Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 22.0 MPa | 3190 psi | ISO 527-1 |
Polikim ULPOLEN® 1000 UHMWPE, Flame Retardant For those producing flammable materials and in the mining industry, explosion and fire are major dangers. It is of vital importance that in conveyor belts and bunkers, lining material is flame retar.. |
|||
Tensile Strength, Ultimate | 22.0 - 62.0 MPa | 3190 - 8990 psi | Average value: 46.6 MPa Grade Count:71 |
Overview of materials for Polystyrene, Heat Resistant Grade This property data is a summary of similar materials in the MatWeb database for the category "Polystyrene, Heat Resistant Grade". Each property range of values reported is minimum and maximum values.. |
|||
Tensile Strength, Ultimate | 22.0 MPa | 3190 psi | ASTM Data |
Americas Styrenics Styron® 484C High Impact Polystyrene
(discontinued **) STYRON® 484C high impact polystyrene resin, is typically used in refrigeration applications, appliances, containers, lids, furniture and profiles. It offers excellent low temperature toughness, exc.. |
|||
Tensile Strength, Ultimate | 22.0 MPa | 3190 psi | 500 mm/min (20 in./min.); ASTM D638, Type IV Specimen |
Eastman M3016-P Polyethylene
(discontinued **) M3016-P is suggested for applications such as spiral-wound can linings, release paper, and photographic paper. M3016-P Has been found to exhibit good barrier properties, temperature resistance, and.. |
|||
Tensile Strength, Ultimate | 22.0 - 28.0 MPa | 3190 - 4060 psi | |
Solvay Specialty Polymers Hyflon® PFA 450 Fluoropolymer
(discontinued **) Data provided by the manufacturer.Hyflon® PFA 450 has outstanding physical and chemical properties typical of fluoropolymers.Hyflon® PFA 420 |
|||
Tensile Strength, Ultimate | 22.0 - 31.0 MPa | 3190 - 4500 psi | Average value: 28.3 MPa Grade Count:6 |
Overview of materials for High Density Polyethylene (HDPE), Carbon Black Filled This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Carbon Black Filled". Each property range of values reported is minimu.. |
|||
Tensile Strength, Ultimate | 22.0 - 39.0 MPa | 3190 - 5660 psi | Average value: 31.6 MPa Grade Count:18 |
Overview of materials for Polyperfluoroalkoxyethylene (PFA), Molded/Extruded This property data is a summary of similar materials in the MatWeb database for the category "Polyperfluoroalkoxyethylene, Molded/Extruded". Each property range of values reported is minimum and max.. |
|||
Tensile Strength, Ultimate | 22.0 MPa @Temperature 90.0 °C |
3190 psi @Temperature 194 °F |
ISO 527 |
LATI LATILUB 82-01M Nylon 12 Base, 1% Molybdenum Disulfide Self Lubricating Plastic
(discontinued **) Description: Latilub self-lubricating plastic materials are more and more often designed to replace metals in applications such as gears, bushings, cams, slides, etc), for which, besides their intri.. |
|||
Tensile Strength, Ultimate | 22.0 - 80.0 MPa @Temperature 80.0 - 120 °C |
3190 - 11600 psi @Temperature 176 - 248 °F |
Average value: 50.9 MPa Grade Count:1 |
Overview of materials for Nylon 66, Glass/Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Glass/Mineral Filled". Each property range of values reported is minimum and maximum values of.. |
|||
Tensile Strength, Ultimate | 22.0 - 80.0 MPa @Strain 1.00 - 8.00 % |
3190 - 11600 psi @Strain 1.00 - 8.00 % |
Average value: 50.9 MPa Grade Count:1 |
Overview of materials for Nylon 66, Glass/Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Glass/Mineral Filled". Each property range of values reported is minimum and maximum values of.. |
|||
Tensile Strength, Ultimate | >= 22.0 MPa | >= 3190 psi | ISO 1184-1983E |
LyondellBasell Montell 0800 Polybutene Key Features: highly isotactic, semi-crystalline homopolymer, good creep resistance, good environmental crack resistance, miscible with polypropylenes, FDA acceptableApplications: concrete carrierMe.. |
|||
Tensile Strength, Ultimate | 22.0 MPa | 3190 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 393 Ionomer DescriptionFormion® FI 393 is a 10% glass fiber reinforced, injection molding grade Ionomer, which has been formulated for scratch resistance, low CLTE, and impact. Formion F1 393U is UV stabilized.. |
|||
Tensile Strength, Ultimate | 22.0 MPa | 3190 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 393 Ionomer DescriptionFormion® FI 393 is a 10% glass fiber reinforced, injection molding grade Ionomer, which has been formulated for scratch resistance, low CLTE, and impact. Formion F1 393U is UV stabilized.. |
|||
Tensile Strength, Ultimate | 22.0 MPa | 3190 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 393 Ionomer DescriptionFormion® FI 393 is a 10% glass fiber reinforced, injection molding grade Ionomer, which has been formulated for scratch resistance, low CLTE, and impact. Formion F1 393U is UV stabilized.. |
|||
Tensile Strength, Ultimate | 22.0 MPa | 3190 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 393 Ionomer DescriptionFormion® FI 393 is a 10% glass fiber reinforced, injection molding grade Ionomer, which has been formulated for scratch resistance, low CLTE, and impact. Formion F1 393U is UV stabilized.. |
|||
Tensile Strength, Ultimate | 22.0 MPa | 3190 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 393 Ionomer DescriptionFormion® FI 393 is a 10% glass fiber reinforced, injection molding grade Ionomer, which has been formulated for scratch resistance, low CLTE, and impact. Formion F1 393U is UV stabilized.. |
|||
Tensile Strength, Ultimate | 22.0 MPa | 3190 psi | ASTM D638/D412 |
Covestro Baydur® STR/F-275 IMR Polyurethane Composite SRIM Foam, 20% Glass Filled, MDI-based 2-Component Liquid System Contains continuous strand fiberglass mat.0.0985 in. thickness.Information provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer.. |
|||
Tensile Strength, Ultimate | 22.0 MPa | 3190 psi | ASTM D638/D412 |
Covestro Bayflex® 110-80 Polyurethane Elastomeric RIM, 15% Milled Glass Reinforced, MDI-based 2-Component Liquid System 0.125 in. thickness. RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and o.. |
|||
Tensile Strength, Ultimate | 22.0 MPa | 3190 psi | ISO 527 |
DSM Fibre Intermediates Nyrim® 2025 (Wollastocoat®), Conditioned Conditioned at 23°C and 50% Relative Humidity.Nyrim is a Block Copolymer of Nylon 6 and an elastomer with exceptional properties in impact resistance, fatigue and abrasion resistance. Nyrim is proc.. |
|||
Tensile Strength, Ultimate | 22.0 MPa | 3190 psi | ISO 527 |
DSM Fibre Intermediates Nyrim® 4000 (Conditioned) Conditioned at 23°C and 50% Relative Humidity.Nyrim is a Block Copolymer of Nylon 6 and an elastomer with exceptional properties in impact resistance, fatigue and abrasion resistance. Nyrim is proc.. |
|||
Tensile Strength, Ultimate | 22.0 MPa | 3190 psi | Vulcanizate, Press cured, TC95 +3min at 160°C |
Dow Nordel® IP 4725P Heat Resistant Molding FormulationNordel® IP 4725P |
|||
Tensile Strength, Ultimate | 22.0 MPa | 3190 psi | Die C (35 min / 145°C); ASTM D412 |
Dow SE SLR-4400 Solution polymerized Styrene Butadiene Rubber (S-SBR) SE SLR-4400 is manufactured by anionic solution polymerization using lithium initiator. It is a product with medium styrene and high vinyl content. The product is partially Sn-coupled and non-stai.. |
|||
Tensile Strength, Ultimate | 22.0 MPa @Thickness 1.14 - 1.52 mm, Temperature 704 °C |
3190 psi @Thickness 0.0449 - 0.0598 in, Temperature 1300 °F |
|
AK Steel 409 Ferritic Stainless steel AK Steel 409 Stainless Steels are especially useful for applications where oxidation or corrosion protection beyond the capacity of carbon steel and some coated steels is needed. Current applicatio.. |
|||
Tensile Strength, Ultimate | 22.0 MPa | 3190 psi | |
BASF Lucalen® A 2910 M Ethylene/Acrylate Copolymer For coating metals such as aluminum and steel, and as a primer for composites of metal or paper with Lupolen. Contains an antioxidant.Data was collected by ISO methods and provided by BASF. |
|||
Tensile Strength, Ultimate | 22.0 MPa | 3190 psi | DIN 53455 |
Ineos Nova S-3201 Medium Impact Compact Polystyrene
(discontinued **) Extremely easy flowing medium impact polystyrene, designed for extreme short cycle times for injection molding of household, packaging and toys. The material is provided with external lubricant to .. |
|||
Tensile Strength, Ultimate | 22.0 - 90.0 MPa | 3190 - 13100 psi | Average value: 45.3 MPa Grade Count:27 |
Overview of materials for Polyethylene Terephthalate (PET), Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), Unreinforced". Each property range of values reported is minimum and m.. |
|||
Tensile Strength, Ultimate | 22.0 - 200 MPa | 3190 - 29000 psi | Average value: 62.0 MPa Grade Count:104 |
Overview of materials for Nylon 6, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Impact Grade". Each property range of values reported is minimum and maximum values of appropri.. |
|||
Tensile Strength, Ultimate | 22.0 MPa | 3190 psi | ASTM D638 |
Elastomer Engineering Elastamide 400 Elastomer Modified RIM Nylon 6 18% crystallinity. Information supplied by Elastomer Engineering. |
|||
Tensile Strength, Ultimate | 22.0 - 115 MPa | 3190 - 16700 psi | Average value: 60.9 MPa Grade Count:150 |
Overview of materials for Polypropylene with 20% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 20% Glass Fiber Filler". Specific grades with glass content between 15% and 24% are i.. |