Overview of materials for Nylon 610, Glass Reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 610 , Nylon 610, Glass Reinforced
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Nylon 610, Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 610, Glass Reinforced". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.15 - 1.63 g/cc
0.0415 - 0.0589 lb/in³
Average value: 1.36 g/cc Grade Count:85
Filler Content 10.0 - 50.0 %
10.0 - 50.0 %
Average value: 29.4 % Grade Count:43
Water Absorption 0.0900 - 4.00 %
0.0900 - 4.00 %
Average value: 0.946 % Grade Count:49
0.900 - 1.50 %

@Temperature 70.0 - 70.0 °C
0.900 - 1.50 %

@Temperature 158 - 158 °F
Average value: 1.23 % Grade Count:8
Moisture Absorption at Equilibrium 0.0900 - 1.30 %
0.0900 - 1.30 %
Average value: 0.935 % Grade Count:14
Water Absorption at Saturation 0.400 - 1.20 %

@Temperature 45.0 - 400 °C
0.400 - 1.20 %

@Temperature 113 - 752 °F
Average value: 0.814 % Grade Count:2
0.400 - 1.20 %

@Treatment Temp. 70.0 - 70.0 °C
0.400 - 1.20 %

@Treatment Temp. 158 - 158 °F
Average value: 0.814 % Grade Count:2
Linear Mold Shrinkage 0.00100 - 0.0100 cm/cm
0.00100 - 0.0100 in/in
Average value: 0.00356 cm/cm Grade Count:76
Linear Mold Shrinkage, Transverse 0.00330 - 0.0110 cm/cm
0.00330 - 0.0110 in/in
Average value: 0.00903 cm/cm Grade Count:37
Melt Flow 5.00 - 39.3 g/10 min
5.00 - 39.3 g/10 min
Average value: 31.5 g/10 min Grade Count:9
Spiral Flow 35.0 - 45.0 cm
13.8 - 17.7 in
Average value: 41.3 cm Grade Count:8
Mechanical Properties Metric English Comments
Hardness, Rockwell R 117 - 120
117 - 120
Average value: 119 Grade Count:15
Ball Indentation Hardness 120 - 245 MPa
17400 - 35500 psi
Average value: 183 MPa Grade Count:12
Tensile Strength, Ultimate 75.0 - 222 MPa
10900 - 32200 psi
Average value: 145 MPa Grade Count:80
70.0 - 155 MPa

@Temperature 60.0 - 150 °C
10200 - 22500 psi

@Temperature 140 - 302 °F
Average value: 108 MPa Grade Count:2
Tensile Strength, Yield 140 - 230 MPa
20300 - 33400 psi
Average value: 170 MPa Grade Count:10
Elongation at Break 2.00 - 25.0 %
2.00 - 25.0 %
Average value: 4.95 % Grade Count:75
3.30 - 6.10 %

@Temperature 60.0 - 150 °C
3.30 - 6.10 %

@Temperature 140 - 302 °F
Average value: 4.59 % Grade Count:2
Elongation at Yield 2.50 - 6.00 %
2.50 - 6.00 %
Average value: 3.79 % Grade Count:18
Modulus of Elasticity 3.50 - 19.0 GPa
508 - 2760 ksi
Average value: 9.24 GPa Grade Count:75
3.00 - 9.80 GPa

@Temperature 60.0 - 150 °C
435 - 1420 ksi

@Temperature 140 - 302 °F
Average value: 5.86 GPa Grade Count:2
Flexural Yield Strength 121 - 355 MPa
17500 - 51500 psi
Average value: 222 MPa Grade Count:62
Flexural Modulus 3.45 - 17.0 GPa
500 - 2470 ksi
Average value: 8.25 GPa Grade Count:66
Compressive Yield Strength 100 - 179 MPa
14500 - 26000 psi
Average value: 150 MPa Grade Count:10
Izod Impact, Notched 0.534 - 1.87 J/cm
1.00 - 3.50 ft-lb/in
Average value: 1.25 J/cm Grade Count:44
Izod Impact, Unnotched 4.27 - 13.7 J/cm
8.00 - 25.7 ft-lb/in
Average value: 9.46 J/cm Grade Count:32
Izod Impact, Notched (ISO) 9.70 - 20.0 kJ/m²
4.62 - 9.52 ft-lb/in²
Average value: 15.6 kJ/m² Grade Count:7
Izod Impact, Unnotched (ISO) 65.0 - 95.0 kJ/m²
30.9 - 45.2 ft-lb/in²
Average value: 82.2 kJ/m² Grade Count:7
Charpy Impact Unnotched 7.50 - 11.0 J/cm²
35.7 - 52.4 ft-lb/in²
Average value: 9.17 J/cm² Grade Count:39
6.00 - 11.0 J/cm²

@Temperature -30.0 - 30.0 °C
28.6 - 52.4 ft-lb/in²

@Temperature -22.0 - 86.0 °F
Average value: 8.87 J/cm² Grade Count:24
Charpy Impact, Notched 0.500 - 3.10 J/cm²
2.38 - 14.8 ft-lb/in²
Average value: 1.58 J/cm² Grade Count:31
0.500 - 1.80 J/cm²

@Temperature -30.0 - 30.0 °C
2.38 - 8.57 ft-lb/in²

@Temperature -22.0 - 86.0 °F
Average value: 1.11 J/cm² Grade Count:24
Falling Dart Impact 8.50 - 11.8 J
6.27 - 8.70 ft-lb
Average value: 9.88 J Grade Count:4
Thermal Properties Metric English Comments
CTE, linear 15.3 - 48.6 µm/m-°C
8.50 - 27.0 µin/in-°F
Average value: 28.0 µm/m-°C Grade Count:23
CTE, linear, Transverse to Flow 72.0 - 88.0 µm/m-°C
40.0 - 48.9 µin/in-°F
Average value: 80.0 µm/m-°C Grade Count:7
Thermal Conductivity 0.300 - 0.562 W/m-K
2.08 - 3.90 BTU-in/hr-ft²-°F
Average value: 0.467 W/m-K Grade Count:10
Melting Point 214 - 260 °C
418 - 500 °F
Average value: 222 °C Grade Count:41
Maximum Service Temperature, Air 90.0 - 160 °C
194 - 320 °F
Average value: 133 °C Grade Count:10
Deflection Temperature at 0.46 MPa (66 psi) 207 - 224 °C
405 - 435 °F
Average value: 220 °C Grade Count:32
Deflection Temperature at 1.8 MPa (264 psi) 190 - 218 °C
374 - 425 °F
Average value: 207 °C Grade Count:62
Deflection Temperature at 8.0 MPa 75.0 - 170 °C
167 - 338 °F
Average value: 133 °C Grade Count:16
Vicat Softening Point 217 - 220 °C
423 - 428 °F
Average value: 219 °C Grade Count:3
Flammability, UL94 HB - V-0
HB - V-0
Grade Count:52
Electrical Properties Metric English Comments
Electrical Resistivity 460 - 1.00e+16 ohm-cm
460 - 1.00e+16 ohm-cm
Average value: 8.77e+14 ohm-cm Grade Count:31
Surface Resistance 1.00e+11 ohm
1.00e+11 ohm
Average value: 1.00e+11 ohm Grade Count:7
Dielectric Constant 3.60 - 4.13
3.60 - 4.13
Average value: 3.78 Grade Count:11
Dielectric Strength 5.00 - 45.0 kV/mm
127 - 1140 kV/in
Average value: 30.6 kV/mm Grade Count:18
Dissipation Factor 0.0110 - 0.0160
0.0110 - 0.0160
Average value: 0.0133 Grade Count:10
Arc Resistance 120 - 130 sec
120 - 130 sec
Average value: 126 sec Grade Count:6
Comparative Tracking Index 600 V
600 V
Average value: 600 V Grade Count:8
Processing Properties Metric English Comments
Processing Temperature 265 - 293 °C
509 - 560 °F
Average value: 283 °C Grade Count:18
Nozzle Temperature 240 - 295 °C
464 - 563 °F
Average value: 269 °C Grade Count:8
Melt Temperature 220 - 310 °C
428 - 590 °F
Average value: 271 °C Grade Count:37
Mold Temperature 60.0 - 120 °C
140 - 248 °F
Average value: 87.5 °C Grade Count:54