DuPont Performance Polymers Hytrel® HTR8636 NC010 TPC-ET  (Unverified Data**)

Category Polymer , Thermoplastic , Elastomer, TPE , Polyester, TP , Polyester Thermoplastic Elastomer
Manufacturer DuPont Performance Polymers
Trade Name Hytrel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Hytrel® HTR8636 NC010 TPC-ET  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Hytrel® HTR8636 NC010 is a medium modulus Hytrel® grade with nominal durometer hardness of 40D. It contains non_discoloring stabilizer. It is specially suitable for extrusion processing.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.023 cm/cm

@Thickness 2.00 mm
 0.023 in/in

@Thickness 0.0787 in
 ISO 294-4
Linear Mold Shrinkage, Transverse 0.016 cm/cm

@Thickness 2.00 mm
 0.016 in/in

@Thickness 0.0787 in
 ISO 294-4
Melt Flow 6.5 g/10 min

@Load 10.0 kg,
Temperature 230 °C
 6.5 g/10 min

@Load 22.0 lb,
Temperature 446 °F
 ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D <= 38
<= 38
ISO 868
35

@Time 15.0 sec
 35

@Time 0.00417 hour
 ISO 868
Tensile Strength at Break 22.0 MPa

@Temperature 23.0 °C
 3190 psi

@Temperature 73.4 °F
 ISO 527 (1BA bar)
Tensile Stress 5.40 MPa

@Temperature 100 °C
 783 psi

@Temperature 212 °F
 ISO 527 (1BA bar)
36.4 MPa

@Temperature -40.0 °C
 5280 psi

@Temperature -40.0 °F
 ISO 527 (1BA bar)
1.30 MPa

@Strain 5.00 %,
Temperature 100 °C
 189 psi

@Strain 5.00 %,
Temperature 212 °F
 ISO 527 (1BA bar)
1.80 MPa

@Strain 10.0 %,
Temperature 100 °C
 261 psi

@Strain 10.0 %,
Temperature 212 °F
 ISO 527 (1BA bar)
2.80 MPa

@Strain 50.0 %,
Temperature 100 °C
 406 psi

@Strain 50.0 %,
Temperature 212 °F
 ISO 527 (1BA bar)
3.30 MPa

@Strain 100 %,
Temperature 100 °C
 479 psi

@Strain 100 %,
Temperature 212 °F
 ISO 527 (1BA bar)
3.40 MPa

@Strain 5.00 %,
Temperature 23.0 °C
 493 psi

@Strain 5.00 %,
Temperature 73.4 °F
 ISO 527 (1BA bar)
4.50 MPa

@Strain 200 %,
Temperature 100 °C
 653 psi

@Strain 200 %,
Temperature 212 °F
 ISO 527 (1BA bar)
5.90 MPa

@Strain 10.0 %,
Temperature 23.0 °C
 856 psi

@Strain 10.0 %,
Temperature 73.4 °F
 ISO 527 (1BA bar)
8.20 MPa

@Strain 50.0 %,
Temperature 23.0 °C
 1190 psi

@Strain 50.0 %,
Temperature 73.4 °F
 ISO 527 (1BA bar)
9.76 MPa

@Strain 5.00 %,
Temperature -40.0 °C
 1420 psi

@Strain 5.00 %,
Temperature -40.0 °F
 ISO 527 (1BA bar)
10.0 MPa

@Strain 100 %,
Temperature 23.0 °C
 1450 psi

@Strain 100 %,
Temperature 73.4 °F
 ISO 527 (1BA bar)
13.7 MPa

@Strain 200 %,
Temperature 23.0 °C
 1990 psi

@Strain 200 %,
Temperature 73.4 °F
 ISO 527 (1BA bar)
14.12 MPa

@Strain 10.0 %,
Temperature -40.0 °C
 2048 psi

@Strain 10.0 %,
Temperature -40.0 °F
 ISO 527 (1BA bar)
17.8 MPa

@Strain 50.0 %,
Temperature -40.0 °C
 2580 psi

@Strain 50.0 %,
Temperature -40.0 °F
 ISO 527 (1BA bar)
17.9 MPa

@Strain 300 %,
Temperature 23.0 °C
 2600 psi

@Strain 300 %,
Temperature 73.4 °F
 ISO 527 (1BA bar)
21.1 MPa

@Strain 100 %,
Temperature -40.0 °C
 3060 psi

@Strain 100 %,
Temperature -40.0 °F
 ISO 527 (1BA bar)
27.5 MPa

@Strain 200 %,
Temperature -40.0 °C
 3990 psi

@Strain 200 %,
Temperature -40.0 °F
 ISO 527 (1BA bar)
34.3 MPa

@Strain 300 %,
Temperature -40.0 °C
 4970 psi

@Strain 300 %,
Temperature -40.0 °F
 ISO 527 (1BA bar)
Elongation at Break >= 50 %

@Temperature 23.0 °C
 >= 50 %

@Temperature 73.4 °F
 nominal; ISO 527 (1BA bar)
192 %

@Temperature 100 °C
 192 %

@Temperature 212 °F
 nominal; ISO 527 (1BA bar)
263 %

@Temperature 100 °C
 263 %

@Temperature 212 °F
 ISO 527 (1BA bar)
277 %

@Temperature -40.0 °C
 277 %

@Temperature -40.0 °F
 nominal; ISO 527 (1BA bar)
337 %

@Temperature -40.0 °C
 337 %

@Temperature -40.0 °F
 ISO 527 (1BA bar)
348 %

@Temperature 23.0 °C
 348 %

@Temperature 73.4 °F
 nominal; ISO 527 (1BA bar)
394 %

@Temperature 23.0 °C
 394 %

@Temperature 73.4 °F
 ISO 527 (1BA bar)
Flexural Modulus 0.0340 GPa

@Temperature 100 °C
 4.93 ksi

@Temperature 212 °F
 ISO 178
0.0770 GPa

@Temperature 23.0 °C
 11.2 ksi

@Temperature 73.4 °F
 ISO 178
0.357 GPa

@Temperature -40.0 °C
 51.8 ksi

@Temperature -40.0 °F
 ISO 178
Thermal Properties Metric English Comments
Melting Point 207 °C
405 °F
10°C/min; ISO 11357-1/-3
Processing Properties Metric English Comments
Melt Temperature 225 °C
437 °F
Optimum; Extrusion
230 °C
446 °F
Optimum; Injection Molding
Mold Temperature 45.0 °C
113 °F
optimum; Injection Molding
45.0 - 55.0 °C
113 - 131 °F
Injection Molding
Drying Temperature 100 °C
212 °F
Extrusion
100 °C
212 °F
Injection Molding
Dry Time 2.00 - 3.00 hour
2.00 - 3.00 hour
Extrusion
2.00 - 3.00 hour
2.00 - 3.00 hour
Injection Molding
Moisture Content <= 0.050 %
<= 0.050 %
Extrusion
<= 0.080 %
<= 0.080 %
Injection Molding
Descriptive Properties Value Comments
Generic TPC-ET
Part Marking Code >TPC-ET<
ISO 11469
Product Category Extrusion Resins
Resin Identification TPC-ET
ISO 1043