Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycoloy®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycoloy® C2951 PC+ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
CYCOLOY C2951 is a flame retardant PC+ABS free from chlorinated or brominated flame retardant additives. High heat resistance is offered for demanding electrical applications, whilst maintaining excellent processability. It is listed under UL-94 5VA at 3.0 mm.
Physical Properties Metric English Comments
Specific Gravity 1.19 g/cc
1.19 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0060 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 10 g/10 min

@Load 2.16 kg,
Temperature 260 °C
10 g/10 min

@Load 4.76 lb,
Temperature 500 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 50.0 MPa
7250 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 63.0 MPa
9140 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 80 %
80 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 4.5 %
4.5 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.90 GPa
421 ksi
50 mm/min; ASTM D638
Flexural Yield Strength 93.0 MPa
13500 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.55 GPa
370 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 5.87 J/cm
11.0 ft-lb/in
ASTM D256
Dart Drop, Total Energy 54.0 J

@Temperature 23.0 °C
39.8 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 72.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
40.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 72.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
40.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 103 °C

@Thickness 6.40 mm
217 °F

@Thickness 0.252 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 89.0 °C

@Thickness 3.20 mm
192 °F

@Thickness 0.126 in
unannealed; ASTM D648
94.0 °C

@Thickness 6.40 mm
201 °F

@Thickness 0.252 in
unannealed; ASTM D648
Vicat Softening Point 105 °C
221 °F
Rate B/50; ASTM D1525
UL RTI, Electrical 85.0 °C
185 °F
UL 746B
UL RTI, Mechanical with Impact 85.0 °C
185 °F
UL 746B
UL RTI, Mechanical without Impact 85.0 °C
185 °F
UL 746B
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
UL 94
5VB

@Thickness 2.50 mm
5VB

@Thickness 0.0984 in
UL 94
5VA

@Thickness 3.00 mm
5VA

@Thickness 0.118 in
UL 94
Electrical Properties Metric English Comments
Arc Resistance 60 - 120 sec
60 - 120 sec
Tungsten; ASTM D495
Comparative Tracking Index 400 - 600 V
400 - 600 V
UL 746A
Hot Wire Ignition, HWI 60 - 120 sec
60 - 120 sec
UL 746A
High Amp Arc Ignition, HAI >= 120 arcs
>= 120 arcs
UL 746A
High Voltage Arc-Tracking Rate, HVTR 25.4 - 80.0 mm/min
1.00 - 3.15 in/min
UL 746A