Overview of materials for Polycarbonate, 40% Glass Filled

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 40% Glass Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polycarbonate, 40% Glass Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, 40% Glass Filled". Specific grades with glass content between 35% and 44% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.44 - 1.54 g/cc
0.0520 - 0.0556 lb/in³
Average value: 1.51 g/cc Grade Count:39
Filler Content 40.0 %
40.0 %
Average value: 40.0 % Grade Count:14
Water Absorption 0.0600 - 0.230 %
0.0600 - 0.230 %
Average value: 0.124 % Grade Count:20
Linear Mold Shrinkage 0.000 - 0.0120 cm/cm
0.000 - 0.0120 in/in
Average value: 0.00205 cm/cm Grade Count:38
Linear Mold Shrinkage, Transverse 0.00100 - 0.00300 cm/cm
0.00100 - 0.00300 in/in
Average value: 0.00250 cm/cm Grade Count:4
Melt Flow 2.00 - 33.0 g/10 min
2.00 - 33.0 g/10 min
Average value: 9.43 g/10 min Grade Count:18
Mechanical Properties Metric English Comments
Hardness, Rockwell M 91.0 - 100
91.0 - 100
Average value: 93.8 Grade Count:9
Hardness, Rockwell R 114 - 122
114 - 122
Average value: 119 Grade Count:9
Tensile Strength, Ultimate 103 - 166 MPa
15000 - 24000 psi
Average value: 143 MPa Grade Count:30
Tensile Strength, Yield 110 - 167 MPa
16000 - 24200 psi
Average value: 145 MPa Grade Count:16
Elongation at Break 1.50 - 6.00 %
1.50 - 6.00 %
Average value: 2.92 % Grade Count:29
Elongation at Yield 3.00 - 4.00 %
3.00 - 4.00 %
Average value: 3.50 % Grade Count:6
Modulus of Elasticity 5.50 - 12.4 GPa
798 - 1800 ksi
Average value: 10.4 GPa Grade Count:21
Flexural Yield Strength 138 - 216 MPa
20000 - 31300 psi
Average value: 190 MPa Grade Count:34
Flexural Modulus 7.00 - 11.7 GPa
1020 - 1700 ksi
Average value: 9.72 GPa Grade Count:39
Compressive Yield Strength 145 - 152 MPa
21000 - 22000 psi
Average value: 148 MPa Grade Count:4
Izod Impact, Notched 0.534 - 1.87 J/cm
1.00 - 3.50 ft-lb/in
Average value: 1.27 J/cm Grade Count:38
Izod Impact, Unnotched 2.67 - 12.8 J/cm
5.00 - 24.0 ft-lb/in
Average value: 8.44 J/cm Grade Count:13
Thermal Properties Metric English Comments
CTE, linear 16.2 - 20.0 µm/m-°C
9.00 - 11.1 µin/in-°F
Average value: 18.3 µm/m-°C Grade Count:7
Thermal Conductivity 0.220 - 0.346 W/m-K
1.53 - 2.40 BTU-in/hr-ft²-°F
Average value: 0.300 W/m-K Grade Count:5
Deflection Temperature at 0.46 MPa (66 psi) 98.9 - 155 °C
210 - 311 °F
Average value: 148 °C Grade Count:26
Deflection Temperature at 1.8 MPa (264 psi) 91.1 - 149 °C
196 - 300 °F
Average value: 143 °C Grade Count:33
Vicat Softening Point 98.9 - 166 °C
210 - 331 °F
Average value: 154 °C Grade Count:8
Flammability, UL94 HB - 5VA
HB - 5VA
Grade Count:26
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+9 - 1.00e+17 ohm-cm
1.00e+9 - 1.00e+17 ohm-cm
Average value: 1.98e+16 ohm-cm Grade Count:15
Surface Resistance 1.00e+10 - 1.00e+15 ohm
1.00e+10 - 1.00e+15 ohm
Average value: 5.25e+14 ohm Grade Count:4
Dielectric Constant 3.30 - 3.60
3.30 - 3.60
Average value: 3.45 Grade Count:6
Dielectric Strength 16.1 - 45.0 kV/mm
410 - 1140 kV/in
Average value: 24.1 kV/mm Grade Count:9
Dissipation Factor 0.000900 - 0.00900
0.000900 - 0.00900
Average value: 0.00501 Grade Count:5
Arc Resistance 120 sec
120 sec
Average value: 120 sec Grade Count:5
Processing Properties Metric English Comments
Processing Temperature 204 - 299 °C
400 - 570 °F
Average value: 269 °C Grade Count:8
Nozzle Temperature 271 - 338 °C
520 - 640 °F
Average value: 306 °C Grade Count:3
Melt Temperature 260 - 343 °C
500 - 650 °F
Average value: 306 °C Grade Count:9
Mold Temperature 48.9 - 121 °C
120 - 250 °F
Average value: 91.0 °C Grade Count:16
Drying Temperature 82.2 - 124 °C
180 - 255 °F
Average value: 114 °C Grade Count:7
Moisture Content 0.0200 %
0.0200 %
Average value: 0.0200 % Grade Count:4
Dew Point -28.9 °C
-20.0 °F
Average value: -28.9 °C Grade Count:3
Injection Pressure 11.0 - 138 MPa
1600 - 20000 psi
Average value: 79.9 MPa Grade Count:11