Outokumpu 4404 Cr-Ni-Mo Austenitic Stainless Steel

Category Metal , Ferrous Metal , Austenitic , Stainless Steel
Manufacturer Outokumpu
Trade Name
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF Outokumpu 4404 Cr-Ni-Mo Austenitic Stainless Steel.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
General purpose steel with excellent corrosion resistance, particularly in the presence of halides.Applications: FiltersBraiding for hydraulic hosesShaftsFastenersMarine componentsAvailable in hot rolled plate (Quarto), hot rolled strip/sheet (CPP), cold rolled strip/sheet, cold rolled narrow strip, bar, and rod forms.
Physical Properties Metric English Comments
Density 8.00 g/cc
0.289 lb/in³
RT
Mechanical Properties Metric English Comments
Hardness, Brinell 165
165
Outokumpu Typical, 20°C, Hot rolled plate (Quarto)/Cold rolled strip/sheet; EN 10003-1
Tensile Strength, Ultimate 570 MPa
82700 psi
Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1
380 MPa
<br>@Temperature 300 °C
 55100 psi
<br>@Temperature 572 °F
 EN min.; EN 10002-5
390 MPa
<br>@Temperature 200 °C
 56600 psi
<br>@Temperature 392 °F
 EN min.; EN 10002-5
430 MPa
<br>@Temperature 100 °C
 62400 psi
<br>@Temperature 212 °F
 EN min.; EN 10002-5
840 MPa
<br>@Temperature -80.0 °C
 122000 psi
<br>@Temperature -112 °F
 EN min; EN 10002-5
1200 MPa
<br>@Temperature -196 °C
 174000 psi
<br>@Temperature -321 °F
 EN min; EN 10002-5
Tensile Strength, Yield 220 MPa
<br>@Strain 0.200 %
 31900 psi
<br>@Strain 0.200 %
 EN min.,RT; EN 10002-1
280 MPa
<br>@Strain 0.200 %
 40600 psi
<br>@Strain 0.200 %
 Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1
320 MPa
<br>@Strain 1.00 %
 46400 psi
<br>@Strain 1.00 %
 Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1
110 MPa
<br>@Strain 0.200 %,<br> Temperature 500 °C
 16000 psi
<br>@Strain 0.200 %,<br> Temperature 932 °F
 EN min.; EN 10002-5
115 MPa
<br>@Strain 0.200 %,<br> Temperature 400 °C
 16700 psi
<br>@Strain 0.200 %,<br> Temperature 752 °F
 EN min.; EN 10002-5
127 MPa
<br>@Strain 0.200 %,<br> Temperature 300 °C
 18400 psi
<br>@Strain 0.200 %,<br> Temperature 572 °F
 EN min.; EN 10002-5
139 MPa
<br>@Strain 1.00 %,<br> Temperature 500 °C
 20200 psi
<br>@Strain 1.00 %,<br> Temperature 932 °F
 EN min.; EN 10002-5
144 MPa
<br>@Strain 1.00 %,<br> Temperature 400 °C
 20900 psi
<br>@Strain 1.00 %,<br> Temperature 752 °F
 EN min.; EN 10002-5
147 MPa
<br>@Strain 0.200 %,<br> Temperature 200 °C
 21300 psi
<br>@Strain 0.200 %,<br> Temperature 392 °F
 EN min.; EN 10002-5
156 MPa
<br>@Strain 1.00 %,<br> Temperature 300 °C
 22600 psi
<br>@Strain 1.00 %,<br> Temperature 572 °F
 EN min.; EN 10002-5
177 MPa
<br>@Strain 0.200 %,<br> Temperature 100 °C
 25700 psi
<br>@Strain 0.200 %,<br> Temperature 212 °F
 EN min.; EN 10002-5
177 MPa
<br>@Strain 1.00 %,<br> Temperature 200 °C
 25700 psi
<br>@Strain 1.00 %,<br> Temperature 392 °F
 EN min.; EN 10002-5
211 MPa
<br>@Strain 1.00 %,<br> Temperature 100 °C
 30600 psi
<br>@Strain 1.00 %,<br> Temperature 212 °F
 EN min.; EN 10002-5
275 MPa
<br>@Strain 0.200 %,<br> Temperature -80.0 °C
 39900 psi
<br>@Strain 0.200 %,<br> Temperature -112 °F
 EN min.; EN 10002-5
350 MPa
<br>@Strain 0.200 %,<br> Temperature -196 °C
 50800 psi
<br>@Strain 0.200 %,<br> Temperature -321 °F
 EN min.; EN 10002-5
355 MPa
<br>@Strain 1.00 %,<br> Temperature -80.0 °C
 51500 psi
<br>@Strain 1.00 %,<br> Temperature -112 °F
 EN min.; EN 10002-5
450 MPa
<br>@Strain 1.00 %,<br> Temperature -196 °C
 65300 psi
<br>@Strain 1.00 %,<br> Temperature -321 °F
 EN min.; EN 10002-5
Elongation at Break 55 %
55 %
Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1
35 %
<br>@Temperature -196 °C
 35 %
<br>@Temperature -321 °F
 EN min
40 %
<br>@Temperature -80.0 °C
 40 %
<br>@Temperature -112 °F
 EN min
Modulus of Elasticity 200 GPa
29000 ksi
RT
165 GPa
<br>@Temperature 500 °C
 23900 ksi
<br>@Temperature 932 °F
172 GPa
<br>@Temperature 400 °C
 24900 ksi
<br>@Temperature 752 °F
179 GPa
<br>@Temperature 300 °C
 26000 ksi
<br>@Temperature 572 °F
186 GPa
<br>@Temperature 200 °C
 27000 ksi
<br>@Temperature 392 °F
194 GPa
<br>@Temperature 100 °C
 28100 ksi
<br>@Temperature 212 °F
Poissons Ratio 0.30
0.30
RT
Fatigue Strength 578 MPa
83800 psi
R=smin/smax=0.1; 2 million cycles, F50
360 MPa
<br>@# of Cycles 2.00e+6
52200 psi
<br>@# of Cycles 2.00e+6
R=smin/smax=0.1;RT; 50% probability of failure
280 MPa
<br>@Strain 0.200 %
 40600 psi
<br>@Strain 0.200 %
 R=smin/smax=0.1; 2 million cycles, F50
Shear Modulus 77.0 GPa
11200 ksi
calculated
Impact Test >= 60.0 J
>= 44.3 ft-lb
Hot rolled plate/Cold rolled strip/sheet, 10x10mm test pieces; EN 10045-1
Thermal Properties Metric English Comments
CTE, linear 16.0 µm/m-°C
<br>@Temperature 100 °C
 8.89 µin/in-°F
<br>@Temperature 212 °F
17.5 µm/m-°C
<br>@Temperature 400 °C
 9.72 µin/in-°F
<br>@Temperature 752 °F
Specific Heat Capacity 0.500 J/g-°C
0.120 BTU/lb-°F
RT
Thermal Conductivity 15.0 W/m-K
104 BTU-in/hr-ft²-°F
RT
20.0 W/m-K
<br>@Temperature 400 °C
 139 BTU-in/hr-ft²-°F
<br>@Temperature 752 °F
Component Elements Properties Metric English Comments
Carbon, C 0.020 %
0.020 %
Chromium, Cr 17.2 %
17.2 %
Iron, Fe 70.58 %
70.58 %
Molybdenum, Mo 2.1 %
2.1 %
Nickel, Ni 10.1 %
10.1 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.0000750 ohm-cm
0.0000750 ohm-cm
RT