade, 15% glass fibers, elastomer-modified, electroplateable, higher notched impact strength and also higher energy absorption under biaxial impact load than BKV 15, even in the dry state, conditioning may be unnecessary in single cases
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ISO 1183 |
| Water Absorption | 8.5 % | 8.5 % | Test Sim. to ISO 62 |
| Moisture Absorption at Equilibrium | 2.5 % | 2.5 % | 23°C/50% R.H.; Test Sim. to ISO 62 |
| Viscosity Test | 134 cm³/g | 134 cm³/g | Viscosity number; ISO 307, 1157, 1628 |
| Linear Mold Shrinkage, Flow | 0.0038 cm/cm | 0.0038 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0051 cm/cm | 0.0051 in/in | ISO 294-4, 2577 |
| Melt Flow | 29 g/10 min @Load 5.00 kg, Temperature 260 °C |
29 g/10 min @Load 11.0 lb, Temperature 500 °F |
Calculated from MVR using melt density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 65.0 MPa | 9430 psi | Conditioned; ISO 527-1/-2 |
| 120 MPa | 17400 psi | ISO 527-1/-2 | |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527-1/-2 |
| 12 % | 12 % | Conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 2.80 GPa | 406 ksi | Conditioned; ISO 527-1/-2 |
| 5.70 GPa | 827 ksi | ISO 527-1/-2 | |
| Charpy Impact Unnotched | 4.00 J/cm² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eU |
| 4.50 J/cm² @Temperature -30.0 °C |
21.4 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |
| 6.50 J/cm² @Temperature 23.0 °C |
30.9 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| 8.00 J/cm² @Temperature 23.0 °C |
38.1 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eA | |
| <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |
| 2.00 J/cm² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eA | |
| Impact | 737 | 737 | Puncture maximum force (N); ISO 6603-2 |
| 636 @Temperature -30.0 °C |
636 @Temperature -22.0 °F |
Puncture maximum force (N); ISO 6603-2 | |
| Puncture Energy | 2.90 J | 2.14 ft-lb | ISO 6603-2 |
| 2.20 J @Temperature -30.0 °C |
1.62 ft-lb @Temperature -22.0 °F |
ISO 6603-2 | |
| 2.20 J @Temperature -30.0 °C |
1.62 ft-lb @Temperature -22.0 °F |
Conditioned; ISO 6603-2 | |
| Tensile Creep Modulus, 1 hour | 2600 MPa | 377000 psi | ISO 899-1 |
| Tensile Creep Modulus, 1000 hours | 2000 MPa | 290000 psi | ISO 899-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C | 16.7 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 100 µm/m-°C | 55.6 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 213 °C | 415 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 60.0 °C | 140 °F | ISO 75-1/-2 |
| Vicat Softening Point | 200 °C | 392 °F | 50°C/h 50N; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC 60695-11-10 |
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
IEC 60695-11-10 | |
| Oxygen Index | 22 % | 22 % | ISO 4589-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | Conditioned; IEC 60093 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 3.7 @Frequency 1.00e+6 Hz |
3.7 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 4.1 @Frequency 100 Hz |
4.1 @Frequency 100 Hz |
IEC 60250 | |
| 4.8 @Frequency 1.00e+6 Hz |
4.8 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 | |
| 8.0 @Frequency 100 Hz |
8.0 @Frequency 100 Hz |
Conditioned; IEC 60250 | |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | IEC 60243-1 |
| 35.0 kV/mm | 889 kV/in | Conditioned; IEC 60243-1 | |
| Dissipation Factor | 0.0080 @Frequency 100 Hz |
0.0080 @Frequency 100 Hz |
IEC 60250 |
| 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| 0.13 @Frequency 1.00e+6 Hz |
0.13 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 | |
| 0.215 @Frequency 100 Hz |
0.215 @Frequency 100 Hz |
Conditioned; IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Release agent | |
| Features | High impact or high impact modified | |
| Form | Pellets | |
| ISO Shortname | ISO 1874-PA 6/66-I, MR,14-060,GF15 | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Hong Kun Group Rhein Pharmaceutical Intermediate
- Kolon SPESIN® KP213G15BL Glass Fiber Reinforced PBT Compound Resin
- Solvay MIRAPOL® A-15 Surfactant
- ExxonMobil Mobil Velocite 3
- Eagle Brass 316L Austenitic Stainless Steel, Full Hardened
- 3M HDT Heat Shrink Tubing
- ATI Allegheny Ludlum Grade 11 Titanium (UNS R52250)
- 3M 8067 All Weather Flashing Tape
- DuPont Appeel® LSR 2044 Modified EVA Lidding Sealing Resin
Copyright © lookpolymers.com All Rights Reserved