Solvay Specialty Polymers Ixef® 1524 Polyarylamide (PARA), 50% Glass Fiber (Dry)

Category Polymer , Thermoplastic , PVDC , Polyvinyl Dichloride (PVDC)
Manufacturer Solvay Specialty Polymers
Trade Name Ixef®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Ixef® 1524 Polyarylamide (PARA), 50% Glass Fiber (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ixef® 1524 is a 50% glass-fiber reinforced, halogen-free flame retardant polyarylamide which exhibits high strength and stiffness, good surface gloss, and excellent creep resistance.Features: Bromine Free; Flame Retardant; Good Chemical Resistance; Good Creep Resistance; Good Dimensional Stability; Halogen Free; High Flow; High Strength; Low Moisture Absorption; Outstanding Surface Finish; Ultra High StiffnessUses: Cell Phones; Electrical/Electronic Applications; HousingsInjection Molding Notes: Ixef® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Ixef® resins be dried prior to molding.Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.68 g/cc
0.0607 lb/in³
ISO 1183
Filler Content 50 %
50 %
Glass Fiber
Water Absorption 0.30 %

@Time 86400 sec
 0.30 %

@Time 24.0 hour
 ISO 62
Water Absorption at Saturation 1.0 %
1.0 %
50% RH; ASTM D570
1.3 %
1.3 %
65% RH; ASTM D570
Linear Mold Shrinkage, Flow 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength, Yield 230 MPa
33400 psi
ISO 527-2
Elongation at Break 1.9 %
1.9 %
ISO 527-2
Tensile Modulus 20.0 GPa
2900 ksi
ISO 527-2
Flexural Strength 330 MPa
47900 psi
ISO 178
Flexural Modulus 18.5 GPa
2680 ksi
ISO 178
Charpy Impact Unnotched 4.80 J/cm²
22.8 ft-lb/in²
Type 1, Edgewise; ISO 179
Charpy Impact, Notched 0.930 J/cm²
4.43 ft-lb/in²
Type 1, Edgewise; ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 227 °C
441 °F
Unannealed; ISO 75-2/A
Flammability, UL94 V-0

@Thickness 0.400 mm
 V-0

@Thickness 0.0157 in
Oxygen Index 37 %
37 %
ISO 4589-2
Glow Wire Test 775 °C

@Thickness 0.400 mm
 1430 °F

@Thickness 0.0157 in
 Glow Wire Ignition Temperature; IEC 60695-2-13
825 °C

@Thickness 1.50 mm
 1520 °F

@Thickness 0.0591 in
 Glow Wire Ignition Temperature; IEC 60695-2-13
850 °C

@Thickness 3.00 mm
 1560 °F

@Thickness 0.118 in
 Glow Wire Ignition Temperature; IEC 60695-2-13
Electrical Properties Metric English Comments
Dielectric Constant 4.44

@Frequency 2.40e+9 Hz
 4.44

@Frequency 2.40e+9 Hz
 ASTM D2520
Dissipation Factor 0.012

@Frequency 2.40e+9 Hz
 0.012

@Frequency 2.40e+9 Hz
 Method B; ASTM D2520
High Voltage Arc Resistance to Ignition (HVAR) >= 300 sec
>= 300 sec
UL 746
Comparative Tracking Index >= 600 V
>= 600 V
UL 746
>= 600 V
>= 600 V
IEC 60112
>= 600 V
>= 600 V
PLC 0; UL 746
Hot Wire Ignition, HWI 95 sec

@Thickness 0.400 mm
 95 sec

@Thickness 0.0157 in
 UL 746
>= 120 sec

@Thickness 3.00 mm
 >= 120 sec

@Thickness 0.118 in
 UL 746
>= 120 sec

@Thickness 1.50 mm
 >= 120 sec

@Thickness 0.0591 in
 UL 746
>= 120 sec

@Thickness 0.750 mm
 >= 120 sec

@Thickness 0.0295 in
 UL 746
High Amp Arc Ignition, HAI 37.6 arcs

@Thickness 0.400 mm
 37.6 arcs

@Thickness 0.0157 in
 UL 746
53.6 arcs

@Thickness 0.750 mm
 53.6 arcs

@Thickness 0.0295 in
 UL 746
70.2 arcs

@Thickness 1.50 mm
 70.2 arcs

@Thickness 0.0591 in
 UL 746
95.4 arcs

@Thickness 3.00 mm
 95.4 arcs

@Thickness 0.118 in
 UL 746
High Voltage Arc-Tracking Rate, HVTR 0.000 - 10.0 mm/min
0.000 - 0.394 in/min
UL 746
Processing Properties Metric English Comments
Rear Barrel Temperature 250 - 260 °C
482 - 500 °F
Front Barrel Temperature 260 - 290 °C
500 - 554 °F
Melt Temperature 280 °C
536 °F
Mold Temperature 120 - 140 °C
248 - 284 °F
Drying Temperature 100 °C

@Time 3600 - 10800 sec
 212 °F

@Time 1.00 - 3.00 hour
Descriptive Properties Value Comments
Additive Flame Retardant
Availability Africa & Middle East
Asia Pacific
Europe
Latin America
North America
Color Black; Colors
Form Pellets
Processing Technique Injection Molding
RoHS Compliance RoHS Compliant